• Transactions of the Korean Society of Automotive Engineers
• /
• v.12 no.2
• /
• pp.117-122
• /
• 2004

The fatigue life in wheels was predicted by simulating the experimental method using Finite-Element analysis. Based on a high frequency fatigue property, calculations of the stresses in wheels were performed by simulating the rotating bending fatigue test. Wheels made of an aluminum alloy(A356.2) were tested using a bending fatigue tester. Results from bending fatigue test showed a linear correlation between bending moment and stress amplitude. Consequently, Finite-Element calculations were performed by a linear analysis. In order to find stress-cycles curves, spoke parts of wheel were tested using a rotary bending fatigue tester. Also, highly accurate Finite-Element analysis requires regression lines and confidence intervals from these results. In conclusion, if the fatigue data related to the material and manufacturing procedure are reliable, the prediction on fatigue lift in wheels can be carried out with high accuracy.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09a
• /
• pp.381-382
• /
• 2006

A comparative study is made on root bending fatigue performance of spur gears and plane bending fatigue performance of notched test bars. R = 0 root bending fatigue tests are made on small spur gears with critical root radius 1.0 mm. The results are compared to plane bending fatigue tests of 0.9 mm radius notched specimens. Results are presented for tests on 4%Ni/2%Cu/1.5%Mo prealloyed PM steel with addition of about 0.6% graphite. Predicted values from the test bars coincide well with the results obtained from the gear root fatigue tests.

• Proceedings of the KSR Conference
• /
• 2011.10a
• /
• pp.3059-3064
• /
• 2011

A Trolley line is a very important equipment among electric railway equipments since it contacts directly with pantograph and supplies electricity on the electromotive. Such it was thought that a trolley line need not to consider fatigue since the replace cycle by wear is shorter than the replace cycle by fatigue breakage. But, the bending fatigue breakage accidents occurred several times at the Shinkansen trolley line in East Japan Railway Company. Therefore, in case of a new developed trolley line, the evaluation for bending fatigue life became more important, But, since there are not an authorized fatigue test method and a testing device for the trolley line, the quantitative evaluation is difficult. In this study, we analyzed the load and environment condition of trolley line used in the actual spot and the developed testing device that can evaluate bending fatigue properties of the trolley line as simulating the real condition. The bending fatigue test of the trolley line was achieved using the developed testing device and estimated the fatigue life of trolley line and also, established the fatigue test process.

• Journal of the Korean Society for Railway
• /
• v.13 no.2
• /
• pp.201-207
• /
• 2010

The replacement criterion of rail by accumulated passing tonnage was estimated by the bending fatigue life of rail. In order to estimate the bending fatigue life, it is basically needed to analyze bending fatigue behavior on the rail. In this study, the bending fatigue test were performed for 50kg/m and 60kg/m rails, and test specimens were distinguished by new and used rails and by the types of welded rail such as base material, thermite weld, and gas pressure weld. Also, this study analyzed the fractured surface, the position of initial crack and the bending fatigue behavior (S-N curve). Therefore, it evaluated S-N curve for welded rails according to the fracture probability. The result from this study might be used essential data in order to estimate the bending fatigue life of rail by the accumulated passing tonnage.

• Journal of Welding and Joining
• /
• v.19 no.1
• /
• pp.112-117
• /
• 2001

The factor affecting on the fatigue strength of spot welded specimen have been studied. To analyze and predict crack initiation position and propagation directions on the spot welded area are very important for strength design of the automobile body structure. In fact, there are a various of loads in running automobile but, it is impossible to replay like an actual conditions in the laboratory. So, in this study tensile-shear type and in-plane bending type specimens were used in fatigue test and includes an analysis of fatigue crack initiation position and propagation directions about earth specimens. The results obtained in the present study are summarized as follows: 1. In tensile-shear type fatigue test, the region of fatigue crack initiation position was affected by out-of-plane bending deformation due to bending angle. 2 In in-plane bending type fatigue test, the behavior of fatigue crack initiation position and propagation derections due to angle between upper plate and lower plate was dominated by magnitude of in-plane bending moment.

• Journal of the Microelectronics and Packaging Society
• /
• v.24 no.4
• /
• pp.47-52
• /
• 2017

Recently, a great attention has been paid to the mechanical behavior of ITO (Indium Tin Oxide) film, which is widely used in current smart devices due to its excellent electrical properties and transparency. In this study, the reliability of ITO thin films on flexible substrates was investigated using bending test and bending fatigue test. According to the relative position of ITO and substrate, the experiment was conducted on both outer and inner bending conditions. Inner bending condition exhibited superior electrical stability compared to outer bending test. The electrical resistance during outer bending fatigue test significantly increased compared to that in the inner bending fatigue. The crack nucleation and propagation differs according to the stress state and they have a great influence on the electrical resistance. The crack morphologies were observed by scanning electron microscopy.

• Journal of the Korean Society for Precision Engineering
• /
• v.17 no.1
• /
• pp.61-67
• /
• 2000

Gears are the most commonly used parts in automotive and industrial applications. One of most common modes of gear failures is tooth breakage, which is usually produced by the bending fatigue failure. It is important to manufacture the gears which can withstand the applied stresses in view of safety and economic requirement. This paper deals with bending fatigue strength for cold forged bevel gear. Especially, to compare fatigue characteristics for manufacturing processes difference, bending fatigue tests of bevel gears made by three different processes respectively. Results indicate that the fatigue strength of bevel gear is improved by cold forging process. Intergranular fracture is found on fatigue fracture surface, and dimples are observed on final fracture surface. The fatigue failure cannot be considered as a deterministic quantity, but must be characterized statistically. This study proposes a method to estimate bending fatigue lift of the bevel gear using the probability-load-life and Weibull analysis.

• Korean Journal of Metals and Materials
• /
• v.46 no.2
• /
• pp.80-87
• /
• 2008

Many researches related to the reliability of Pb-free solder joints with PCB (printed circuit board) surface finish under thermal or vibration stresses are in progress, because the electronics is operating in hash environment. Therefore, it is necessary to assess Pb-free solder joints life with PCB surface finish under thermal and mechanical stresses. We have investigated 4-points bending fatigue lifetime of Pb-free solder joints with OSP (organic solderability preservative) and ENIG (electroless nickel and immersion gold) surface finish. To predict the bending fatigue life of Sn-3.0Ag-0.5Cu solder joints, we use the test coupons mounted 192 BGA (ball grid array) package to be added the thermal stress by conducting thermal shock test, 500, 1,000, 1,500 and 2,000 cycles, respectively. An 4-point bending test is performed in force controlling mode. It is considered that as a failure when the resistance of daisy-chain circuit of test coupons reaches more than $1,000{\Omega}$. Finally, we obtained the solder joints fatigue life with OSP and ENIG surface finish using by Weibull probability distribution.

• Journal of Welding and Joining
• /
• v.16 no.2
• /
• pp.84-92
• /
• 1998

On this study, the variations of hardness and microstructure were observed at he spot-welded part of 5182 alminum alloy sheets with thickness of 1.2 mm. The hardness of spot-welded part of aluminum alloy indicated the lowest value at nugget center. Also, the position where fatigue crack exists was investigated by surveying microstructure of the spot-welded sections. Mean load-deformation diagrams were obtained from static tensile test. Fracture was occurred completely within 5 mm after transforming elastic into plastic area. Fatigue test was stopped when the specimens of fatigue test had the final displacement of 0.2mm and measured fatigue bending angle and crack length. This study utilized them, investigated the relations between fatigue bending angle and fatigue crack length and made a estimation of the fatigue fracture life of resistance spot welded part of 5182 aluminum alloy sheet. The relative equation o fatigue crack length and fatigue failure life can be represented by {TEX}$L_{C}${/TEX}=α{TEX}$N_{f}^ {β}${/TEX}.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.9 no.1
• /
• pp.25-34
• /
• 2010

Fretting damage reduces fatigue life of the material due to low amplitude cyclic sliding and changes in the contact surfaces of strongly connected machine and structures such as bolt, key, fixed rivet and connected shaft, which have relative slip of repeatedly very low frequency amplitude. In this study, the fretting fatigue behavior of 7050-T7451 aluminum alloys used mainly in aircraft and automobile industry were evaluated. The plain fatigue test and fretting fatigue test under cyclic bending load carried out commercial bending fatigue tester and specially devised equipments to cause fretting damage. From these experimental work, the following results obtained: (1) The plain fatigue limit for stress ratio R=-l was about 151MPa. (2) In case of fretting fatigue, fatigue limit for stress ratio R=-l about 72MPa, the fatigue limit for R=0 about 81MPa, and the fatigue limit for R=0.3 about 93MPa. (3) The fatigue limit reduction rates by the fretting damage were about 52%(R=-1), 46%(R=0) and 38%(R=0.3) respectively. (4) The fatigue limit reduction rate decreased with stress ratio increase. In fretting bending test, as stress ratio increased, occurrence of initial oblique crack by fretting decreased or phased out, so that fracture surfaces were formed by plain fatigue crack occurrence, and such tendency was notable as stress amplitude increased. (5) Tire tracks and rubbed scars were observed in the fracture surface and contacted surface.