• 소성∙가공
• /
• 제23권2호
• /
• pp.110-115
• /
• 2014

Low cycle fatigue characteristics are very important in the development of automobile suspension parts. Fatigue properties using the strain life approach are usually obtained from low cycle fatigue tests. However, low cycle fatigue testing requires a lot of time and cost. In the current study, an attempt to estimate low cycle fatigue properties of high strength steel sheet from tensile test and tensile simulations is performed. In addition, low cycle fatigue testing was conducted to compare the fatigue properties obtained from tensile testing and simulations. In conclusion, the results effectively predict the low cycle fatigue properties. However, some deviations still exist.

• 대한금속재료학회지
• /
• 제47권7호
• /
• pp.391-396
• /
• 2009

Tensile, low cycle fatigue, and fatigue crack growth rate tests were conducted at RT and $300^{\circ}C$ for type 304 stainless steel. Tensile was tested under displacement control and low cycle fatigue was tested under strain control. Fatigue crack growth rate test was conducted under load control and crack was measured by DCPD method. Yield strength and elongation decreased at $300^{\circ}C$. Dynamic strain aging was not detected at $300^{\circ}C$. Low cycle fatigue life increased but fatigue strength decreased at $300^{\circ}C$. Fatigue crack growth rate increased at $300^{\circ}C$. Dislocation structures were mixed with cell and planar and did not change with temperature. Grain size did not change but plastic strain increased at $300^{\circ}C$. Strain induced martensite after low cycle fatigue test increased at RT but decreased at $300^{\circ}C$. It was concluded that the increase of low cycle fatigue life at $300^{\circ}C$ was due to the decrease of strain induced martensite at which crack was initiated.

• 동력기계공학회지
• /
• 제14권6호
• /
• pp.29-34
• /
• 2010

As the steam temperature of fossil power plant boiler is increasing, the use of 9Cr-1Mo high alloy material is prevalent and it is needed to investigate the characteristics of low cycle fatigue for high alloy and austenite stainless steel that has used up to recently. As a result of test, in 9Cr-1Mo high alloy steel, the relation of strain and fatigue life is non-linear and the crack mode of low cycle fatigue is brittle but in the austenite stainless steel, that of strain and fatigue life is linear and the crack mode of low cycle fatigue is ductile. Comparing the fatigue life between high alloy and austenite stainless steel, there is no consistent characteristics as to strains. But the fatigue life of 9Cr-1Mo steel is longer by 25% than that of STS304 stainless steel in the relatively low, 0.3% strain. In the other strain, the fatigue life of two materials is similar.

• 한국초전도ㆍ저온공학회논문지
• /
• 제25권4호
• /
• pp.28-31
• /
• 2023

This study presents a comprehensive procedure for the low cycle fatigue test of ultrasonically welded (UW) coated conductor (CC) lap-joints. The entire process is examined in detail, from the robust fabrication of the UW REBCO CC joints to the reliability testing under a low number of repeated cycle fatigue conditions. A continuous I_c measurement system enables real-time monitoring of I_c variations throughout the fatigue tests. The study aims to provide a step-by-step procedure that involves joint fabrication, electromechanical property (EMP) tests under uniaxial tension for stress level determination, and subsequent low-cycle fatigue tests. The joints are fabricated using a hybrid method that combines UW with adding In-Sn soldering, achieving a flux-free hybrid welding approach (UW-HW flux-free). The selected conditions for the low cycle fatigue tests include a stress ratio of R=0.1 and a frequency of 0.02 Hz. The results reveal some insights into the fatigue behavior, irreversible changes, and cumulative damage in the CC joints.

• 소성∙가공
• /
• 제19권1호
• /
• pp.11-16
• /
• 2010

The influence of pre-strain on low cycle fatigue behavior of Fe-18Mn-0.05Al-0.6C TWIP steel was studied by conducting axial strain-controlled tests. As-received plates were deformed by rolling with reduction ratios of 10 and 30%, respectively. A triangular waveform with a constant frequency of 1 Hz was employed for low cycle fatigue test at the total strain amplitudes in the range of ${\pm}0.4\;{\sim}\;{\pm}0.6$ pct. The results showed that low-cycle fatigue life was strongly dependent on the amount of pre-strain as well as the strain amplitude. Increasing the amount of prestrain, the number of reversals to failure was significantly decreased at high strain amplitudes, but the effect was negligible at low strain amplitudes. A new model for predicting fatigue life of pre-strained body has been suggested by adding ${\Delta}E_{pre-strain}$ to the energy-based fatigue damage parameter. Also, high-cycle fatigue lives predicted using the low-cycle fatigue data well agreed with the experimental ones.

• 대한기계학회논문집
• /
• 제13권2호
• /
• pp.307-315
• /
• 1989

본 연구에서는 단조과정을 거친후 노멀라이징(normalizing) 처리된 SF45A강종과 압연후 자연 냉각시킨 SM41B강종의 두 국산 강종에 대해 저사이클 피로시험을 행하여 저사이클 피로특성을 밝히고, 강재의 가공공정과 부하변형율변화에 따른 피로과정중의 연화 및 경화 거동을 관찰하였다. 그리고 저사이클 피로파면의 미시적 고찰을 통해서 부하변형율 크기에 따른 미시적 파면 양상의 변화를 밝혀 파괴 해석의 기초자료로 제공하였다.

• 한국안전학회지
• /
• 제33권3호
• /
• pp.8-14
• /
• 2018

Ni-base superalloy has excellent resistance to extreme environments such as high temperatures and high stresses and are used as materials for large gas turbines. In this paper, the specimens were taken from the blade that were used for a long time, and their life span was studied by microstructure analysis and avoidance of cursing. The microstructural analysis of the specimens was carried out using a OM and SEM to observe the coarsening, carbides on gamma prime. Low-cycle fatigue tests were performed on new material and airfoil of long time-used blade. The test was conducted under various deformation conditions and temperature conditions of $760^{\circ}C$ and $870^{\circ}C$. The low cycle fatigue test was carried out using the Coffin-Manson equation and the fatigue life was predicted. After the test, crack path and fracture surface were analyzed using SEM.

• 국제강구조저널
• /
• 제18권4호
• /
• pp.1384-1396
• /
• 2018

One of the failure modes observed in steel yield energy dissipating devices (SYEDs) excited by a strong earthquake would be the low-cycle fatigue failure. Fatigue cracks of a SYED are prone to initiate at the notch areas where stress concentration is usually occurred, which is demonstrated by the cyclic tests and analyses carried out for this study. Since the fatigue failure of SYEDs dramatically deteriorates their structural capacities, the thorough investigation on their fatigue life is usually required. To do this, sophisticated modeling with considering a time-consuming and complicate fracture mechanism is generally needed. This study makes an effort to investigate the low-cycle fatigue life of SYEDs predicted by a simplified method utilizing damage indices and fatigue prediction equations that are based on the plastic strain amplitudes obtained from typical finite element analyses. This study shows that the low-cycle fatigue failure of SYEDs predicted by the simplified method can be conservatively in good agreement with the test results of SYED specimens prepared for experimental validation.

• Corrosion Science and Technology
• /
• 제3권5호
• /
• pp.222-225
• /
• 2004

A portable RF HTS SQUID-based susceptometer was applied to the measurement of fatigue behavior for type 316L(N) stainless steel containing 0.04% to 0.15% nitrogen content. Strain-controlled low cycle fatigue (LCF) tests were conducted at RT and $600^{\circ}C$ in air an atmosphere, and the magnetic moments were measured after the fatigue test using HTS SQUID. The magnetic moment of an as-received sample is higher than that of a fatigued sample in all the temperature ranges irrespective of the nitrogen content. The fatigue life decreased with an increasing test temperature up to $500^{\circ}C$, but increased at $600^{\circ}C$. The change of the magnetic moments by LCF test is attributed to the stress induced micro defects.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2009년도 추계학술대회 논문집
• /
• pp.259-262
• /
• 2009

The influence of pre-strain in low-cycle fatigue behavior of Fe-18Mn-0.05Al-0.6C TWIP steel was studied by conducting axial strain-controlled tests. As-received plates were deformed by rolling with reduction ratios of 10 and 30%, respectively. A triangular waveform with a constant frequency of 1 Hz was employed for low cycle fatigue test at the strain amplitudes in the range of ${\pm}0.4{\sim}{\pm}0.6$ pct. The results showed that low-cycle fatigue life was strongly dependent on the amount of pre-strain as well as the strain amplitude. Increasing the amount of prestrain, the number of reversals to failure was significantly decreased at high strain amplitudes, but the effect was negilgible at low strain amplitudes. A new model for predicting fatigue life of pre-strained body has been devised adding a correction term of ${\Delta}E_{pre-strain}$ to the energy-based fatigue damage parameter.