• The Transactions of the Korean Institute of Electrical Engineers P
• /
• v.51 no.2
• /
• pp.77-81
• /
• 2002

In this study, PZT thin films were fabricated using sol-gel processing onto Si/$SiO_2$/Ti/Pt substrates. PZT sol with different Zr/Ti ratio(20/80, 30/70, 40/60, 52/48) were prepared, respectively. The films were fabricated by using the spin-coating method on substrates. The films were heat treated at $450^{\circ}C$, $650^{\circ}C$ by rapid thermal annealing(RTA). The preferred orientation of the PZT thin films were observed by X-ray diffraction(XRD), and Scanning electron microscopy(SEM). All of the resulting PZT thin films were crystallized with perovskite phase. The fine crystallinity of the films were fabricated. Also, we found that the ferroelectric properties from the dielectric constant of the PZT thin films were over 600 degrees, P-E hysteresis constant. And the leakage current densities of films were lower than $10^{-8}A/cm^2$. It is concluded that the PZT thin films by sol-gel process to be convinced of application for ferroelectric memory device.

• Proceedings of the KIEE Conference
• /
• 2005.11a
• /
• pp.87-89
• /
• 2005

$Bi_{3.25}Y_{0.75}Ti_{3}O_{12}$[BYT] ferroelectric thin films were deposited by RF-Sputtering method on the $Pt/Ti/SiO_2/Si$. We investigated the effects of processing condition (especially post-annealing) on the structural and ferroelectric properties of the BYT thin films. Increasing the annealing temperature, the peak intensity of (117) increased and c-axis orientation decreased. The BYT thin films crystallized well at $600^{\circ}C$ for 30min. No secondary phases observed in the XRD pattern. At annealing temperature of $700^{\circ}C$, the thin films had no cracks and the grain was uniform. The calculated lattice constants of BYT thin films were a=0.539nm, b=0.536nm, c=3.288nm. The remnant polarization of the $Bi_{3.25}Y_{0.75}Ti_{3}O_{12}$ capacitor reached $1.8uC/cm^2$ at an applied field about 400kV/cm. The BYT thin films can be used as capacitors in Ferroelectric Random Access Memory device.

• Journal of the Korean Ceramic Society
• /
• v.43 no.11 s.294
• /
• pp.688-692
• /
• 2006

Ferroelectric lanthanides-substituted $Bi_4Ti_3O_{12}$ $(Bi_{4-x}Ln_xTi_3O_{12}, BLnT)$ thin films approximately 200 nm in thickness were deposited by metal organic chemical vapor deposition onto Pt(111)/Ti/SiO$_2$/Si(100) substrates. Many researchers reported that the lanthanides substitution for Bi in the pseudo-perovskite layer caused the distortion of TiO$_6$ octahedron in the a-b plane accompanied with a shift of the octahedron along the a-axis. In this study, the effect of lanthanides (Ln=Pr, Eu, Gd, Dy)-substitution and crystallization temperature on their ferroelectric properties of bismuth titanate $(Bi_4Ti_3O_{12}, BIT)$ thin films were investigated. As BLnT thin films were substituted to lanthanide elements (Pr, Eu, Gd, Dy) with a smaller ionic radius, the remnant polarization (2P$_r$) values had a tendency to increase and made an exception of the Eu-substituted case because $Bi_{4-x}Eu_xTi_3O_{12}$ (BET) thin films had the smaller grain sizes than the others. In this study, we confirmed that better ferroelectric properties can be expected for films composed of larger grains in bismuth layered peroskite materials. The crystallinity of the thin films was improved and the average grain size increased as the crystallization temperature,increased from 600 to 720$^{\circ}C$. Moreover, the BLnT thin film capacitor is characterized by well-saturated polarization-electric field (P-E) curves with an increase in annealing temperature. The BLnT thin films exhibited no significant degradation of switching charge for at least up to $1.0\times10^{11}$ switching cycles at a frequency of 1 MHz. From these results, we can suggest that the BLnT thin films are the suitable dielectric materials for ferroelectric random access memory applications.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.20 no.3
• /
• pp.223-227
• /
• 2007

The effect of Eu contents on the ferroelectric properties of $Bi_{4-x}Eu_xTi_3 O_{12}$ (BET) thin films has been investigated. Bismuth Europium titanate thin films with a Eu contents were prepared on the $Pt/Ti/SiO_2/Si$ substrate by metal-organic decomposition technique. The structure and the morphology of the films were analyzed using X-ray diffraction (XRD) and field emission scanning microscopy (FE-SEM), respectively. From the XRD analysis, it was found that BET thin films have polycrystalline structure, and the layered-perovskite phase is obtained when the Eu contents exceeds 0.2 (x > 0.2). Also, the ferroelectric characteristics of the BET thin films were found to be dependent on the Eu content. Particularly, the BET films doped with x = 0.75 show better ferroelectric properties (remanent polarization 2Pr = 60.99 C/$cm^2$ and only a little polarization fatigue up to $3.5{\times}10^9$ bipolar switching cycling) than those doped with other Eu contents.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1998.11a
• /
• pp.335-338
• /
• 1998

Ferroelectric Sr$_2$(Nb,Ta)$_2$O$_{7}$ (SNTO) thin films were prepared by chemical solution deposition processes. SNTO thin films were spin-coated on Pt/Ti/SiO$_2$/(100)Si substrates. After multiple coating, dried thin films were heat-treated for decomposition of residual organics and crystallization. B site-rich impurity phase, i.e. [Sr(Nb,Ta)$_2$O$_{6}$], was found after annealing, where its appearance was dependent on process temperature indicating the possible reaction with substrate. Dielectric and other relevant electrical properties were measured and the results showed a little possibility in ferroelectric gate random access memory devices.s.s.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.07b
• /
• pp.861-864
• /
• 2002

Ferroelectric $Bi_{4-x}Nd_xTi_3O_{12}$(BNdT) thin films with the composition(x=0.75) were prepared on pt/Ti/$SiO_2$/Si(100) substrate by metal-organic deposition. The electrical and structural characteristics of BNdT thin films were investigated to develop ferroelectric thin films for capacitor layers of FRAM. After spin coating, thin films were annealed at $650^{\circ}C$ for 1hour in oxygen atmosphere. Scanning electron micrographs showed uniform surfaces composed of rod-like grains. The $Bi_{4-x}Nd_xTi_3O_{12}$(X=0.75) thin film capacitors with a Pt top electrode showed better ferroelectric properties. At the applied voltage of 5V, the dielectric constant$(\varepsilon_r)$, dissipation factor$(tan{\delta})$, remanent polarization(2Pr) and nonvolatile swiching charge of the $Bi_{4-x}Nd_xTi_3O_{12}$(x=0.75)thin films were about 346.7, 0.095, $56{\mu}C/cm^2$ and $38{\mu}C/cm^2$ respectively. Also the capacitor did not show any significant fatigue up to $8{\times}10^{10}$ read/write switching cycles at a frequency of 1MHz.

• Journal of the Korean Ceramic Society
• /
• v.42 no.11 s.282
• /
• pp.763-769
• /
• 2005

Ferroelectric $ReMnO_3$(Re:Ho, Er) thin films were deposited on Si(100) substrate by Metal-Organic Chemical Vapor Deposition (MOCVD). Crystallinity and electric properties of $ReMnO_3$(Re:Ho, Er) thin films were investigated as a function of thermal heat treatment process, CHP (Conventional Heat-treatment Process) and RTP (Rapid Thermal Process). $ReMnO_3$(Re:Ho, Er) thin films prepared by RTP showed higher c-axis preferred orientation and homogeneous surface roughness than those prepared by CHP. The remnant polarization of ferroelectric hysteresis loop of $ReMnO_3$(Re:Ho, Er) thin films was strongly dependent on the c­axis preferred orientation of hexagonal single phase, and the leakage current characteristics of thin films were dependent on the homogeneity of grain size as well as surface roughness of thin films.

• Korean Journal of Materials Research
• /
• v.16 no.6
• /
• pp.394-399
• /
• 2006

Ferroelectric $HoMnO_3$ thin films were deposited on the Si(100) substrate at $700^{\circ}C$ for 2 hrs by metalorganic chemical vapor deposition (MOCVD) and post-annealed at 850oC by rapid thermal process (RTP). Electrical properties and crystalline phases of $HoMnO_3$ thin films were investigated as a function of postannealing time. Single phase of hexagonal symmetry with c-axis preferred orientation was obtained from $HoMnO_3$ thin films post-annealed at $850^{\circ}C$ for 5 min, while the c-axis preferred orientation was decreased with the increase of post-annealing time, and the thin films post-annealed at $850^{\circ}C$ for 15 min showed the mixture phases of hexagonal and orthorhombic symmetry. P-E (Polarization-Electric field) hysteresis loop of ferroelectric $HoMnO_3$ thin films was observed only for the single phase of hexagonal symmetry, but that was not observed for the mixture phases of the hexagonal and orthorhombic symmetry, which was discussed with the bond valence of Mn ion of crystalline phase. Leakage current density was dependent on the microstructure of thin films as well as the change of valence of Mn ion.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1999.05a
• /
• pp.509-512
• /
• 1999

Ferroelectric Sr$_2$(Nb, Ta)$_2$O$_{7}$(SNTO), La$_2$Ti$_2$O$_{7}$(LTO) thin films were prepared by sol-gel processes. SNTO, LTO thin films were spin-coated on Pt/TiO$_2$/SiO$_2$/Si(100). Pt/Ti/SiO$_2$/Si(100). PT/ZrO$_2$/SiO$_2$/Si(100) substrates. After multiple coating, dried thin films were heat-treated for decomposition of residual organics and crystallization. Dielectric and other relevant electrical properties were measured and the results showed a little possibility in ferroelectric gate random access memory devices.ces.

• Proceedings of the KIEE Conference
• /
• 2006.10a
• /
• pp.101-102
• /
• 2006

PZT thin films, which are the representative ferroelectric materials in ferroelectric random access memory (FRAM), have some serious problem such as the imprint, retention and fatigue which ferroelectric properties are degraded by repetitive polarization. BL T thin film capacitors were fabricated by plasma etching, however, the plasma etching of BLT thin film was known to be very difficult. In our previous study, the ferroelectric materials such as PZT and BLT were patterned by chemical mechanical polishing (CMP) using damascene process to top electrode/ferroelectric material/bottom electrode. It is also possible to pattern the BLT thin film capacitors by CMP, however, the CMP damage was not considered in the experiments. The properties of BLT thin films were changed by the change of polishing pressure although the removal rate was directly proportional to the polishing pressure in CMP process.