• 한국해양공학회지
• /
• 제8권2호
• /
• pp.38-46
• /
• 1994

The method of JSME S001-83 and ASTM E813-87 have been adapted for evaluation of the elastic-plastic fracture toughness J sub(IC) of SB41 steel. This SB41 steel have the characteristics of low-stength CT specimens. The test results obtained have been considered and compared on the basis of resulted data from two kinds of methods(JSME S001-83, ASTM E813-87) and two kinds of specimen configurations(smooth, side-grooved). On the basis of results from consideration and comparison, the difficulties for its application were presented in case when the standard ASTM E813-87 method was employed for the measurement of J sub(IC) in SB41 steel. A modified method was applied for measuring J sub(IC) in SB41 steel that it used the blunting line real-measured by experiment instead of the standard blunting line theoretically determined, and the result from that procedure was analyzed and the usefulness of that method was examined and considered.

• 한국안전학회지
• /
• 제12권3호
• /
• pp.45-51
• /
• 1997

To evaluate the elastic-plastic fracture toughness by this modified offset method, the origin of J-R curve is set with drawing the blunting line on the maximum point of the negative crack growth and R curve is modified by adding the blunting factor of the experimented point on the R curve. The elastic-plastic fracture toughness $J_{IC]$ of A5083-H112 material by the modified offset method we 44kN/m on the smooth CT specimens.

• 대한기계학회논문집
• /
• 제13권4호
• /
• pp.653-659
• /
• 1989

본 연구에서는 실험방법과 해석방법 등의 차이가 Ｊ$_{IC}$ 값에 미치는 영향을 고찰하여 보았으며, E 813-81법으로 해석된 Ｊ$_{IC}$ 값으로 환산하는 방법을 제안하고 몇 가지 재료와 환경에서 그 오차를 검토하였다.하였다.

• 대한기계학회논문집
• /
• 제10권4호
• /
• pp.494-503
• /
• 1986

본 연구에서는 저강도.고연성재인 일반구조용압연강 SB41의 평골 CT 시험편과 양측면홈이 있는 CT시험편을 사용하여 ASTM R유선법, JSME R유선법,SZW법, 초음파법 및 전입차법에 따라 J$_{IC}$를 종합적으로 평가하였다. 복수시험편법인 ASTM 및 JSME 및 JSME R유선법을 상호 비교고찰하므로써 저강도.고연성재에 대한 파환인성평가 의 적용한계를 명확히 하였으며 단일시험편법인 초음파 및 전입차시험법은 효율적이고 간편한 J$_{IC}$평가법임을 확인하였다.

• 한국해양공학회지
• /
• 제7권2호
• /
• pp.91-102
• /
• 1993

The elastic-plastic fracture thoughness J sub(IC) of Nuclear Reactor Vessel Steel(SA 508-3) which has high toughness was discussed at temperatures RT, $-20^{\circ}C$, $200^{\circ}C$ and 1/2/CT specimen was used for this study. Especially the two methods recommended in ASTM and JSME were compared. It was difficult to find J sub(IC) by ASTM R-curve method with the specimen used for this research, while JSME R-curve method yielded good result. The stretched zone width menthod gave slightly larger J sub(IC) values than those by the R-curve method for SA 508-3 steel.

• 한국해양공학회지
• /
• 제9권1호
• /
• pp.111-119
• /
• 1995

The elastic-plastic fracture toughness($J_{IC}$) and fracture resistance (J-R curve) of SA508-3 alloy steel used for nuclear reactor pressure vessel are investigated by using CT-type specimens. Fracture toughness tests are conducted by unloading compliance method and multiple specimen method at room temperature, -2$0^{\circ}C$ and 20$0^{\circ}C$. The apparent negative crack growth phenomenon which usually arises in partial unloading compliance test is well known. The negative crack growth phenomenon in determining J sub(IC) or J-R cure from partial unloading compliance experiments may be eliminated by the offset technique. In this study, the evaluation of $J_{IC}$ multiple specimen method recommended by the JSME gives the most reliable results by using half-size CT(similar-type) specimens.

• 대한기계학회논문집
• /
• 제16권9호
• /
• pp.1627-1631
• /
• 1992

본 연구에서는 균열길이 감소현상의 처리법에 대하여 고찰하고자 하며, 내용 을 요약하면 다음과 같다. (1) 오프세트(offset)법의 배경 및 오프세트법에 의한 균열길이 감소현상의 처리 방법 을 제안하였다. (2) 실제의 균열길이의 측정과 $J_{IC}$실험해석을 통하여, 수정식과 오프세트법의 타 당성을 검토하였다.

• 한국해양공학회지
• /
• 제8권2호
• /
• pp.157-165
• /
• 1994

Effect of an accelerated iso-thermal aging (375 degree C x 66days, 375 degree C x 200days) on elastic-plastic fracture resistance curve were examined in SA533B low alloy steel. Fracture toughness test are conducted by unloading compliance method at room temperature. But the apparent negative crack growth phenomenon, usually arise in partial unloading compliance test. The phenomenon of negative crack growth may be eliminated by the offset technique. There is no effect of aging on J sub(IC) and dJ/da in iso-thermal aged (375 degree C x 66 days) specimen, but there is very little effect in iso-thermal aged (375 degree C x 200 days) specimen.

• Journal of Welding and Joining
• /
• 제5권2호
• /
• pp.44-52
• /
• 1987

The fracture toughness, $J_{IC}$ of high frequency electric resistance welded steel pipe for smooth and side-grooved CT specimen was evaluated by unloading compliance method. The crack growth, .${\delta}a$ was obtained from the equation of Donald and Saxena & Hudak, and $J_{IC}$ was determined from the curve of J-${\delta}a$ relations. The crack growth on the experiment using unloading compliance method is underestimated as compared with ${\delta}a$ measured directly by the SEM, so the reliability of $J_{IC}$ from saxena & Hudak equation is large than that from Donald. The $J_{IC}$ value of side-grooved CT Specimen is estimated less than that of smooth, and this is the effect of the side-groove, the shear-lip of crack tip and the reduction of crack tunnelling phenomena.

• 한국해양공학회지
• /
• 제1권1호
• /
• pp.127-137
• /
• 1987

The evaluation of the elastic-plastic fracture toughness $J_{1C}$ was performed on the center of weld metal(CWM), the heat affected zone (HAZ) and the base metal (BM) of API 5LB steel pipes welded by the high frequency electric resistance welding. The $J_{1C}$ was evaluated by the JSME R-Curve and JSME SZW methods using the smooth and side-grooved specimens. The results are as follows; (1) The $J_{1C}$ values by the SZW method are overestimated as compared with those by the R-curve method, because the micro-crack is formed as SZW increase with the deformation at SZ after initiation of the ductile crack. (2) The everage of $J_{1C}$ values by the the R-curve and the SZW methods in side-grooved specimens tended to decrease in comparison with smooth specimens 9.42% at CWM, 4.2% at HAZ, 23.2% at BM, respectively. (3) The boundary of the fatigue pre-crack, stretched zone, and dimple regions appeared more clearly in side-grooved specimens, for the slight change of SZW in the direction of the plate thickness, as compared with smooth specimens.