• Elastomers and Composites
• /
• 제55권1호
• /
• pp.20-25
• /
• 2020

The effect of the isocyanate index (NCO index) on the particle size and particle size distribution of a waterborne polyurethane dispersion (WPUD) with polycarbonate-diol was determined. The WPUDs were prepared using a conventional acetone process with polycarbonate-polyol (M_n = 2028), 4,4'-methylenebis(cyclohexyl isocyanate) (H₁₂MDI), 2,2-bis(hydroxymethyl) propionic acid (DMPA), and dibutyltin dilaurate catalyst. At NCO index values below 1.5, the number average particle diameter of the WPUDs significantly increased with the NCO index, whereas the particle diameter slightly varied at higher NCO indexes. The dependency of the WPUD viscosity on the NCO index exhibited similar behavior to that of the particle size. The relative values of the full width at half maximum of the WPUD particle distribution curves at various NCO indexes were not influenced by the NCO index.

• 한국가스학회지
• /
• 제16권6호
• /
• pp.115-122
• /
• 2012

LNG저장탱크의 보냉제로 사용되는 폴리우레탄 폼의 NCO index에 대한 영향을 알아보기 위해 대체발포제인 HFC-365mfc를 사용하여 NCO index와 촉매를 변화시키면서 폴리우레탄 폼을 합성하였다. 폴리우레탄 폼의 물성변화를 고찰하기 위해 만능시험기, 시차주사열량계, 주사전자현미경, 적외선 분광기를 이용하였다. 촉매의 종류를 PC-8과 33LV, TMR-2로 변화시키고 양을 변화시킨 결과 촉매의 종류에 따라 압축강도의 차이가 발생하였으나 밀도에는 영향을 미치지 않음을 확인하였다. 또한 촉매의 첨가량이 증가할수록 압축강도도 증가하는 경향을 나타내었다. 겔화촉매인 PC-8과 33LV를 사용한 폼을 노화시킨 결과 NCO index가 증가하면 유리전이온도와 압축강도가 증가하였으나 삼량화 촉매인(TMR-2)를 사용한 폼을 노화시킨 결과 노화전후의 물성차이가 발생하지 않았으며 이는 초기 반응시 삼량화 여부에 기인함을 FT-IR을 사용하여 규명하였다.

• 공업화학
• /
• 제28권1호
• /
• pp.57-63
• /
• 2017

본 연구에서는 다양한 NCO index에서 물 함량 변화가 자동차용 폴리우레탄 시트 폼 패드의 정적 안락감에 미치는 영향을 알아보았다. 정적 안락감에 영향을 미치는 요인을 파악하기 위해 UTM을 사용한 정하중 특성 시험을 통하여 히스테리시스 곡선을 나타냈으며, 이를 통해 25% 변형 시 경도와 65% 변형 시 경도, hysteresis loop area, hysteresis loss (%), 그리고 Sag factor를 구하였다. 동일한 NCO index에서 물 함량이 증가함에 따라 우레아 결합의 증가로 경도가 증가하고, 가교밀도가 증가하는 경향을 swelling ratio 측정으로 확인하였으며, 이에 따라 복원력은 감소하는 경향을 확인하였다. 또한 표면 경도의 증가로 인해 Sag factor가 감소하는 경향을 확인하였다. 동일한 물 함량에서 NCO index가 증가함에 따라 우레탄과 우레아 결합이 이소시아네이트와 추가 반응하여 가교도와 경도가 증가하고 이에 따라 복원력이 감소함을 확인하였다.

• 한국염색가공학회지
• /
• 제30권2호
• /
• pp.90-97
• /
• 2018

Hydrophilic reactive hot-melt polyurethane adhesive(HRHA) using a hydrophilic polyol having different molecular weight and NCO index was synthesized. This HRHA was synthesized using Polyethylene glycol(PEG) as a hydrophilic polyol, Polypropylene glycol(PPG) and Polycaprolactone diol(PCL) as hydrophobic polyols, and Methylene diphenyl diisocyanate(MDI) as an isocyanate. The changes in IR spectrum, viscosity and thermal properties of HRHA with different PEG molecular weights and NCO index were investigated, and the tensile strength and elongation of the HRHA casting film and the peel strength, moisture permeability and water pressure of the HRHA coated fabric were confirmed. In this experiment, as the molecular weight of PEG and NCO index increased, the adhesive strength, tensile strength, elongation and moisture permeability was increased but viscosity and Tg was decreased.

• Elastomers and Composites
• /
• 제55권1호
• /
• pp.13-19
• /
• 2020

4,4'-Methylenebis(2-chlorobenzenamine) (MOCA)-free fast curing polyurethanes were prepared. In this study, the processibility of a fast curing polyurethane system was characterized by assessing the pot life. The obtained pot life of the polyurethane was 6-8 s, indicating that this prepolymer-curative system is appropriate for ribbon flow casting. The influence of the NCO index on the viscosity and mechanical properties was evaluated. The viscosity, tensile strength, tear strength, and hardness of the as-prepared polyurethanes showed an increasing trend, with an increase in the NCO index, whereas the elongation at break increased initially and then decreased with an increase in the NCO index. The gel fraction and crosslink density showed a direct correlation with the NCO index, which substantiated the improved mechanical properties at the higher NCO index. The coefficients of friction and abrasion deteriorated with an increase in the NCO index.

• Elastomers and Composites
• /
• 제53권2호
• /
• pp.86-94
• /
• 2018

The effect of the NCO index and catalyst type on the thermal stability of poly(urethane-isocyanurate) (PUIR) foams was investigated to identify a method for enhancing the flame resistance of PUIR. PUIR foams were prepared using 4,4-diphenylmethane diisocyanate (MDI) and [(diethylene glycol)adipate]diol, which were synthesized by esterification of adipic acid and diethylene glycol. Dabco K-15, Dabco TMR-30, and Toyocat RX-5 were used as the catalysts for trimerization and gelation. The amount of urea and isocyanurate groups in PUIR was semi-quantitatively determined by normalizing their absorbance with the phenyl absorbance measured by FT-IR. The normalization data showed that Dabco TMR-30 effectively generated isocyanurate groups in PUIR. As a result, Dabco TMR-30 effectively raised the decomposition temperature and increased the 800 K and 900 K residues of the PUIR foam synthesized with an NCO index of 200.

• 폴리머
• /
• 제29권5호
• /
• pp.457-462
• /
• 2005

Polymeric 4,4'-diphenylmethane diisocyanate(PMDI), OH 값이 480인 혼합 폴리올, 실리콘 계면활성제, 세 종류의 촉매 그리고 발포제로 불화탄화수소계를 사용하여 폴리우레탄 발포체(PUF)를 제조하였다. 촉매로는 balance 촉매(PC-8), 젤 화촉매(33LV) 그리고 삼량화 촉매(TMR-2)가 이용되었으며, 이소시아네이트(NCO) 인덱스(index)와 노화시간에 따른 PUF의 물성에 대한 촉매의 영향을 조사하였다. PC-8과 33LV를 이용한 PUF의 압축강도는 NCO 인덱스에 따라 큰 변화를 보이지 않은 반면 발포셀의 크기는 약간 증가하였다. 삼량화 촉매의 경우에, PUF의 압축강도는 NCO인덱스에 따라 8.75에서 $10.5 kg_f/cm^2$으로 증가하였고 발포셀의 크기는 감소하였다. 33LV를 이용한 PUF의 압축강도는 노화시간이 증가함에 따라 9.21에서 $10.15 kg_f/cm^2$으로 증가하였으나 삼량화 촉매인 TMR-2를 이용한 경우에는 거의 변화가 나타나지 않았다. 이는 미반응 MDI에 의한 추가적인 가교반응에 의해 설명할 수 있고 FTIR의 결과로 확인하였다.

• 한국가스학회지
• /
• 제12권3호
• /
• pp.38-42
• /
• 2008

본 연구에서는 폴리에스테르 폴리올의 구조와 이소시아네이트 인덱스의 변화에 따라 초저온($-190^{\circ}C$)과 상온($25^{\circ}C$)에서 폴리우레탄 접착제의 접착강도변화를 고찰하였다. 전단강도는 폴리우레탄 접착제를 plywood에 접착하여 측정하였으며, 접착제의 화학적, 기계적 물성 변화를 UTM, DSC, FT-IR로 비교 분석 하였다. 지방족 폴리에스테르 폴리올을 사용하여 합성한 폴리우레탄은 초저온에서의 전단강도가 상온에서의 전단강도보다 증가하였으나 방향족 폴리에스테르 폴리올을 사용하여 합성한 폴리우레탄의 경우는 초저온에서의 전단강도가 상온에서보다 작아지는 경향을 나타내었다. 또한 접착강도는 사용된 MDI의 양에 비례하여 증가하였으며, 지방족계 폴리올은 초저온에서 그리고 방향족계 폴리올은 상온에서 높은 접착 강도를 보임을 알 수 있었다.

• 공업화학
• /
• 제19권4호
• /
• pp.427-431
• /
• 2008

해수 하에서 경시변화에 따른 경질 폴리우레탄 폼의 물성변화를 알아보기 위해 이소시아네이트 인덱스를 변화시키며 경질 폴리우레탄 폼(PUF)을 합성하였다. 해수 하에서 이소시아네이트의 인덱스가 90, 100, 130, 150으로 증가함에 따라 PUF의 인장강도는 각각 10%, 3%, 7%, 4%씩 감소하였고, 압축강도는 각각 7%, 6%, 5%, 4%씩 감소하였다. PUF의 물성저하를 규명하기 위해 PUF의 기공을 확인한 결과 기공의 변화는 없었다. 해수 하에서 PUF의 유리전이온도($T_g$), 인장 모듈러스는 증가하였는데 적외선 스펙트럼 분석결과 우레아, 알로파네이트, 바이우렛이 증가하는 것을 알 수 있었다. 해수 하에서 PUF는 가교도 증가하고 이로 인해 폼이 brittle하게 형성되어 $T_g$의 증가에도 불구하고 기계적 물성이 저하된 것으로 사료된다. 해수 하에서 PUF의 물성변화를 고찰하기 위해 만능시험기, 시차 주사 열량계, 주사 전자 현미경, 적외선 분광계를 이용하였다.

• 한국가스학회:학술대회논문집
• /
• 한국가스학회 2003년도 춘계학술발표회 논문집
• /
• pp.182-192
• /
• 2003