• 한국기계연구소 소보
• /
• s.20
• /
• pp.79-87
• /
• 1990

Advanced ceramics have some excellent properties as the material for the mechanical component. It is, however, very difficult to grind ceramics with high efficiency because of their high strength, hardness and brittleness. Thus it is required also by a strong boom of demands for development of Machinable ceramics with high machinability in the most of industries. In present research, experiments are carried out to compare the machinability of sample Machinable ceramics. A $\ell$N(Aluminum Nitride) with additives of BN(Boron Nitride), yttrium. CaO are turned with cut-off tool type tungsten carbide bite using conventional turning machine.

• Journal of the Korean Society for Precision Engineering
• /
• v.21 no.1
• /
• pp.61-70
• /
• 2004

Generally, ceramics are very difficult-to-cut materials because of its high strength and hardness. The machining process of ceramics can be characterized by cracking and brittle fracture. In the machining of ceramics, edge chipping and crack propagation are the principal reasons to cause surface integrity deterioration. Such phenomenon can cause not only poor dimensional and geometric accuracy, but also possible failure of the ceramic parts. Ceramics can be machined with traditional method such as grinding and polishing. However, such processes are generally cost-expensive and have low material removal rate. Thus, in this paper, to overcome these problems. BN powder, which gives good cutting property, is added for the fabrication of machinable ceramics by volume of 5,10,15,20,25 and 30%. And, mechanical properties, R-curve behavior and machining tests are carried out to evaluate the machining properties of the manufactured machinable ceramics.

• Journal of the Korean Ceramic Society
• /
• v.28 no.9
• /
• pp.730-738
• /
• 1991

Machinable ceramics containing ${\beta}$-spodumene crystal was fabricated by melting method using domestic pyrophyllite. Raw materials were batched by molar ratio of 8:2, 7:3, 6:4, and 5:5 for fluorophlogopite and ${\beta}$-spodumene. These compounds were melted at 1450$^{\circ}C$ for 1 hr and formed in graphite mold. Base glasses were heat-treated according to 2-step schedule which was determined from DTA, XRD analysis and SEM observation. Fabricated machinable ceramics have excellent themal, chemical properties and machinability.

• Proceedings of the Korean Society of Machine Tool Engineers Conference
• /
• 2002.04a
• /
• pp.296-301
• /
• 2002

In this study, we investigated the machinability of machinable ceramics which were developed by a research lab. of Inha Univ., Korea. The effect of the nozzle scanning times, the size of patterns and compositions of BN in ceramics on the erosion depth of samples with no mask and samples with three different mask pattern in powder blasting of machinable ceramics. The blasting conditions were the impact angles 90$^{\circ}$, scanning times of noble up to 30 and the stand-off distances 100mm. The widths of mask pattern were 0.1mm, 0.5mm and 1 mm. The powder was alumina sharp particles, WA#600. The mass flow rate of powder during the erosion test was fixed constant at 150g/min and the blasting pressure of powder at 0.25Mpa

• Journal of the Korean Ceramic Society
• /
• v.47 no.6
• /
• pp.498-502
• /
• 2010

Aluminium titanate($Al_2TiO_5$) has extremely anisotropic thermal expansion properties in single crystals, and polycrystalline material spontaneously microcracks in the cooling step after sintering process. These fine intergranular cracks limit the strength of the material, but provide an effective mechanism for absorbing strain energy during thermal shock and preventing catastrophic crack propagation. Furthermore, since machinable BN-ceramics used as an insulating substrate in current micro-electronic industry are very expensive, the development of new low-cost machinable substrate ceramics are consistently required. Therefore, cheap $Al_2TiO_5$-machinable ceramics was studied for the replacement of BN ceramics. $Al_2O_3-Al_2TiO_5$ ceramic composite was fabricated via in-situ reaction sintering. $Al_2O_3$ and $TiO_2$ powders were mixed with various mol-ratio and sintered at 1400 to $1600^{\circ}C$ for 1 h. Density, hardness and strength of sintered ceramics were systematically measured. Phase analysis and microstructures were observed by XRD and SEM, respectively. Machinability of each specimens was tested by micro-hole machining. The results of research showed that the $Al_2TiO_5$-composites could be used for low-cost machinable ceramics.

• Journal of the Korean Ceramic Society
• /
• v.52 no.6
• /
• pp.423-428
• /
• 2015

The machinability of materials is an important factor in engineering applications. Many ceramic components that have complex shapes require machining, typically using diamond tools, which leads to high production cost. Machinable ceramics containing h-BN have recently been developed, but these materials are very expensive because of high cost of raw materials and machining. Therefore the development of low-cost machinable ceramics is desirable. In this study, mullite-$ZrO_2$ ceramics were prepared additions of $Al_2TiO_5$. $ZrSiO_4$, $Al_2O_3$, and $Al_2TiO_5$ powders mixed at various molar ratios with sintering at 1400, 1500, and $1600^{\circ}C$ for 1 hr. Phase formation and microstructure of the sintered ceramics were observed by XRD and SEM, respectively. The machinability of each specimen was tested using the micro-hole machining method. The machinability results show that the ceramics sintered at temperatures over $1500^{\circ}C$ can be used as good low-cost machinable mullite-$ZrO_2-Al_2TiO_5$ ceramics.

• Journal of the Korean Society of Safety
• /
• v.24 no.2
• /
• pp.7-12
• /
• 2009

The machining process of ceramics can be characterized by cracking and brittle fracture. In the machining of ceramics, edge chipping and crack propagation are the principal reasons to cause surface integrity deterioration. Such phenomenon can cause not only poor dimensional and geometric accuracy, but also possible failure of the ceramic parts. Thus, traditional ceramics are very difficult-to-cut materials. Generally, ceramics are machined using conventional method such as grinding and polishing. However these processes are generally costly and have low MRR(material removal rate). To overcome such problems, in this paper, h-BN powder, which gives good cutting property, is added for the fabrication of machinable ceramics by volume of 10 and 15%. The purpose of this study is an analysis of endmill's rake angle for appropriate tools design and manufacturing for the machinable ceramics. In this study, Experimental works are executed to measure cutting force, surface roughness, tool fracture, on different axial rake angle of endmills. Cutting parameters, namely, feed, cutting speed and depth of cut are used to accomplish purpose of this paper. Required experiments are performed, and the results are investigated.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.3 no.1
• /
• pp.15-21
• /
• 2004

The machining process of ceramics can be characterized by cracking and brittle fracture. In the machining of ceramics, edge chipping and crack propagation are the principal reasons to cause surface integrity deterioration. Such phenomenon can cause not only poor dimensional and geometric accuracy, but also possible failure of the ceramic parts. Thus, traditional ceramics are very difficult-to-cut materials. To overcome such problems, in this paper, h-BN powder, which gives good cutting property, is added for the fabrication of machinable ceramics by volume of 5, 10, 15, 20, 25 and 30%. The objectives of this paper is to evaluate the fracture phenomenon of the tungsten carbide tool and the variation of surface integrity of the manufactured machinable ceramics under various cutting conditions during end mill machining With CNC machining center.

• Transactions of the Korean Society of Machine Tool Engineers
• /
• v.13 no.2
• /
• pp.33-39
• /
• 2004

Sandblasting has recently been developed into a powder blasting technique for brittle materials. In this study, the machinability of $Si_3N_4$-hBN based machinable ceramics are evaluated for micro - pattern making processes using powder blasting. Material properties of the developed machinable ceramics according to the variation of h-BN contents give a good machinability to the ceramics. The effect of scanning times, the size of patterns and variation of BN contents on the erosion depth of samples without mask and samples with different mask patterns in powder blasting of $Si_3N_4$-hBN ceramics are investigated. The Parameters are the impact angle of $90^{\circ}$, the scanning times of nozzle up to 40, and the stand-off distances of 100mm The widths of masked pattern are 0.1mm 0.5mm and 1mm. The powder used is Alumina particles, WA#600. and the blasting pressure of powder is 0.2MPa. Through required experiments, the results are investigated and analyzed. As the results, the machinability of the developed ceramics increases as the BN contents in the ceramics.

• Journal of the Korean Society for Precision Engineering
• /
• v.21 no.4
• /
• pp.48-56
• /
• 2004

Ceramics are very difficult-to-cut materials because of its high strength and hardness. Their machining mechanism is characterized by cracking and brittle fracture. In this paper, to give good machinability to the ceramics, h-BN powders are added to $Si_3N_4$, by volume of 20, 25 and 30%. And the machinability of the produced ceramics is tested using micro drilling system. Through required experimental works, it is shown that the micro drilling machinability is varied along with the volumetric percentage of h-BN powders. Also, it is verified that the obtained results can be used to develop new machinable ceramics of good material properties and machinability.