• The Transactions of The Korean Institute of Electrical Engineers
• /
• v.65 no.9
• /
• pp.1504-1510
• /
• 2016

The aim of this study is to improve properties both glass transition temperature($T_g$) and coefficient of thermal expansion(CTE) using epoxy/micro-nano alumina composites with adding glycerol diglycidyl ether (GDE:1,2,3,5g). This paper deals with the effects of GDE addition for epoxy/micro alumina contents (40, 50, 60wt%)+surface modified nano alumina(1_phr) composites. 20 kinds specimen were prepared with containing micro, nano alumina and GDE as a micro composites(10, 20, 30, 40, 50, 60, 70wt%) or a nano/micro alumina composites(1phr/40, 50, 60wt%). Average particle size of nano and micro alumina used were 30nm and $1{\sim}2{\mu}m$, respectively. The micro alumina used were alpha phase with Heterogeneous and nano alumina were gamma phase particles of spherical shape. The glass transition temperature and coefficients of thermal expansion was evaluated by DSC and TMA. The glass transition temperature decreased and coefficients of thermal expansion become smaller with filled contents of epoxy/micro alumina composites. On the other hand, $T_g$ and CTE as GDE addition variation(1,2,3,5g) of epoxy/micro-nano alumina composites decreased and increased respectively.

• The Transactions of The Korean Institute of Electrical Engineers
• /
• v.65 no.9
• /
• pp.1511-1517
• /
• 2016

The aim of this study is to improve of properties for electrical AC insulation breakdown strength using epoxy/micro-nano alumina composites with adding glycerol diglycidyl ether (GDE:1,3,5g). This paper deals with the effects of GDE addition for epoxy/micro alumina contents (40,50,60wt%)+surface modified nano alumina(1_phr) composites. 14 kinds specimen were prepared with containing epoxy resins, epoxy micro composites and epoxy nano-micro alumina mixture composites. Average particle size of nano and micro alumina used were 30nm and $1{\sim}2{\mu}m$, respectively. The micro alumina used were alpha phase with Heterogeneous and nano alumina were gamma phase particles of spherical shape. The electrical AC insulation breakdown strength was evaluated by sphere to sphere electrode system and raising velocity 1kV/s. The AC breakdown strength decreased insulation properties of multi-composites according to increasing micro alumina and GDE addition contents.

• The Transactions of The Korean Institute of Electrical Engineers
• /
• v.65 no.6
• /
• pp.1026-1031
• /
• 2016

Neat Epoxy, nano alumina composites, micro alumina composites and multi-nano alumina composites were prepared and experiment were performed to measure their partial discharge resistant characteristics. The partial discharge resistance obtained for the microcomposites, nanocomposites and multi-nanocomposites are compared with those of unfilled epoxy and with GDE amount for surface modifier. It was observed that compare multi-nano alumina composites to micro alumina composites, the partial discharge resistance to degradation gets improved considerably. The improvement in the degradation resistance is attributed to the interface intension between the nano alumina composites and GDE, micro alumina and epoxy neat.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.29 no.12
• /
• pp.796-802
• /
• 2016

In order to develop an electrical insulation material for gas GIS (insulation switch gear) spacer, 4 types of epoxy/micro-alumina (40, 50, 60, 70 wt%) composites and 9 types of epoxy/nano-alumina (1, 3, 5 g)/micro-alumina (40, 50, 60, 70 wt%) composites were prepared and tensile test was carried out. In here, nano-alumina was previously surface-treated with GDE (glycerol diglycidyl ether). As micro-alumina and GDE-treated nano-alumina contents increased, tensile strength increased and the highest value was shown in the system with 3 g GDE-treated nano-alumina.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.29 no.9
• /
• pp.565-570
• /
• 2016

In this work, the complex permittivity of epoxy resins is measured. Epoxy resins, epoxy with micro size fillers and epoxy with micro+nano alumina composites have been evaluated for dielectric properties according to frequency variation. The dielectric spectroscopy measurement and analyses are carried out in the frequency range of $10^{-2}Hz$ to 1MHz and constant to room temperature. The results of dielectric loss suggest that significant improvement in the electrical performance can be expected by using samples containing nano and micro fillers mixture when compared to materials containing only microfillers. As the result, we verified the specific characteristics of dielectric permittivity and dielectric loss namely, relative permittivity become low with improving dispersibility of nano+micro mixture composites and become rise with agglomerate of nano particles.