• Transactions of the Korean Society of Automotive Engineers
• /
• v.10 no.3
• /
• pp.130-135
• /
• 2002

This study investigates the effect of curing method on the bonding strength of aluminum/CFRP composites. The surface of aluminum panel was treated by DC plasma. Lap shear tests and T-peel tests were performed based on the procedure of ASTM 906-94a and ASTMD1876-95, respectively. Test samples were fabricated by using the co-curing method and the secondary curing method. The results showed that the shear strength of test samples made by the co-curing method was 2.5 times greater than that of test samples made by the secondary curing method. The T-peel strength of the co-curing method case was almost 2 times greater than that of the secondary curing method case.

• Composites Research
• /
• v.23 no.2
• /
• pp.31-39
• /
• 2010

In this paper, composite panels with hat-shaped stiffeners were made using the co-curing, co-bonding and secondary bonding methods. Co-curing is a manufacturing method in which the hat part and the plate are cured simultaneously in a manner that is more cost effective than other methods. Co-bonding is a method in which the stacked prepregs are cured with other cured parts, and secondary bonding is a method in which cured parts are bonded together using an adhesive. A rubber mold was manufactured for co-curing of composite panel with hat-shaped stiffeners, and finite element analyses were done to evaluate the expanding pressure of the rubber mold consistent with the curing temperature. The manufactured panels were also evaluated using a 3-D measurement tester and an ultrasonic tester. Pull-off tests were performed to evaluate their mechanical properties.

• Journal of the Korean Society of Tobacco Science
• /
• v.20 no.1
• /
• pp.19-25
• /
• 1998

The bulk curing experiment to the improve the quality of flue-cured leaves were carried out to evaluate relationship between cyclic curing and conventional curing method. We studied the effect of the cyclic change of wet bulb temperature at the yellowing stage of flue curing on chemical properties of cured leaves. The wet bulb temperature was automatically controlled between preset high($38^{\circ}C$) and low point ($35^{\circ}C$) everyone hour cyclically during 12 hours after starting luring. As a result, the acceleration of the increase in the chemical properties of cured leaves were observed. As to the chemical properties, there was decreased in citric acid, increased in malic acid of the nonvolatile organic acids and all higher fatty acids content of leaves cured by this method compared with in that of conventional curing method, while a major chemical compounds in relation to aromatic essence of cigarette smoke in essential oil components of lured leaves was mostly higher in this method than those of conventional ones, and it was evaluated that there was decreased in CO, TPM, Tar, and $CO_2$ content of the cigarette smoke comparing to the conventional luring method.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2005.05b
• /
• pp.273-276
• /
• 2005

Polymer-modified mortar was developed for improving the performance of modified mortar which is mixed with polymer, and it is used for protecting and repairing materials of building because of their excellent performance to improve characteristics which are compressive strength, flexural strength, and adhesive strength. However, the performances of the polymer-modified mortars are highly affected by materials, which are polymer, mortar, and aggregates, and conditions which are curing environment and testing method. Furthermore, dry curing method after hydrated curing has been recommended to make strong polymer film for the best curing method to make excellent characteristics. In this report, We investigated the co-relation between curing methods and the characteristics, which are compressive strength, flexural strength, and adhesive strength for the polymer-modified mortars that are used in the domestic area.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2004.10a
• /
• pp.83-87
• /
• 2004

In this work, the cure cycle of co-cured metal/composite structure was investigated to decrease fabricating thermal residual stresses between the metal and the composite material. DSC (Differential scanning calorimetry) experiment and static lap shear test of co-cured aluminum/composite double lap joint as well as the curvature experiment of co-cured steel/composite strip were performed to investigate the effect of curing cycle on the thermal residual stress of co-cured hybrid structures. From the experiments, it was found that post curing method after abrupt cooling of co-cured aluminum/composite hybrid structure at certain point of degree of cure during curing process could eliminate fabricating the thermal residual stresses.

• Journal of the Korea Institute of Military Science and Technology
• /
• v.20 no.5
• /
• pp.620-632
• /
• 2017

A chemical vapor curing method(CVC) was developed to cure polycarbosilane(PCS) fibers by using cyclohexene vapour as a non-oxygen active reactant, instead of air in oder to prepare the silicon carbide(SiC) fiber with low oxygen content. A cross-linked PCS fibers by cyclohexene vapor showed a completely different variation in IR spectra in comparison to the air-cured PCS fiber. CVC method resulted in less than 3 wt% in oxygen content. In this experiment conditions, The average tensile strength and modulus of SiC fiber obtained by CVC had 1995 MPa and 183 GPa respectively, which is higher than that of SiC fiber prepared by air-curing process.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2013.05a
• /
• pp.33-34
• /
• 2013

Recently, as the policy of state that it is the low carbon green growth is promoted, the effort for reducing the CO₂ gas generation ejected from the construction industry in the cement production is continued. That is, the method using the mineral admixtures including the silica fume and red mud, silica fume and etc. it is the industrial byproduct with the method solving the exhaustion problem of the environmental contamination settlement and natural resources, the great quantity as the cement substitute material is examined. Accordingly, in this research, the strength characteristic of the curing body differentiating the curing method of the ternary system inorganic binder using the blast furnace slag and red mud, silica fume and etc. as the cement substitute material tried to be examined.

• Composites Research
• /
• v.13 no.4
• /
• pp.42-53
• /
• 2000

A study has been made to establish an optimum condition in the surface treatment and curing method that is important for the fabrication of Al 7075/CFRP laminates. PAA(Phosphoric Acid Anodizing) provided a good adhesive strength and FPL(Sulfuric / Sodium Dichromate Acid Etching) had a similar adhesive strength with PAA. On the other hand, the poor adhesive strength was shown on vapor degrease and CAA(Chromic Acid Anodizing). By using the atomic force microscope(AFM), it was found that the PAA oxide surface obviously had a greater degree of microroughness as compared to vapor degrease, CAA and FPL treated surfaces. These results support the concept of a mechanical interlocking of the adhesive with-in the oxide pores as the predominant adhesion mechanism. In curing methods, the adhesive strength of co-curing method was higher than that of secondary curing method. With respect to stability of specimen shape, the secondary curing method was better than co-curing method. DMA(Dynamic Mechanical Analysis) test revealed $T_g$ in curing times over 60 min is nearly same, so it is estimated they will have similar degree of curing and joint durability in using FM300M adhesive film.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2001.05a
• /
• pp.172-175
• /
• 2001

The co-cured Joining method, which is regarded as an adhesively bonded Joining method, is an efficient joining technique because both curing and bonding processes for the composite structures can be achieved simultaneously. It requires neither surface treatment onto the composite adherend nor an additional adhesive joining process because the excess resin, which is extracted from composite materials during consolidation, accomplishes the co-cured Joining process. Since the adhesive of the co-cured joint is the same material as the resin of the composite adherend, the analysis and design of the co-cured joint for composite structures are simpler than those of an adhesively bonded joint, which uses an additional adhesive. In this paper, effects of the manufacturing parameters, namely surface roughness, stacking sequence of the composite adherend, and manufacturing pressure in the autoclave during curing process, on the tensile load bearing capacity of the co-cured single lap joint will be experimentally investigated.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2023.05a
• /
• pp.115-116
• /
• 2023

This study aims to investigate and improve the carbon dioxide sequestration capability and the mechanical properties of non-hydraulic low calcium silicate cement especially designed for CO₂ reaction and ordinary Portland cement subjected to the carbonation curing facilitating pH swing method. Nitric acid (HNO₃) was utilized as an liquid for the mixing of cement paste to enhance the initial dissolution of Ca ions from the cements by promoting low pH environment and prevent the direct precipitation of Ca with the anion, owing to the high solubility of Ca(NO₃)₂ in water. The results presented that the higher the concentration of HNO₃, the higher the compressive strength and CO₂ sequestration (until 0.1 M). Ca dissolution caused by the harsh acid attack onto the anhydrous cement particle lead to the higher carbonation reaction degree, forming abundant CaCO₃ crystals after the reaction. However, cement paste mixed with excessively high concentration of HNO₃ presented deterioration due to the too harsh pH environment and abundant NO₃- ions which are known to retard the reaction of cement.