• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.21 no.6
• /
• pp.569-574
• /
• 2008

In the device structure of ITO/tris(8-hydroxyquinoline) aluminum ($Alq_3$)/Al device, we investigated the efficiency improvement of organic light-emitting diodes (OLEDs) depending on the hole-size of crucible boat. The device was manufactured using a thermal evaporation under the base pressure of $5{\times}10^{-6}\;Torr$. The $Alq_3$ organics were evaporated to be 100 nm thick at a deposition rate of $1.5\AA/s$, and in order to investigate the optimal surface roughness of $Alq_3$, the $Alq_3$ was thermally evaporated to be 0.8 mm, 1.0 mm, and 1.5 mm as a hole-size of the boat, respectively. We found that luminance and external quantum efficiency are superior when the hole-size of the boat is 1.0 mm. The external quantum efficiency of the device made with the hole-size of 1.0 mm boat were improved by a factor of ten compared to the devices made with the hole-size of non boat.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.06a
• /
• pp.34-35
• /
• 2009

We have studied the electrical and optical of organic light-emitting diodes depending on hole size of crucible boat using BCP materials. The thickness of TPD, $Alq_3$ and BCP was manufactured 40 nm, 60 nm and 5 nm under a base pressure of $5\times10^{-6}$ Torr using at thermal evaporation, respectively. In order to investigate the optimal surface roughness of BCP, the BCP was thermally evaporated to be 0.8 nun, 1.0 mm, 1.2 mm and 1.5 mm as a hole size of crucible boat, respectively. As the experimental results, we found that the luminous efficiency and the external quantum efficiency of the device is superior to others when hole size of crucible boat using BCP is 1.2 mm. Also, compared to the ones from the devices having the hole size of crucible boat is 1.0 mm and 1.5mm layer, the external quantum efficiency were improved by 2.5 and 2.4 times.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.11a
• /
• pp.29-30
• /
• 2007

In a device structure of ITO/tris(8-hydroxyquinoline) aluminum $(Alq_3)$/Al device, We investigated an the electrical characteristics of Organic Light-Emitting Diodes (OLEDs) depending on the hole-size of boat. The device was manufactured using a thermal evaporation under a base pressure of $5{\times}10^{-6}$ [Torr]. The $Alq_3$ organics were evaporated to be 100 [nm] thick at a deposition rate of $1.5[{\AA}/s]$, and in order to investigate the optimal surface roughness of $Alq_3$, the $Alq_3$ was thermally evaporated to be 0.8 [mm], 1.0 [mm], 1.5 [mm], and 3.0 [mm] as a hole-size of the boat respectively. We found that when the hole-size of the boat is 1.0 [mm], luminance and external quantum efficiency are superior.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.22 no.1
• /
• pp.74-80
• /
• 2009

In the structure of ITO/N,N'-diphenyl-N,N' bis (3-methylphenyl)-1,1'-biphenyl-4,4'-diamine(TPD)/tris (8-hydroxyquinoline)aluminum($Alq_3$)/Al device, we studied the efficiency improvement of organic light-emitting diodes due to variation of deposition rate of hole transport layer (TPD) materials using hole-size of crucible boat. The thickness of TPD and $Alq_3$ was manufactured 40 nm, 60 nm, respectively under a base pressure of $5{\times}10^{-6}$ Torr using a thermal evaporation. The $Alq_3$ used for an electron-transport and emissive layer were evaporated to be at a deposition rate of $2.5\;{\AA}/s$. When the deposition rate of TPD increased from 1.5 to $3.0\;{\AA}/s$, we studied the efficiency improvement of TPD using the hole-size of crucible is 1.0 mm. When the deposition rate of TPD is $2.5\;{\AA}/s$, we found that the average roughness is rather smoother, the luminous efficiency the external quantum efficiency is superior to the others. Compared to the two from the devices made with the deposition rate of TPD is $2.0\;{\AA}/s$ and $3.0\;{\AA}/s$, the external quantum efficiency was improved by four-times and two-times, respectively.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.22 no.11
• /
• pp.980-986
• /
• 2009

In a triple-layered structure of ITO/N,N'-diph enyl-N,N'bis(3-methylphenyl)-1,1' - biphenyl-4,4'-diamine(TPD)/tris(8-hydroxyquinoline)aluminum($Alq_3$)/(2,9-Dimethyl-4,7-diphenyl-1,10-phenanthroline(BCP)/Al device, we have studied the electrical and optical characteristics of organic light-emitting diodes(OLEDs) depending on the deposition condition of BCP layer. Several different sizes of holes on boat and several different deposition rates were employed in evaporating the organic materials. And then, electrical properties of the organic light-emitting diodes were measured and the performance of the devices was analyzed. It was found that the hole-size of crucible boat and the evaporation rate affect on the surface roughness of BCP layer as well as the performance of the device. When the hole-size of crucible boat and the deposition rate of BCP are 1.2 mm and $1.0\;{\AA}/s$, respectively, average surface roughness of BCP layer is lower and the efficiency of the device is higher than the ones made with other conditions. From the analysis of current density-luminance-voltage characteristics of a triple layered device, we divided the conductive mechanism by four region according to applied voltage. So we have obtained a coefficient of ${\beta}_{ST}$ in schottky region is $3.85{\times}10^{-24}$, a coefficient of ${\beta}_{PF}$ in Poole-Frenkel region is $7.35{\times}10^{-24}$, and a potential barrier of ${\phi}_{FN}$ in Fower-Nordheim region is 0.39 eV.