• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.25 no.4
• /
• pp.253-257
• /
• 2016

The effects of re-peening on the compressive residual stress and fatigue life of Al7075-T6 were investigated. The compressive residual stress induced on the surface of components by shot peening is known to increase the fatigue life. However, the fatigue load relaxes the compressive residual stress of components. Re-peening is a technique to again induce the relaxed compressive residual stress and increase the total fatigue life of components. In this study, the re-peening process was applied to fatigue-loaded specimens. The compressive residual stress and fatigue life were examined for re-peened specimens with fatigue ratios of 30%, 50%, and 70%. The results showed that the compressive residual stress of the specimens was relaxed under the fatigue load. The re-peening process significantly increases the compressive residual stress and total fatigue life.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.18 no.12
• /
• pp.3149-3158
• /
• 1994

In this paper, using the formulation of dynamic equivalent load considering the effects of moment load and the equation to estimate the cage rotational speed, the new life equation of deep groove ball bearing under radial and moment loads was proposed. Fatigue life test apparatus with the measuring equipment of shaft and cage speed was designed and developed to be capable of subjecting combined radial and moment load. Fatigue life tests were executed by sudden death test method and the reliability of fatigue lives was evaluated by Weibull distribution analysis. From the results of fatigue tests and analysis, the relationships between film parameters and life adjustment factors were acquired. And it was turned out that so as to estimate the effect of moment load on fatigue life, the life adjustment factor as well as the dynamic equivalent load must be taken into account.

• Journal of the Korean Society for Precision Engineering
• /
• v.19 no.12
• /
• pp.127-133
• /
• 2002

The objective of this study is to investigate fatigue life and fatigue crack propagation behavior The experiment of fatigue life for MMC have been carried out for the stress ratio R＝0.1 at 20Hz. Fatigue lift limit of AC4CH alloy is about 70 ㎫ and Fatigue limit of MMC has been increment to 120 ㎫, therefore, fatigue limits of MMC is about 71 % higher than that of AC4CH alloy Crack propagation tests on half-size CT specimen of thickness 12.5mm were conducted by using sinusoidal waveform. The crack length was monitored by compliance method. Test conditions were at 0.1 and 0.05 of load ratio at 10Hz of loading frequency and test load was 2.3kN. The effects of stress ratio on the fatigue crack propagation behavior for MMC was discussed within the Paris law. As the results of this study, Fatigue crack propagation increased with increasing the load ratio.

• Journal of the Korean Society of Mechanical Technology
• /
• v.13 no.2
• /
• pp.31-37
• /
• 2011

Sheet aluminum alloys have been used in manufacturing of machine structures. In fatigue crack propagation behavior of thin sheet aluminum alloys, it is important that fatigue crack growth rate is affected by crack closure phenomenon. In this work, we analyzed the characteristics of fatigue crack propagation behavior in experiment of constant stress condition for thin sheet Al 2024-T3 alloys, and identified the retardation behavior of crack growth by comparing experimental results of thin and thick plate specimen. We attempt to operate the fatigue life estimating process using the fatigue related material constants from referred fatigue crack propagation analysis. And we analyzed the experimental and prediction results of fatigue life of thin sheet aluminum alloy in order to identify the relation between retardation behavior of fatigue crack growth and crack closure phenomenon.

• Journal of the Society of Naval Architects of Korea
• /
• v.45 no.6
• /
• pp.679-687
• /
• 2008

The fatigue life of ship structure under cyclic loading condition is made up of crack initiation and propagation stages. For a welding member in ship structure, the fatigue crack propagation life is more important than the fatigue crack initiation life. To calculate precisely the fatigue crack propagation life at the critical welding location, the knowledge of the residual stress sensitivity on the fatigue strength is necessary. In this study, thermo elastic-plastic analysis was conducted in order to examine the effect of residual stress on the fatigue crack propagation life. Also the fatigue crack propagation lives considering residual stress were calculated using fatigue crack growth code, AFGROW, on the basis of fracture mechanics. AFGROW is widely used for fatigue crack growth predictions under constant and variable amplitude loading. The reliability of AFGROW on the fatigue of ship structure was confirmed by the comparison of the estimated results with the fatigue propagation test results.

• Special Issue of the Society of Naval Architects of Korea
• /
• 2009.09a
• /
• pp.87-92
• /
• 2009

CSR for bulk carrier has been required 25 years operation life in North Atlantic condition. As the fatigue life requirement of ship structure is increased it is necessary to study to satisfy the fatigue life which is much severe. Therefore from the fatigue analysis, especially fatigue strength for double bottom & lower stool connection area is not enough. To satisfy the fatigue life, it needs to increase double bottom strength or insert thicker plate. In this study, the consideration though structure modification have been doe with 81K bulk carrier and to find the solution of fatigue problem.

• Proceedings of the KSME Conference
• /
• 2001.11a
• /
• pp.99-104
• /
• 2001

Effect of mean stress on the fatigue life of natural rubber for engine mount was investigated. Fatigue damage parameter based on the maximum Green-Lagrange strain was employed to account for the effect of mean stress. A procedure to predict the fatigue life of rubber components based on the maximum Green-Lagrange strain method was proposed. Nonlinear finite element analysis and fatigue test of jang-gu shape specimen were conducted to predict the fatigue life of engine mount. Predicted fatigue lives have a good agreement with tested lives within a factor of 3.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.16 no.3
• /
• pp.137-143
• /
• 2008

For most bearings, it is a common requirement to have long durability. Especially wheel bearing fatigue life is the most important in automotive quality. The contact fatigue life analysis of automotive wheel bearing considering real raceway rough surface is presented in this paper. Contact stresses are obtained by contact analysis of a semi-infinite solid based on the use of influence functions; the subsurface stress field is obtained using rectangular patch solutions. Mesoscopic multiaxial fatigue criterion which can yield satisfactory results for non-proportional loading is then applied to predict fatigue damage. Suitable counting method and damage rule were used to calculate the fatigue life of random loading caused by rough surface. The life analysis considering real rough surface of wheel bearing raceway is in good agreement with the experimental results.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.12 no.4
• /
• pp.181-190
• /
• 2004

The interest of the fatigue life of rubber components such as engine mounts is increasing according to the extension of warranty period of the automotive components. Automotive engine mounts get damaged due to thermal and mechanical loadings. This paper discusses a fatigue life prediction of the 3-dimensional dumbbell specimens for natural rubber compound considering the effects of maximum strain and heat aging temperature. Displacement controlled fatigue life tests were performed using specimens with different levels of maximum strain and various hardness. The basic mechanical properties test and the fatigue test of aged rubber specimen under normal and elevated temperature were executed. A procedure to predicted the fatigue life of vulcanized natural rubber material based on the maximum strain method was proposed, and then this curve was in good agreement with fatigue test data less than 200% error range.

• Journal of Welding and Joining
• /
• v.19 no.4
• /
• pp.406-412
• /
• 2001

This study is focussed on the numerical prediction of the thermal fatigue life of a ${\mu}BGA$(Micro Ball Grid Array) solder joint. Numerical method is used to perform three-dimensional finite element analysis for Sn-37mass%Pb. Sn-3.5mass%Ag solder alloys during the given thermal cycling. Strain values, along with the result of mechanical fatigue tests for solder alloys were then used to predict the solder joint fatigue life using the Coffin-Manson equation. In this study, a practical correlation for the prediction of the thermal fatigue life is suggested by using the dimensionless variable $\gamma$. As a result. it could be found that Sn-3.5mass%Ag has longer fatigue life than Sn-37mass%Pb in low cycle fatigue. In addition. the result with ${\gamm}ashow$a good agreement with the FEA results.