• Korean Journal of Materials Research
• /
• v.11 no.6
• /
• pp.508-511
• /
• 2001

Experimental studies of the brittle-ductile transition (BDT) for pre-cracked sapphire single crystals were carried out. The BDT temperature in sapphire single crystals were $1000\pm$$25^{\circ}C$ and 1100$\pm$$25^{\circ}C$ at constant strain rate 3.3$\times$$10^{-5}$/sec and 3.3$\times$$10^{-6}$/sec, respectively. With aid of the BDT model, the activation energy for prism plane slip {1120} <1100> dislocation velocity was in the range of 4.6$\pm$2.3eV This activation energy for dislocation velocity with BDT model was compatible with the result of the dislocation velocity (3.8eV) using the etch-pit techniques.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.05c
• /
• pp.178-181
• /
• 2003

In this work, we etched PZT films with various additive gases ($O_2$ and Ar) in $Cl_2/CF_4$ plasmas, while mixing ratio was fixed at 8/2. After the etching, the plasma induced damages are characterized in terms of hysteresis curves, leakage current, retention properties, and switching polarization. When the electrical properties of PZT etched in $O_2$ or Ar added $Cl_2/CF_4$ were compared, the value of remanent polarization in $O_2$ added $Cl_2/CF_4$ plasma is higher than that in Ar. added plasma. The maximum etch rate of the PZT thin films was 145 nm/min for 30% Ar added $Cl_2/CF_4$ gas having mixing ratio of 8/2 and 110 nm/min for 10% $O_2$ added to that same gas mixture. In order to recover the ferroelectic properties of the PZT thin films after etching, we annealed the etched PZT thin films at $550^{\circ}C$ in an $O_2$ atmosphere for 10 min. From the hysteresis curves, leakage current, retention property and switching polarization, the reduction of the etching damage and the recovery via the annealing was turned out to be more effective when $O_2$ was added to $Cl_2/CF_4$ than Ar. X-ray diffraction (XRD) showed that the structural damage was lower when $O_2$ was added to $Cl_2/CF_4$. And the improvement in the ferroelectric properties of the annealed samples was consistent with the increased intensities of the (100) and the (200) PZT peaks.

• Transactions on Electrical and Electronic Materials
• /
• v.13 no.3
• /
• pp.157-161
• /
• 2012

In this study, we investigated the etching characteristics of ITO thin films and the effects of inert gases added to $Cl_2/BCl_3$ inductivity coupled plasma. The maximum etch rate of ITO thin film was 130.0 nm/min upon the addition of Ar (6 sccm) to the $Cl_2/BCl_3$ (4:16 sccm) plasma, which was higher than that with He or $N_2$ added to the plasma. The ion bombardment by $Ar^+$ sputtering was due to the relatively low volatility of the by-products formed in the $Cl_2/BCl_3$ (4:16 sccm) plasma. The surface of the etched ITO thin film was characterized by x-ray photoelectron spectroscopy (XPS) and atomic force microscopy (AFM). From the XPS results, it is concluded that the proper addition of Ar and He to the $Cl_2/BCl_3$ plasma removes carbon and by-products from the surface of the etched ITO thin film.

• Journal of Sensor Science and Technology
• /
• v.8 no.3
• /
• pp.291-297
• /
• 1999

The plasma etching of tungsten thin films has been studied with $SF_6$ gas in RIE system. The etch rate of ${\alpha}$-phase W film with $SF_6$ gas plasma has been showed to depend strongly on process parameters ($SF_6$, $SF_6-N_2$ gas). Effect of $N_2$ addition and etching selectivity between W film and photoresist have also been studied in detail. Etching profiles between W film and photoresist were investigated by SEM. The compounds on W surface after $SF_6-N_2$ gas plasma treatment were examined by XPS and the concentration of F ions was detected by OES during plasma on.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2000.02a
• /
• pp.175-175
• /
• 2000

Si(100) surfaces were exposed to gas-phase thermal-energy hydrogen atoms, H(g). We find that thermal H(g) atoms etch, amorphize, or penetrate into the crystalline silicon substrate, depending on the employed Ts range during the H(g) exposure. We find that etching is enhanced as Ts is lowered in the 300-700K range, while amorphous silicon hydride (a-Si:H) formation dominates at a Ts below 300K. This result was well explained by the fact that formation of the etching precursor, SiHx(a), and amorphization are both facilitated by a lower Ts, whereas the final step for etching, SiH3(a) + H(g) longrightarrow SiH3(g), is suppressed at a lower Ts. we also find that direct absorption of H(g) by the crystalline bulk of Si(100) substrate occurs within a narrow Ts window of 420-530K. The bulk-absorbed hydrogen evolved out molecularly from Si(100) at a Ts 80-120K higher than that for surface monohydride phase ($\beta$1) in temperature-programmed desorption. This bulk-phase H uptake increased with increasing H(g) exposure without saturation within our experimental limits. Direct absorption of H(g) into the bulk lattice occurs only when the surface is atomically roughened by surface etching. While pre-adsorbed hydrogen atoms on the surface, H(a), were readily abstracted and replaced by D(g), the H atoms previously absorbed in the crystalline bulk were also nearly all depleted, albeit at a much lower rate, by a subsequent D(g) at the peak temperature in TPD from the substrate sequentially treated with H(g) and D(g), together with a gas phase-like H2 Raman frequency of 4160cm-1, will be presented.

• Journal of the Korean Vacuum Society
• /
• v.20 no.3
• /
• pp.182-188
• /
• 2011

Polysilazane and polymethylsilazane based precursor films were deposited on Si-substrate by spin-coating, subsequently annealed at $150{\sim}850^{\circ}C$, and characterized. Structural analysis, shrink, compositional change, etch rate, and gap-filling were observed. Annealing the precursor films led to formation of spin-on dielectric films. C-containing precursor films showed that less loss of N, H, and C while less gain of O than that of C-free precursor films at $400^{\circ}C$, but more loss of N, H, and C while more gain of O at $850^{\circ}C$. Thus polysilazane based precursor films exhibited less reduction in thickness of 14.5% than silazane based one of 15.6% at $400^{\circ}C$ but more 37.4% than 19.4% at $850^{\circ}C$. FTIR indicated that C induced smaller amount of Si-O bond, non-uniform property, and lower resistance to chemical etching.

• Journal of the Semiconductor & Display Technology
• /
• v.18 no.4
• /
• pp.35-39
• /
• 2019

Effect of Ge₂Sb₂Te₅ (GST) chalcogen composition on plasma induced damage was investigated by using Ar ions and F radicals. Experiments were carried out with three different modes; the physical etching, the chemical etching, and the ion-enhanced chemical etching mode. For the physical etching by Ar ions, the sputtering yield was obtained according to ion bombarding energy and there was no change in GST composition ratio. In the plasma mode, the lowest etch rate was measured at the same applied power and there was also no plasma induced damage. In the ion-enhanced chemical etching conditions irradiated with high energy ions and F halogen radicals, the GST composition ratio was changed according to the density of F radicals, resulting in higher roughness of the etched surface. The change of GST composition ratio in halogen plasma is caused by the volatility difference of GST-halogen compounds with high energy ions over than the activation energy of surface reactions.

• Applied Chemistry for Engineering
• /
• v.22 no.2
• /
• pp.230-234
• /
• 2011

In this work, the primary material for a single layered hardmask which can afford a spin-on process was prepared by the minture of organic and inorganic sources. The preparation of hybrid polymer was attempted by esterification from silanol terminated siloxane compounds and acetonide-2,2-bis(methoxy)propionic acid. The optical, thermal and morphological properties of the test hardmask film was examined in terms of cross-linking agent and additives. In addition, the etch rate of hardmask film and photo resist layer were compared. The hybrid polymer prepared from organic and inorganic materials was found to be useful for hardmask film to form the nano-patterns.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.30 no.2
• /
• pp.66-72
• /
• 2020

The difference of plasma resistance between the CAS glass bulk and coating films were compared. Plasma resistance was confirmed by analyzing the etch rate and the microstructure of the surface when the CAS glass bulk and the glass coating film were etched with CF₄/O₂/Ar plasma gas. CAS glass coating film was etched up to 25 times faster than the glass bulk. A statistically high correlation between the surface roughness and the etching rate of the coating film was derived, and thus, the high surface roughness of the coating film was determined to cause rapid etching. In addition, cristobalite crystals that has a low Ca content and a high Si content, was foamed on the glass coating film. Therefore, the CAS glass coating film is considered to have low plasma resistance compared to the glass bulk.

• Korean Journal of Materials Research
• /
• v.4 no.1
• /
• pp.63-74
• /
• 1994

The ultrathin oxide films less than 100$\AA$ were grown by thermal oxidation in $N_2O$ ambient to improve the controllability of thickness, thickness uniformity, process reproducibility and their electrical properties. Oxidation rate was reduced significantly at very thin region due to the formation of oxynitride layer in $N_2O$ ambient and moreover nitridation of the oxide layer was simultaneously accompanied during growth. The nitrogen incorporation in the grown oxide layer was characterized with the wet chemical etch-rate and ESCA analysis of the grown oxide layer. All the oxides thin films grown in $N_2O$, pure and dilute $O_2$ ambients show Fowler-Nordheim electrical conduction. The electrical characteristics of thin oxide films grown in $N_2O$ such as leakage current, electrical breakdown, interface trap density generation due to the injected electron and reliability were better than those in pure or dilute ambient. These improved properties can be explained by the fact that the weak Si-0 bond is reduced by stress relaxation during oxidation and replacement by strong Si-N bond, and thus the trap sites are reduced.