• Journal of Energy Engineering
• /
• v.12 no.4
• /
• pp.302-308
• /
• 2003

The peformence tests of zinc-based desulfurization sorbents using the yellow earth as support for the hot gas clean up were carried out. The zinc-based sorbent with 25 wt％ yellow earth was prepared, and their properties such as the reaction rate, the sulfur capacity and the attrition resistance, were investigated. The reactivity tests for hot gas desulfurization was performed at middle temperatures (sulfidation/regeneration：480$^{\circ}C$/580$^{\circ}C$). During multi-cyclic desulfurization, the deactivation of zinc-based sorbent was decreased by the addition of yellow earth, and their efficiency was enhanced. The ZnO/yellow earth sorbent had high reactivity, good regenerability, long-term durability (about 19 gS/100 g sorbent for 10-cycles) and high attrition resistance (AI=19.1％). It was concluded that the peroperties of zinc-based sorbent were improved by metal oxides (Fe$_2$O$_3$, Na$_2$O, MnO$_2$, etc) in the yellow earth. From these results, it was confirmed that the desulfurization properties of zinc-based sorbents at middle temperatures could be improved by the yellow earth using as support.

• Journal of Korean Society of Environmental Engineers
• /
• v.22 no.11
• /
• pp.2067-2076
• /
• 2000

The experiments have been made to develop manganese-based sorbent(MT, MFT) for the removal of hydrogen sulfide from simulated hot coal gases. Manganese-based sorbents were tested in an ambient-pressure fixed-bed reactor to calculate H2S removal efficiency. and a three hole jet attrition tester to characterize the sorbent physical properties. According to the experimental results of attrition test. the attrition resistance of 5% bentonite containing sorbent was higher than that of 2% bentonite. The attrition resistances of both sorbents increased with induration temperature. Effects of sulfidation temperature. space velocity. and $H_2S$ concentrations on the $H_2S$ removal efficiency were investigated. Experimental results showed that $H_2S$ could be removed from 5,100ppmv to 20ppmv at $450^{\circ}C$, and to 30~65ppmv at $550{\sim}650^{\circ}C$ for both MT/MFT sorbents. As for the change of space velocity, the breakthrough time was decreased with space velocity.

• Journal of Environmental Health Sciences
• /
• v.22 no.4
• /
• pp.1-9
• /
• 1996

Experiments have been made to test the practical feasibility of using calcined manganese ore to desulfurize hot reducing gas. In this study, the effects of particle size of sorbents, temperature of sulfidation, flow rate and sorbent characteristics on the $H_2S$ removal efficiency of calcined manganese ore were investigated. Experimental results showed that the removal efficiency of $H_2S$ was optimum when the temperature was about 800$\circ$C and that the smaller particle size the higher the $H_2S$ removal efficiency. When the temperature was above 800$\circ$C, the reactivity of sorbent has lowered because agglomeration of sorbent increased intraparticle transport resistance, and this phenomenon was confirmed by SEM photographs. As the temperature increases, capacity for the $H_2S$ removal was increased but the equilibrium concentration of $H_2S$ was not affective.

• Journal of Korean Society of Environmental Engineers
• /
• v.22 no.2
• /
• pp.291-302
• /
• 2000

This experiments have been made to develop of manganese-based sorbent for the removal of hydrogen sulfide from hot coal gases. Manganese-based sorbent were tested in an ambient-pressure fixed-bed reactor to determine steady state $H_2S$ concentrations, breakthrough times and feasibility of the sorbent when subjected to cycle sulfidation and regeneration testing. Effects of particle size of sorbent, temperature of sulfidation, regeneration temperature and regeneration characteristics on the $H_2S$ removal efficiency were investigated. Experimental results showed that the $H_2S$ removal efficiency was optimal when the temperature was about $800^{\circ}C$ and the smaller particle size, the better $H_2S$ removal efficiency but in the range of 0.214~0.631mm didn't influence it much. The equilibrium constant(K) is represented as a log(K)=3.396/T-1.1105 and the utilization efficiency of sorbents was about 92% at $800^{\circ}C$. Regeneration in air produced $SO_2$ concentration as high as 8.5% at $800^{\circ}C$, 8.4% at $850^{\circ}C$, and 8.8% at $900^{\circ}C$ and may be used in sulfuric acid production.