• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.18 no.4
• /
• pp.521-526
• /
• 2017

In the GTA welding process of Al 7075 alloy using different types of filler metals, the tensile test and micro-hardness test were conducted to evaluate the mechanical characteristics. Also, the radiographic test result showed that the weld met the criterion of level 1 in accordance with KS D 0242 for verifying the welding integrity and there were no welding defects. The tensile test result obtained using Al 7075 as a filler metal showed that the material was fractured in the weld zone. The tensile strengths of the materials using Al 7075 and ER 4043 as the filler metal were about 240MPa and 253MPa, their yield strengths were about 132MPa and 120MPa and their elongation percentages were 6.6% and 13%, respectively. The micro-hardness value of the deposited metal zone when using Al 7075 as the filler metal was Hv 132. However, the micro-hardness of the material using ER4043 as the filler metal was about 24% lower than that using Al 7075. When the chemical composition of the filler metal is the same as that of the material itself, fracture can occur in the deposited metal zone. Therefore, it is not desirable to use the same material as the filler metal for the welding of Al 7075 alloy. Moreover, the use of Al-Si based ER 4043 as a filler metal is more desirable than using the same material as a filler metal for welding Al 7075.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.20 no.4
• /
• pp.1-7
• /
• 2021

In this study, MIG welding was performed on extruded 6005A-T6 material, which is used in the base panel of railway vehicles. The material was considered as the experimental base material, and argon shielding gas and ER5356 and ER4043 filler metals were used as the consumable welding materials. Welding coupons were prepared under various welding conditions by using an auto-welding system that various welding conditions applied 2.5Hz and 4.5Hz the pulse frequency of SynchroPuls function of welding machine and 1.0mm and 1.5mm of root face affect the weld penetration of welding joint. The welding current and voltage were also varied for this testing. On the basis of the results obtained, optimum welding conditions are proposed.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.20 no.6
• /
• pp.17-25
• /
• 2021

In this study, the mechanical properties of railway-vehicle aluminum under frame was investigated based on the metal inert gas (MIG) welding conditions. An aluminum-alloy (6005A-T6) extruded material used in the lower panel of a railway vehicle was connected through MIG welding to determine the mechanical properties of MIG welds. Argon shielding gas and filler materials, such as ER5356 and ER4043, were used as consumable welding materials. For the welding conditions of the test specimen, welding frequencies of 2.5 and 4.5 Hz were applied using the SynchroPuls function, and the root faces were 1.0 and 1.5 mm. The mechanical properties of the MIG welds were determined through tensile, bending, and fatigue tests.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.10 no.5
• /
• pp.625-634
• /
• 1986

The strain distribution on a welded aluminum alloy transition joint produced by a static tensile load has been measured using a moire method combined with photoelastic coating method. The test specimens were made of aluminum alloy 6061-T6 and 2014-T6 butt welded with ER-4043 filler metal, and were post welded heat treated (solid solution heat treatment 502.deg. C 70min.) and precipitated (artificial aging 171.deg. C 600min.) to cause an abrupt change of mechanical properties between the base metals and weld metal. The photoelastic epoxy rubber was cemented on the specimen grating which had been reproduced on the specimen surface by using an electropolishing. The measurements were compared with strains computed by Finite Element Analysis. The following results were abtained. (1) The maximum strain were distributed along the center line in the transverse directiion of the weld metal. (2) The strain gradient along the fusion line increased approaching the V-groove tip and the maximum value was observed at a quarter of width from the V-groove tip. (3) The moire method combined with photoelastic coating was proved very useful for real time strain measurement in the welded aluminum alloy transition joint.