• 한국연소학회:학술대회논문집
• /
• 2013.06a
• /
• pp.19-20
• /
• 2013

The cofiring of renewable fuel in coal fired boilers is an attractive option to mitigate $CO_2$ emissions, since it is relatively low cost option for efficiently converting renewable fuel to electricity by adding biomass as partial substitute of coal. However, it would lead to reduce plant efficiency and flexibility in operation, and increase operation cost and capital cost associated with renewable fuels handling and firing equipment. The aim of this study is to investigate reduction of carbon dioxide at varying percentage of biomass in fuel blend to the boiler biomass, and estimate operation and capital cost. Wood pellet, PKS (palm kernel shell), EFB (empty fruit bunch) and sludge are considered as a renewable fuels for a cofiring with coal. Several approaches by the cofiring ratio are chosen from past plant demonstrations and commercial cofiring operation, and they are evaluated and discussed for CO2 reduction and cost estimation.

• Journal of the Korean Ceramic Society
• /
• v.34 no.6
• /
• pp.601-610
• /
• 1997

In cofiring of multilayered alumina with tungsten, the change of camber with lamination condition was experimented and the effect of sintering shrinkage of alumina and tungsten was investigated. From the exact measurement of sintering shrinkage of tungsten thick film, as lamination pressure increased, the sintering shrinkage of alumina decreased but that of tungsten thick film was not changed. So it was though that the main factor which induced the sintering shrinkage difference between ceramics and metal with lamination condition was the change of sintering shrinkage of ceramics. In case of high lamination pressure, high green sheet density, the cofired specimen showed low camber due to low shrinkage difference between alumina and tungsten and there was a linear relation between camber and shrinkage difference. It was found that this shrinkage difference could change the thickness of tungsten film and the microstructure within via hole during cofiring.

• Macromolecular Research
• /
• v.12 no.4
• /
• pp.391-398
• /
• 2004

Thick-film photolithography is a new technology that combines lithography processes, such as exposure and development, with the conventional thick-film process applied to screen-printing. In this study, we developed a low-temperature cofireable silver paste applicable for thick-film processing to form fine lines using photolitho-graphic technologies. The optimum paste composition for forming fine lines was investigated. The effect of processing parameters, such as the exposing dose, had on the fine-line resolution was also investigated. As the result, we found that the type of polymer and monomer, the silver powder loading, and the amount of photoinitiator were the main factors affecting the resolution of the fine lines. The developed photoimageable silver paste was printed on a low-temperature cofireable green sheet, dried, exposed, developed in an aqueous process, laminated, and then fired. Our results demonstrate that thick-film fine lines having widths < 20 $\mu\textrm{m}$ can be obtained after cofiring.

• Proceedings of the Korean Ceranic Society Conference
• /
• 2002.10a
• /
• pp.105.1-105
• /
• 2002

• Journal of the Korean Ceramic Society
• /
• v.41 no.4
• /
• pp.313-322
• /
• 2004

Thick film photolithography is a new technology in that the lithography process such as exposure and development is applied to the conventional thick film process including screen-printing. In this research, low-temperature cofireable silver paste, which enabled the formation of thick film fine-line using photolithographic technology, was developed. The optimum composition for fine-line forming was studied by adjusting the amounts of silver powder, polymer and monomer, and the additional amount of photoinitiator, and then the effect of processing parameter such as exposing dose on the formation of fine-line was also tested. As the result, it was found that the ratio of polymer to monomer, silver powder loading, and the amount of photoinitiator were the main factors affecting the resolution of fine-line. The developed photosensitive silver paste was printed on low-temperature cofireable green sheet, then dried, exposed, developed in aqueous process, laminated, and fired. Results showed that the thick film fine-line under 20$\mu\textrm{m}$ width could be obtained after cofiring.

• Journal of Energy Engineering
• /
• v.19 no.4
• /
• pp.251-257
• /
• 2010

Korea have a plan to enforce the Renewable Portfolio Standard(RPS) in 2012 for climate change action and effective use of energy but because of lack of renewable energy resources and limits of technology development, it will be hard to fullfill a target for RPS obligation in domestic power generation sector and woodchip biomass cofiring with coal combustion is the one of the alternative methods of the goal. Woodchip biomass cofiring with coal combustion is easy to approach technical design and has competitiveness of $CO_2$ & renewble energy certificate benefit and also has much lower generation cost than any other renewable energy resources. Because of that reason, woodchip biomass cofiring with coal combustion should be needed to fullfill the goal for RPS obligation in domestic power generation sector with midlong-term direction.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2007.11a
• /
• pp.40.1-40.1
• /
• 2007

• Journal of the Korean Ceramic Society
• /
• v.31 no.4
• /
• pp.427-435
• /
• 1994

Cu-metallized low firing temperature substrates were synthesized by cofiring green sheet of cordierite-based glass with Cu. By Sol-Gel method, Cu powder was coated with borosilicate gel which should act as a glass frit in Cu paste during cofiring. Theoretical weight ratios of Glass/Cu were controlled to be 2.5, 5, 10 and 15% by varying alkoxide concentrations. Average particle size of coated Cu was 0.629~0.674 ${\mu}{\textrm}{m}$ in comparison to that of as-received Cu(0.596 ${\mu}{\textrm}{m}$), which increased with alkoxide concentration but did not increase above certain concentration. The weight ratios of coated layer were 2.11~5.37%. The properties of Cu-metallized low firing temperature substrate, cofired at 90$0^{\circ}C$ for 1h under H2/N2 atmosphere, were as follows; sheet resistance was 13~43 m{{{{ OMEGA }}/$\square$, adhesion strength was 1.0~2.1 kgf/$\textrm{mm}^2$. From the observations of SEM photographs, the gel coated on Cu performed excellently as a glass frit.

• Proceedings of the International Microelectronics And Packaging Society Conference
• /
• 2001.07a
• /
• pp.151-156
• /
• 2001

Using the photoimageable thick film conductors, $25\mu\textrm{m}$ line widths and $25\mu\textrm{m}$ spaces can be obtained. Test patterns are made by green tape lamination, paste printing, exposing to UV light, developing in an aqueous process and cofiring. Postfiring method using alumina substrate can be also applied to fine line formation. Series gap resonator formed by photopatterning process showed the improved signal transmission characteristics compared to that obtained by conventional screen printing.

• Journal of the Microelectronics and Packaging Society
• /
• v.9 no.2
• /
• pp.19-25
• /
• 2002

Glass composed of $Li_2$O.MgO. $MgF_2$.$SiO_2$.$B_2O_3$ for the fabrication of green sheet was prepared by melting process, and glass ceramics was prepared by the process of nucleation and grystal growth for the glass of $Li_2$O.MgO. $MgF_2$.$SiO_2$.$B_2O_3$ system with Lithium fluorhectorite and Lithium boron fluorphlogopite crystal phase. Powderization of the glass ceramics was carried out by water swelling. The average particle size at this point was 2.574 $\mu\textrm{m}$. Slurry was prepared for green sheet using high viscous sol fabricated by water swelling, which shows cleavage phenomenon in prepared glass ceramics. The optimum ratio of powder to water for the tape casting was 18:100, and its viscosity was 11,000~14,000 cps.