Nano-Scale Observation of Fatigue Striations for Aluminum Alloy (알루미늄 합금 피로 스트라이에이션의 나노 스케일 관찰)

  • Choi, Sung-Jong;Kwon, Jae-Do;Ishii, Hitoshi
    • Proceedings of the KSME Conference
    • /
    • 2000.04a
    • /
    • pp.153-158
    • /
    • 2000
  • Atomic Force Microscope (AFM) was used to study cross sectional profiles and dimensions of fatigue striations in 2017-T351 aluminum alloy. Their widths (SW) and heights $(SH,\;SH_h)$ were measured from the cross sectional Profiles of three-dimension AFM images. The following results that will be helpful to understand the fatigue crack growth mechanism were obtained. (1) Coincidence of the crack growth rate with the striation width was found down to the growth rate of $10^{-5}$ mm/cycle. (2) The relation of $SH={\alpha}(SW)^{1.2}$ was obtained. (3) The ratio of the striation height to its width SH/SW and did not depend on the stress intensity factor range ${\Delta}K$ and the stress ratio R. From these results, the applicability of the AFM to nano-fractography is discussed.

  • PDF

The Observation of Fatigue Striations for Aluminum Alloy by Atomic Force Microscope(AFM) (원자력 현미경(AFM)에 의한 알루미늄 합금의 피로 스트라이에이션 관찰)

  • Choe, Seong-Jong;Gwon, Jae-Do
    • Transactions of the Korean Society of Mechanical Engineers A
    • /
    • v.24 no.4 s.175
    • /
    • pp.955-962
    • /
    • 2000
  • Scanning Probe Microscope (SPM) such as Scanning Tunneling Microscope (STM) and Atomic Force Microscope (AFM) was shown to be the powerful tool for nano-scale characterization of a fracture surface . AFM was used to study cross sectional profiles and dimensions of fatigue striations in 2017-T351 aluminum alloy. Their widths (SW) and heights (SH) were measured from the cross sectional profiles of three-dimension AFM images. The following results that will be helpful to understand the fatigue crack growth mechanism were obtained. (1) Coincidence of the crack growth rate with the striation width was found down to the growth rate of 10-5 mm/cycle. (2) The relation of SH=0.085(SW)1.2 was obtained. (3) The ratio of the striation height to its width SH/SW did not depend on the stress intensity factor range K and the stress ratio R. (4) Not only the SW but also the SH changed linearly with the crack tip opening displacement (CTOD) when plotted in log-log scale. From these results, the applicability of the AFM to nano-fractography is discussed.

Nano-Scale Observation of Fatigue Striations for Aluminum Alloy (알루미늄 합금 피로 스트라이에이션의 나노 스케일 관찰)

  • Choe, Seong-Jong;Gwon, Jae-Do;Ishii, Hitoshi
    • Transactions of the Korean Society of Mechanical Engineers A
    • /
    • v.25 no.7
    • /
    • pp.1047-1054
    • /
    • 2001
  • Atomic Force Microscope (AFM) was used to study cross sectional profiles and dimensions of fatigue striations in 2017-T351 aluminum alloy. Their widths(SW) and heights (SH, SH(sub)h, SH(sub)ι) were measured from the cross sectional profiles of three-dimension AFM images. The following results that will be helpful to understand the fatigue crack growth mechanism were obtained. (1) The relation of SH=$\alpha$(SW)(sup)1.2 was obtained. (2) The ratio of the striation height to its width SH/SW, SH(sub)h/SW and SH(sub)ι/SW did not depend on the stress intensity factor range ΔK and the stress ratio R( =P(sub)min/P(sub)max = K(sub)min/K(sub)max). (3) Effect of precipitate on the morphology of striation was changed by the relative dimensional difference between the striation width SW and the precipitates. From these results, the applicability of the AFM to nano-fractography is discussed.

Effects of Tungsten Addition on Tensile Properties of a Refractory Nb-l8Si-l0Ti-l0Mo-χW (χ=0, 5, 10 and 15 mot.%) In-situ Composites at 1670 K

  • 김진학;Tatsuo Tabaru;Hisatoshi Hirai
    • Transactions of Materials Processing
    • /
    • v.8 no.3
    • /
    • pp.233-233
    • /
    • 1999
  • To investigate the effect of tungsten addition on mechanical properties, we prepared refractory (62χ)Nb-18Si-l00Mo-l0Ti-χW (χ=0, 5, 10 and 15 mol.%) in-situ composites by the conventional arc-casting technique, and then explored the microstructure, hardness and elastic modulus at ambient temperature and tensile properties at 1670 K. The microstructure consists of relatively fine (Nb, Mo, W, Ti)/sub 5/Si₃, silicide and a Nb solid solution matrix, and the fine eutectic microstructure becomes predominant at a Si content of around 18 mol.%. The hardness of (Nb, Mo, W, Ti(/sub 5/Si₃, silicide in a W-free sample is 1680 GPa, and goes up to 1980 GPa in a W 15 mol.% sample. The hardness, however, of Nb solid solution does not exhibit a remarkable difference when the nominal W content is increased. The elastic modulus shows a similar tendency to the hardness. The optimum tensile properties of the composites investigated are achieved at W 5 mol.% sample, which exhibits a relatively good ultimate strength of 230 MPa and an excellent balance of yield strength of 215 MPa, and an elongation of 3.7%. The SEM fractography generally indicates a ductile fracture in the W-free sample, and a cleavage rupture in W-impregnated ones.

Mechanical Properties and Failure Analysis of $Al_2O_3/ZrO_2$ Composites ($Al_2O_3/ZrO_2$복합체의 기계적 물성 및 파괴거동)

  • Hong, Gigon-Hong;Han, Dong-Bin
    • Korean Journal of Materials Research
    • /
    • v.2 no.3
    • /
    • pp.172-179
    • /
    • 1992
  • $Al_2O_3/ZrO_2$ composites were fabricated by pressureless sintering from commercial powders and/or nano composite powder of $Al_2O_3/ZrO_2$. The Properties of the composites such as density, strength, hardness and fracture toughness were evaluated. Microstructures and fracture surfaces ware also examined. The flexural strength remains unchanged(~640 MPa) as long as the content of commercial powders is not extreamly high, and depends on microstructures of the composites. Fracture toughness(4.3-5.3 $Mpa{\cdot}m^{1/2}$) increases with increasing content of commercial powders. Fractography shows that failure-initiating sources are 1)surface flaws resulting from machining damage, 2)crack-shaped voids formed due to $ZrO_2$ agglomeration, and 3)surface separation caused by inhomogeneous blending and by sinterability difference between nato composite powder and commercial powders of $Al_2O_3/ZrO_2$. Failure mode of the composites was mainly transgranular.

  • PDF