• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.32 no.1
• /
• pp.6-12
• /
• 2019

Bonding properties of epoxy-containing solder joints were investigated by a high temperature aging test. Specimens were prepared by bonding an R3216 standard chip resistor to an OSP-finished PCB by a reflow process with two basic types of solder (SAC305 & Sn58Bi) pastes and two epoxy-solder (SAC305+epoxy & Sn58Bi+epoxy) pastes. In all epoxy solder joints, an epoxy fillet was formed in the hardened epoxy, lying around the outer edge of the solder joint, between the chip and the Cu pad. In order to analyze the bonding characteristics of solder joints at high temperatures, a high-temperature aging test at $150^{\circ}C$ was carried out for 14 days (336 h). After aging, the intermetallic compound $Cu_6Sn_5$ was found to have formed in the solder joint on the Cu pad, and the shear stress on the conventional solder joint was reduced by a significant amount. The reason that the shear force did not decrease much, even though in epoxy solder, was thatbecause epoxy hardened at the outer edge of the supported solder joints. Using epoxy solder, strong bonding behavior can be ensured due to this resistance to shear force, even in metallurgical changes such as those where intermetallic compounds form at solder joints.

• Journal of Welding and Joining
• /
• v.33 no.3
• /
• pp.32-39
• /
• 2015

With the simplicity of process and high reliability in chip or package bonding, epoxy solder paste (ESP) has been recently considered as a competitive bonding material. The ESP material is composed of solder powder and epoxy formulation which can remove oxide layers on the surface of solder powder and pad finish metal. The bonding formed using ESP shows outstanding bonding strength and suppresses electrical short between adjacent pads or leads owing to the reinforced structure by cured epoxy after the bonding. ESP is also expected to suppress the formation and growth of whisker on the pads or leads. With the mentioned advantages, ESP is anticipated to become a spotlighted bonding material in the assembly of flexible electronics and electronic modules in automotive vehicles.

• Journal of the Microelectronics and Packaging Society
• /
• v.22 no.1
• /
• pp.69-74
• /
• 2015

With difficulties during the cleaning of reflow flux residues due to the decrease of the part size and interconnection pitch in the advanced electronic devices, the need for the no-clean solder paste is increasing. In this study, an epoxy curable solder paste was made with SAC305 solder powder and the curable flux of which the main ingredient is epoxy resin and its reflow solderability, flux residue corrosivity and solder joint mechanical properties was investigated with comparison to the commercial rosin type solder paste. The fillet shape of the cured product around the reflowed solder joint revealed that the curing reaction occurred following the fluxing reaction and solder joint formation. The copper plate solderability test result also revealed that the wettability of the epoxy curable solder paste was comparable to those of the commercial rosin type solder pastes. In the highly accelerated temperature and humidity test, the cured product residue of the curable solder paste showed no corrosion of copper plate. From FT-IR analysis, it was considered to be resulted from the formation of tight bond through epoxy curing reaction. Ball shear, ball pull and die shear tests revealed that the adhesive bonding was formed with the solder surface and the increase of die shear strength of about 15~40% was achieved. It was considered that the epoxy curable solder paste could contribute to the improvement of the package reliability as well as the removal of the flux residue cleaning process.

• Journal of the Microelectronics and Packaging Society
• /
• v.21 no.4
• /
• pp.97-103
• /
• 2014

Among various lead-free solders, the Sn-58Bi solders have been considered as a highly promising lead-free solders because of its low melting temperature and high tensile strength. However, Sn-58Bi solder has the poor ductility. To enhance the mechanical property of Sn-58Bi solder, epoxy-enhanced Sn-58Bi solders have been studied. This study compared the microstructures and the mechanical properties of Sn-58Bi solder and Sn-58Bi epoxy solder with aging treatment. The solders ball were formed on the printed circuit board (PCB) with organic solderability preservative (OSP) surface finish, and then the joints were aged at 85, 95, 105 and $115^{\circ}C$ for up to 100, 300, 500 and 1000 hours. The shear test was conducted to evaluate the mechanical property of the solder joints. $Cu_6Sn_5$ intermetallic compound (IMC) layer grew with increasing aging time and temperature. The IMC layer for the Sn-58Bi epoxy solder was thicker than that for the Sn-58Bi solder. According to result of shear test, the shear strength of Sn-58Bi epoxy solder was higher than that of Sn-58Bi solder and the shear strength decreased with increasing aging time.

• Journal of the Microelectronics and Packaging Society
• /
• v.27 no.1
• /
• pp.55-65
• /
• 2020

The use of underfill materials in semiconductor packages is not only important for stress relieving of the package, but also for improving the reliability of the package during shock and vibration. However, in recent years, as the size of the package becomes larger and very thin, the use of the underfill shows adverse effects and rather deteriorates the reliability of the package. To resolve these issues, we developed the package using a solid epoxy material to improve the reliability of the package as a substitute for underfill material. The developed solid epoxy was applied to the package of the application processor in smart phone, and the reliability of the package was evaluated using thermal cycling reliability tests and numerical analysis. In order to find the optimal solid epoxy material and process conditions for improving the reliability, the effects of various factors on the reliability, such as the application number of solid epoxy, type of PCB pad, and different solid epoxy materials, were investigated. The reliability test results indicated that the package with solid epoxy exhibited higher reliability than that without solid epoxy. The application of solid epoxy at six locations showed higher reliability than that of solid epoxy at four locations indicating that the solid epoxy plays a role in relieving stress of the package, thereby improving the reliability of the package. For the different types of PCB pad, NSMD (non-solder mask defined) pad showed higher reliability than the SMD (solder mask defined) pad. This is because the application of the NSMD pad is more advantageous in terms of thermomechanical stress reliability because the solderpad bond area is larger. In addition, for the different solid epoxy materials with different thermal expansion coefficients, the reliability was more improved when solid epoxy having lower thermal expansion coefficient was used.

• Electronics and Telecommunications Trends
• /
• v.35 no.4
• /
• pp.1-10
• /
• 2020

Since the 1960s, semiconductor packaging technology has developed into electrical joining techniques using lead frames or C4 bumps using tin-lead solder compositions based on traditional reflow processes. To meet the demands of a highly integrated semiconductor device, high reliability, high productivity, and an eco-friendly simplified process, packaging technology was required to use new materials and processes such as lead-free solder, epoxy-based non cleaning interconnection material, and laser based high-speed processes. For next generation semiconductor packaging, the study status of two epoxy-based interconnection materials such as fluxing and hybrid underfills along with a laser-assisted bonding process were introduced for fine pitch semiconductor applications. The fluxing underfill is a solvent-free and non-washing epoxy-based material, which combines the underfill role and fluxing function of the Surface Mounting Technology (SMT) process. The hybrid underfill is a mixture of the above fluxing underfill and lead-free solder powder. For low-heat-resistant substrate applications such as polyethylene terephthalate (PET) and high productivity, laser-assisted bonding technology is introduced with two epoxy-based underfill materials. Fluxing and hybrid underfills as next-generation semiconductor packaging materials along with laser-assisted bonding as a new process are expected to play an active role in next-generation large displays and Augmented Reality (AR) and Virtual Reality (VR) markets.

• Proceedings of the International Microelectronics And Packaging Society Conference
• /
• 2002.05a
• /
• pp.79-84
• /
• 2002

The bottom-leaded plastic(BLP) packages have attracted substantial attention since its appearance in the electronic industry. Since the solder materials have relatively low creep resistance and are susceptible to low cycle fatigue, the life of the solder joints under the thermal loading is a critical issue for the reliability The represent study established a finite element model for the analysis of the solder joint reliability under thermal cyclic loading. An elasto-plastic constitutive relation was adopted for solder materials in the modeling and analysis. A 28-pin BLP assembly is modeled to investigate the effects of various epoxy molding compound, leadframe materials on solder joint reliability. The fatigue life of solder joint is estimated by the modified Coffin-Hanson equation. The two coefficients in the equation are also determined. A new design for lead is also evaluated by using finite element analysis. Parametric studies have been conducted to investigate the dependence of solder joint fatigue life on various package materials.

• Journal of the Microelectronics and Packaging Society
• /
• v.22 no.1
• /
• pp.35-41
• /
• 2015

In this study, in order to improve the reliability of ACF interconnections, solder ACF joints were investigated interms of solder joint morphology and solder wetting areas, and evaluated the electrical properties of Flex-on-Board (FOB) interconncections. Solder ACF joints with the ultrasonic bonding method showed excellent solder wetting by broken solder oxide layers on solder surfaces compared with solder joints with remaining solder oxide layer bonded by the conventional thermo-compression (TC) bonding method. When higher target temperature was used, Sn58Bi solder joints showed concave shape due to lower degree of cure of resin at solder MP by higher heating rate. ACFs with epoxy resins and SAC305 solders showed lower degree of resin cure at solder MP due to the slow curing rate resulting in concave shaped solder joints. In terms of solder wetting area, solder ACFs with $25-32{\mu}m$ diameters and 30-40 wt% showed highest wetted solder areas. Solder ACF joints with the concave shape and the highest wetting area showed lower contact resistances and higher reliability in PCT results than conventional ACF joints. These results indicate that solder morphologies and wetting areas of solder ACF joints can be controlled by adjustment of bonding conditions and material properties of solder and polymer resin to improve reliability of ACF joints.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.13 no.10
• /
• pp.805-811
• /
• 2000

Reliability of PBGA(plastic ball grid array) package is weak compared with normal plastic packages. The low reliability is caused by low resistance to the popcorn cracking, which is generated by moisture absorption in PCB(prited circuit board). In this paper, plasma treatment process was used and we analyzed its effects to interface adhesion. The contents of C and Cl decrease after plasma treatment but those of O, Ca, N relatively increase. The plasma treatment improves the adhesion between EMC(epoxy molding compound) and PCB(solder mask). The grade of improvement was over 100% Max, which depends on the properties of EMC. The RMS(root mean square) roughness value of the solder mask surface increases to plasma treatment. There is little difference of adhesion in RF power and treatment time.

• Journal of Welding and Joining
• /
• v.16 no.4
• /
• pp.92-97
• /
• 1998

Because of the low melting temperature of solder, each temperature cycle initiates an irrecoverable creep deformation at the solder interconnection which connects the package body with the PCB. The crack starts and propagates from the position where the creep deformation is maximized. This work has tried to compare and analyze the thermal fatigue life of solder interconnection which is affected by the lead material, the size of die pad, chip thickness, and interface delamination of 48-Pin TSOP under the temperature cycle ($0^{\circ}C$~1$25^{\circ}C$). The crack initiation position and thermal fatigue life which are calculated by using FEA method are well matched with the results of experiments. The thermal Fatigue life of copper lead frame is extended around 3.6 times longer than that of alloy 42 lead frame. It is maximized when the chip size is matched with the length of the lead. It tends to be extended as the thickness of chip got thinner. As the interfacial delamination between die pad and EMC is increased, the thermal fatigue life tends to decrease in the beginning of delamination, and increase after the delamination grew after 45% of the length of die pad.