• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 2002.10b
• /
• pp.175-176
• /
• 2002

Our study is to search for tribological properties of diamond-like carbon (DLC) films as known as anti- wear hard thin film on various polymers. This report deals with the deposition of DLC films on various polymer substrates in vacuum by magnetron radio frequency (RF) sputtering method with using argon plasma and graphite, titanium target. The properties of friction and wear are measured using a ball-on-disk wear -testing machine. The properties of friction and wear have been remarkably improved by DLC coating. Moreover the composition of DLC films has been analyzed by using auger electron spectroscopy(AES). The wear rate of titanium-containing DLC film is lower than that of no-metal-containing DLC film.

• 한국신재생에너지학회:학술대회논문집
• /
• 2008.05a
• /
• pp.41-44
• /
• 2008

본 연구에서는 고분자 전해질 연료전지용 금속분리판의 전기화학적 부식을 방지하기 위한 금속 첨가 DLC(Diamond-like-carbon) 표면처리 방법을 개발하였으며, stainless steel 304를 모재로 하여 텅스텐 첨가 DLC, 티타늄 첨가 DLC, 몰리브덴 첨가 DLC 금속분리판을 제작하였다. 제작된 금속분리판을 이용하여 내구성 평가,전기화학적 부식 특성, 성능평가 및 접촉저항 특성 등을 평가하였다. 전기화학적 부식특성의 경우 각각의 분리판에 대해 6.69, 1.2, 1.0 ${\mu}A/cm^2$로 모재인 STS 304의 25 ${\mu}A/cm^2$의 부식전류밀도에 비해 우수한 부식특성을 보였다. 또한 초기 성능에서 몰리브덴 첨가 DLC 분리판의 경우 300 mA/$cm^2$에서 0.757 V로 측정되었으며, 이는 graphite 분리판 측정 결과인 0.758 V와 유사한 성능을 보였다. 또한 내구성 평가에서 초기 성능 대비 성능 감소율이 10% 감소하는데 소요된 시간은 graphite 분리판의 경우 2,000시간으로 나타났으며, 몰리브덴 첨가 DLC 분리판의 경우 1,700시간으로 측정되었다. 1,500시간 까지의 성능 감소율은 grphite,텅스텐 첨가DLC,티타늄 첨가DLC, 몰리브덴 첨가 DLC 분리판 순으로 각각에 대해 37.7, 60.3, 92.8, 45.7 ${\mu}V$/hr로 나타났다.