• Journal of Ocean Engineering and Technology
• /
• v.13 no.3 s.33
• /
• pp.36-48
• /
• 1999

Fatigue life and crack retardation behavior after penetration were experimentally examined using surface pre-cracked specimens of aluminium alloy 5083. The Wheeler model retardation parameter was used successfully to predict crack growth behavior after penetration. By using a crack propagation rule, the change in crack shape after penetration can be evaluated quantitatively. Advanced, waveform-based acoustic emission (AE) techniques have been successfully used to evaluate signal characteristics obtained form fatigue crack propagation and penetratin behavior in 6061 aluminum plate with surface crack under fatigue stress. Surface defects in the structural members are apt to be origins of fatigue crack growth, which may cause serious failure of the whole structure. The nondestructive analysis on the crack growth and penetration from these defects may, therefore, be one of the most important subjects on the reliability of the leak before break (LBB) design. The goal of the present study is to determine if different sources of the AE could be identified by characteristics of the waveforms produced from the crack growth and penetration. AE signals detected in four stages were found to have different signal per stage. With analysis of waveform and power spectrum in 6061 aluminum alloys with a surface crack, it is found to be capabilities on real-time monitoring for the crack propagation and penetration behavior of various damages and defects in structural members.

• Journal of Ocean Engineering and Technology
• /
• v.11 no.3
• /
• pp.29-38
• /
• 1997

Crack penetration behavior by fatigue crack propagation and measurements of AE before-and-after crack penetration were examined using SS41 steel plate. Experimental crack shape of SU type was in good agreement with calculated shape rather than S type. Crack propagation behavior on the front surface appears not to change markedly after penetration. However, crack growth on the back surface appears to accelerate as reported by author. As a crack propagates, AE occurred heavily just before penetration. Then, it decreases and crack is penetrating. A transition from plane strain to plane stress was observed by fractographic study. At this time, separation of fracture surface was shown which affects AE occurrence.

• Journal of the Korean Society of Fisheries and Ocean Technology
• /
• v.28 no.2
• /
• pp.197-207
• /
• 1992

Fatigue life and penetration behavior were examined analytically by variety of initial front face crack length and initial crack depth. The fatigue crack shape before penetration is almost semielliptical, and the aspect ratio by calculation using the Newman-Raju's formula is smaller than the value obtained by the experiment. It is found that the crack growth behavior on the back surface after penetration is unique and can be divided into three stage a, b and c. By using the K value proposed by the authors, particular crack growth behavior and the change in crack shape can be evaluated quantitatively. It is found that fatigue life and penetration behavior were more dependent on initial front face crack length than initial crack depth.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.15 no.6
• /
• pp.1990-2001
• /
• 1991

The fatigue life and crack penetration behavior of high strength steel have been studied in detail both experimentally and analytically. The fatigue crack shape of a smooth specimen is almost semicircular, while a specimen with stress concentration becomes semielliptical according to stress concentration shape. The aspect ratio of smooth specimens calculated using the Newman-Raju's formular is smaller than the value obtained from the experiment. On the other hand, the aspect ratio of the stress concentration specimen shows a good agreement with experimental results. It is found that the crack growth behavior on the back surface after the penetration is unique and can be divided into three stages ; rapid growth region, constant growth region and acceleration growth region. By using the K value suggested in this study, the particular crack growth behavior and crack shape can be estimated quantitatively.

• Journal of the Korean Institute of Gas
• /
• v.4 no.1 s.9
• /
• pp.33-39
• /
• 2000

Stress intensity factor after penetration was discussed experimentally using long surface pre-cracked specimens of aluminum alloy 5083. The propagation behavior evaluation of long surface crack by equation proposed at penetration of short surface crack could be need modification to evaluate precisely because the error was high as aspect ratio is little. The modification of stress intensity factor with consideration of aspect ratio at penetration of long surface crack can be analyzed the behavior of crack penetration quantitatively.

• Journal of the Korean Institute of Gas
• /
• v.3 no.1
• /
• pp.1-7
• /
• 1999

Fatigue behavior of before-and-after penetration was examined experimentally using surface pre-cracked specimens of aluminium alloy 5083-0. The fatigue crack shape before penetration is almost semicircular, and the measured aspect ratio is larger than the value obtained by calculation using K values proposed by Newman-Raju. It is found that the crack growth behavior on the back side after penetration is unique and can be divided into three stages. By using a crack propagation rule in case of long surface crack, the change in crack shape after penetration can be evaluated quantitatively.

• Journal of Ocean Engineering and Technology
• /
• v.9 no.1
• /
• pp.83-91
• /
• 1995

Surface defects in structural members are apt to be origins of fatigue cracks growth, which may cause serious failure of whole structures. Most structure has a part where stress concentrates such as welded joints, corner parts, etc. And then, analysis on crack growth and penetration from these defects, therefore, is one of the most important subjects for the reliability of LBB design. The present paper has performed an experimental and analysis on the fatigue crack propagation by variety in crack length of surface cracked plate with stress concentration part. The crack growth behavior can be explained quantitatively by using Newman-Raju equation and the stress partitioning method proposed by ASME B&P Code Sec. XI. The stress concentration factor $K_t$ has affected on the crack growth. The crack growth after penetration depends upon the initial front side crack length.

• Proceedings of the KSME Conference
• /
• 2001.11a
• /
• pp.67-72
• /
• 2001

The LBB behavior and the crack opening displacement after a crack penetrated wall thickness of statically indeterminate piping system were investigated in this study, compared with statically determinate piping system. The reduction of ultimate strength caused by a crack was relatively small in the statically indeterminate piping system. The statically indeterminate piping system has more safety margin for LBB behavior than the statically determinate piping system. The crack opening displacement could be evaluated by using the plastic rotation angle proposed to evaluate the crack opening displacement after crack penetration in pipe with a non-penetrating crack.

• Journal of Mechanical Science and Technology
• /
• v.16 no.1
• /
• pp.24-31
• /
• 2002

The leak-before-break (LBB) behaviors of a structural component under high and low fatigue loads are an important problem in nuclear power plants, liquid nitrogen gas tankers and chemical plants. This paper is an experimental study to evaluate the crack opening behavior after penetration for plate and pipe specimens. Crack opening displacement after penetration under low fatigue load could be satisfactorily determined at the center of the plate thickness regardless of the specimen size. In the case of high fatigue load, it is shown that the crack opening displacement at the center of a penetrated crack carl be derived using the gross stress, $\sigma$/sug G/, and the front surface crack length, a$\_$s/, together with the back surface crack length, a$\_$b/.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.34 no.6
• /
• pp.725-730
• /
• 2010

The leak-before-break behavior and the crack opening displacement were investigated of statically indeterminate piping system and statically determinate piping system after a crack penetration. The reduction in the ultimate strength caused by a crack was relatively small in the statically indeterminate piping system. The leak-before-break in the statically indeterminate piping system had a larger safety margin than that in the statically determinate piping system. The crack opening displacement after crack penetration in a pipe with a nonpenetrating crack was evaluated by using a plastic rotation angle.