• Tribology and Lubricants
• /
• v.21 no.1
• /
• pp.16-20
• /
• 2005

Friction and wear characteristics between two steel surfaces under fretting condition are investigated experimentally. The fretting damage caused by low-amplitude oscillatory sliding can be classified into three regimes of gross-slip, mixed-slip and partial-slip due to stick-slip phenomenon. One of the most important characteristics of fretting wear is the transition from gross-slip to mixed-slip. This study was focused on getting the degree of stick-slip out of the friction transition under fretting condition. Fretting wear is divided into three conditions of gross-slip/mixed-slip/partial-slip. The criteria for the division are friction and displacement amplitude, wear scar morphology and dissipated energy. In this test, friction force and displacement were measured for detecting the transition from mixed-slip to gross-slip and qualitatively predicting the degree of the wear.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 2001.06a
• /
• pp.81-88
• /
• 2001

To study the influence of the shape of contacting bodies (especially the end profile) on slip regime, wear test is conducted in the case of the contact between tube and support. Two different end profiles of the support are used such as truncated wedge and rounded punch. During the test, 10, 30 and 50 N are applied as normal force and slip displacement varies between 10-200 $\mu\textrm{m}$. The tube and the support specimens are made of Zircaloy-4 and a specially designed wear tester is used. Tests are carried out in air at room temperature. Wear on the tube is examined by measuring microscope. Partial and gross slip regimes are classified from the observed wear shape. Surface roughness tester is also used to measure the wear depth and contour, from which wear volume is evaluated. The transition from partial to gross slip is also investigated by investigating the considerable increase of wear volume. From the result, the boundary between the partial and the gross slip is newly determined in the conventional fretting map for the present specific contact configuration. Since the transition is related with the amount of energy dissipation from the contact surface so is wear, it is regarded that wear can be restrained by designing a proper shape of support.

• Journal of Mechanical Science and Technology
• /
• v.15 no.9
• /
• pp.1274-1280
• /
• 2001

The fretting wear behavior of the contact between Zircaloy-4 tube and Inconel 600, which are used as the fuel rod cladding and grid, respectively, in PWR nuclear power plants was investigated in air. In the study, number of cycles, slip amplitude and normal load were selected as the main factors of fretting wear. The results indicated that wear increased with load, slip amplitude and number of cycles but was affected mainly by the slip amplitude. SEM micrographs revealed the characteristics of fretting wear features on the surface of the specimens such as stick, partial slip and gross slip which depended on the slip amplitude. It was found that fretting wear was caused by the crack generation along the stick-slip boundaries due to the accumulation of plastic flow at small slip amplitudes and by abrasive wear in the entire contact area at high slip amplitudes.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 2000.06a
• /
• pp.263-268
• /
• 2000

The fretting damage of the contact between Zircaloy-4 and Inconel 600 have Investigated. A fretting wear tester was designed to be suitable for this fretting test. In this study, the number of cycles, slip amplitude and normal load were selected as main factors of fretting wear. As the result of this research the wear volume increased with the increase of loads, slip amplitudes and the number of cycles and was more affected by slip amplitudes rather than by load. According to SEM, stick, partial slip, gross slip were observed on the surface of both specimens and wavy worn surfaces as the typical fretting damage were also Investigated due to accumulation of plastic flow.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 1996.05a
• /
• pp.1-3
• /
• 1996

The characteristics of fretting wear are reviewed. Fretting damage depends on slip amplitude and classified into three groups: (1) an annular damage according to Mindlin's analysis at microslip region, (2) strong adhesive deformation without loose wear particles at the intermediate region, and (3) formation of fine oxide particles at the gross slip region. The critical slip amplitude of fretting is the boundary between (2) and (3). The boundary slip amplitude depends on normal load. The wear rate increases and saturates with increasing slip amplitude. But it is constant by considering the critical amplitude. The role of oxide particles are discussed. Three different actions are noted: accelerating wear, preventing wear and insignificant effect. The oxide shows two opposing effect depends on normal load and slip amplitude. This is related to the removal rate from the interface (abrasive action) and compaction rate at the interface to form a protective layer. The effect of oxidation is significant to determine the wear and friction. The diffusion of oxygen is restricted at the small amplitude. As a result, crack formation at the boundary is a predominant damage, related to fretting fatigue damage.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.6 no.6
• /
• pp.226-233
• /
• 1998

In this paper, an experimental study was performed to investigate the speed ratio-torque-thrust characteristics for metal belt CVT. It is observed from the experimental results that nondimensional secondary thrust force follows with the existing theoretical formula with ${\mu}$=0.09~0.12 depending on the torque and the speed ratio. In order to represent these characteristics, an effective friction coefficient was introduced. Also, the slip characteristics between the belt and the pulley were investigated experimentally and traction coefficients at gross slip were obtained for various speed ratios. Using the traction coefficients and the effective friction coefficients, an improved formula for the secondary thrust force was suggested assuming that thrust force is the summation of the thrust of pseudo inactive arc and the thrust of pseudo active arc. The effective friction coefficient and the improved formula for the speed ratio-torque-thrust relationship suggested in this work can be used to obtain the appropriate secondary thrust.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.21 no.3
• /
• pp.511-518
• /
• 1997

The technique of fretting fatigue test was developed and fretting fatigue tests of A12024-T4 were conducted under several conditions. The newly developed calibration methods for measuring surface contact tractions showed good linearity and repeatability. The plate type specimen to which tow bridge type pads were attached and vision system was used to observe the crack behaviour. The oblieque cracks appeared in the early stage of crack growth and they became mode I cracks as they grow about 1 mm. The mode I transition points were found to be longer when surface tractions are higher or bulk stress is lower. Before the crack becomes mode I crack, 'well point' where crack grow about rate is minimum, was detected under every experimental condition. The crack behaviour was found to be affected by surface tractions, contact area, bulk stress. It was also found that partial slip and stick condition is most detrimental and the crack starts from the boundary of stick and slip. For gross slip crack started at the outside edge of pad. After crack mode transition, fretting fatigue cracks showed almost same behaviour of plain mode I fatigue cracks. Equivalent stress intensity factor was used to analyze the behaviour of fretting fatigue cracks and it was found that stress intensity factors can be applied to fretting fatigue cracks.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 2001.06a
• /
• pp.89-95
• /
• 2001

The fretting wear characteristics of Zircaloy-4 tube at room and high temperature were Investigated experimentally. In this study, the number of cycles, slip amplitude and temperature were selected as main factors of fretting wear. The results of this research showed that the wear volume Increased with the Increase of slip amplitudes and the number of cycles but decreased with temperature and the coefficient of friction were observed different tendency between room and high temperature. According to SEM(EDS) only gross slip were observed on the surface of both specimens and compacted oxide were on worn surfaces. XRO patterns showed that the crystallization of ZrO$_2$ were observed on the worn surface at high temperature. The fretting wear were Investigated due to oxidation and accumulation of plastic flow.

• Proceedings of the KSME Conference
• /
• 2001.06a
• /
• pp.157-162
• /
• 2001

Fretting is a potential degradation mechanism of structural components and equipments exposed to various environments and loading conditions. The fretting degradation, for example, can be observed in equipments of nuclear, fossil as well as petroleum chemical plants exposed to special environments and loading conditions. It is well known that a cast stainless steel(CF8M) used in a primary reactor coolant(RCS) degrades seriously when that material is exposed to temperature range ken $290^{\circ}C{\sim}390^{\circ}C$ for long period. This degradation can be resulted into a catastrophical failure of components. In the present paper, the characteristics of the fretting fatigue are investigated using the artificially aged CF8M specimen. The specimen of CF8M are prepared by an artificially accelerated aging technique holding 1800hr at $430^{\circ}C$ respectively. Through the investigations, the simple fatigue endurance limit of the virgin specimen is not altered from that obtained from the fatigue tests imposed the fretting fatigue. The similar tests are performed using the degraded specimen. The results are not changed from those of the virgin specimen. The significant effects of fretting fatigue imposed on both virgin and degraded specimen on the fatigue strength are not found.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.18 no.7
• /
• pp.1730-1737
• /
• 1994

Theoretical equations for an influence of fiber breaks on the frictional heating phenomenon in a uniaxially fiber-reinforced ceramic matrix composite are formulated. The microslip and gross slip phases are considered for deriving the equations. During a complete loading/unloading cycle, the work done against friction is derived. In order to estimate interfacial shear in a unidirectionally reinforced ceramic matrix composite which has fiber fractures as well as matrix cracks, parametric studies using the derived equations are done. In a case of less than 10% fiber fractures, additional frictional work due to fiber breaks can be neglected compared to the rest.