• Journal of the Korean Ceramic Society
• /
• v.48 no.5
• /
• pp.348-353
• /
• 2011

By gel-casting, the silicon-polymer green bodies were prepared for silicon nitride ceramics, sintered by microwave gas phase reaction. Considering the viscosity and the idle time of slurries, we decided the operational conditions of related processes, and the optimum concentrations of raw materials powders, organic monomers, cross-linker, dispersant, initiator, and catalyst. So we could get the machinable green bodies, having about 50 MPa of bending strength without cracks by selecting drying conditions carefully.

• Transactions of Materials Processing
• /
• v.31 no.5
• /
• pp.290-295
• /
• 2022

Recently, the use of high-tech ceramic parts in functional electronic parts, automobile parts and semiconductor equipment parts is increasing. These ceramics materials are required to have high reproducibility, reliability, large size and complex shapes. The researchers initiated the work to develop a new shaping method called gel casting, which allows high performance ceramic materials with a complex shape to be produced. The manufacturing process parameters of gel casting include uniform mixing of the initiator, bubble removal, and slip injection. In this study, we analyzed the dispersion and gelation characteristics according to the change in the additive content of the alumina slurry in the gel casting process. The alumina slurry for gel casting was prepared by mixing a solvent, a monomer and a dispersant through a ball mill. Alumina powder and a gelation initiator were added to the mixed solution, and ball milling was performed for 24 hours. A viscosity of 6,435 cps and a stable zeta potential value were obtained under the conditions of alumina powder content of 55 vol% and dispersant 2.0 wt%. After curing for 12 hours by adding aps 0.1wt%, TEMED 0.2wt%, and Monomer 3, 5wt%, it was possible to separate from the molding cup, confirming that the gelation was completed.

• Journal of the Korean Ceramic Society
• /
• v.40 no.12
• /
• pp.1159-1164
• /
• 2003

Two processing routes (i.e., the gel casting and polymer preform routes) using polymer beads were studied to fabricate porous ceramics with a cellular structure. The gel casting route, comprising the gel casting of a ceramic slurry mixed with polymer beads, was found to be inadequate to produce porous ceramic bodies with a interconnected pore structure, due to complete coating of the slurry on the polymer beads, which left just isolated pores in the final sintered bodies. The polymer preform route, involving the infiltration of a polymer beads preform with the ceramic slurry, successfully produced porous ceramics with a highly interconnected network of spherical pores. The pore size of 250-300 $\mu\textrm{m}$ was demonstrated and the porosity ranged from 82 to 86%. This process is advantageous to control the pore size because it is determined by the sizes of polymer beads used. Another feature is the avoidance of hollow skeleton, giving a high strength.

• Journal of the Korean Ceramic Society
• /
• v.52 no.6
• /
• pp.449-454
• /
• 2015

The fabrication process of zirconia gel-casting was studied to obtain dense zirconia on a large scale or with complicated shapes. As an experimental parameter, two different particle sizes ($0.1{\mu}m$ and $0.7{\mu}m$) of zirconia powder were applied to the gel-casting process. The viscosity behavior of slurries incorporating 40 vol% of zirconia powder was examined as a function of the dispersant content and the solid load to determine the optimum dispersion conditions. In addition, the gelation time with an initiator, the de-binding behavior, and the main factors affecting densification were examined. The densification of the gel-casted zirconia green body depended on the mixing ratio between the monomer and the dimer and on the zirconia particle size. A green body with a small particle size of $0.1{\mu}m$ showed less densification, with a relative density of 93%. This may be due to the excess number of bubbles created through interactions between the larger particle surface and polymer additives during the ball-milling process.

• Proceedings of the Korean Ceranic Society Conference
• /
• 2000.04a
• /
• pp.46.2-46.2
• /
• 2000

• Korean Journal of Materials Research
• /
• v.11 no.10
• /
• pp.869-878
• /
• 2001

Alumina $(Al_2O_3)$ green bodies were fabricated by gel-casting using three kinds of alumina with different particle size (mean particle size: 4.6 $\mu\textrm{m}$, 0.32 $\mu\textrm{m}$, 10nm). The effects of particle size on gel-casting process and green microstructure were investigated. The optimum dispersion conditions using ammonium salt (D-3019) as dispersant were 0.2 wt% (4.63 $\mu\textrm{m}$), 0.5 wt% (0.32 $\mu\textrm{m}$), and 5.0 wt% (10 nm), in high solid loading. The optimum solid loading of each starting material for gel-casting was obtained as 59 vol% (4.63 $\mu\textrm{m}$), 57 vol% (0.32 $\mu\textrm{m}$), 15 vol% (10 nm), depending on particle size, indicating that nano-size particle (10 nm) represent lower solid loading as high specific surface area than those of other two starting materials. The drying at ambient conditions (humidity; $\thickapprox$90%) was performed more than 48hrs to enable ejection of the part from the mold and then at $120^{\circ}C$ for 2hrs in an air oven, showing no crack and flaw in the dried green bodies. The pore size and distribution of the gelcast green bodies showed the significant decrease with decreasing particle size. Green microstructure was dependent on the pore size and distribution due to the particle size, and on the deairing step. The green density maximum obtained was 58.9% (4.63 $\mu\textrm{m}$), 60% (0.32 $\mu\textrm{m}$), 47% (10 nm) theoretical density (TD), and the deairing step applied before gel-casting did not affect green density.

• Journal of the Korean Ceramic Society
• /
• v.46 no.6
• /
• pp.653-656
• /
• 2009

Alumina bushing used for manufacturing glass fiber was fabricated by gel-casting which can fabricate complex forms. When solid loading is increased, density was increased and shrinkage and absorption were decreased. The sample loading with 57 vol% solid was optimum for alumina suspension, which showed the best physical properties. The cast sample was sintered at $1550{^{\circ}C}$ for two hours with sintering additive, $Y_2O_3$. The result showed that the alumina bushing with $Y_2O_3$ sintering additive has a density of 98%, shrinkage of 11% and bending strength of 196 kg/$cm^2$.

• Journal of the Korean Ceramic Society
• /
• v.31 no.12
• /
• pp.1467-1474
• /
• 1994

The effects of the dispersion, drying, and binder burning-out on the green-microstructures of gelcasted alumina were studied. The slip consisting of 55 vol% alumina powder and 5 wt% organic materials was well-dispersed by adding 0.28 wt% polyelectrolyte polymer. Green bodies were dried at >85% relative humidity at room temperature. Green-microstructures were observed to be depended on the heating rate during binder burnout. Constant drying rate was not observed in drying process of gelcasted alumina. Sintered body showed its relative density higher than 99% when it was sintered at 1$600^{\circ}C$ for 2 hours.

• Polymer(Korea)
• /
• v.30 no.6
• /
• pp.563-567
• /
• 2006

Poly(vinyl alcohol) (PVA) and gelatin (GEL) blend membranes were prepared by solution casting method under a high electric field. SEM observation of the membrane showed that gelatin rich domains were elongated and oriented to the direction of the applied electric field in PVA matrix. This can be attributed to the electrostatic emulsifying effects due to a reduction in interfacial tension. In addition, it was observed through WAXD and swelling measurements that the degree of crystallinity of membranes increased with applied electric field strength. This may be interpreted to be caused by the orientation effect of GEL domains in the blend membrane, and the self-annealing effect due to some heat generated from high electric field during casting.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11b
• /
• pp.341-345
• /
• 2001

In this study, nano-sized powders of $Si0_2-0^{\sim}15mol%B_2O_3$ composition were prepared by sol-gel processing method using TEOS(Tetra ethyl ortho silicate) and $H_3BO_3$ solution. The powders were tape-cast on High silicate glass sheet(HSG) substrate and sintered to form a layer of undercladding for the planar light wave module, During the sol-gel processing, $H_2O/Si$ mole ratio were varied to modify the size of the powders in a range from 600 to 75nm. The dispersion of the powder was modified by changing the pH of the slurry. Sintering temperature of the tape was observed to decrease with the size of the powder and the $B_2O_3$ content in the powder. When the silica powders of 75-125nm in diameter containing 15mol% $B_2O_3$ were used, 98 TD% was obtained at $1250^{\circ}C$, which is approximately $300^{\circ}C$ reduction in sintering temperature compared with micrometer-sized powders.