• Journal of Adhesion and Interface
• /
• v.21 no.4
• /
• pp.143-155
• /
• 2020

Hydrophobic Organic-Inorganic (O-I) hybrid materials prepared by sol-gel process have been widely used at functional coating fields such as coatings for anti-corrosion, anti-icing, self-cleaning, anti-reflection. The key point for fabricating hydrophobic surface is to optimize the surface energy and roughness of the coating films. There are typical processes to control the surface energy and roughness which are 'In situ fabricating', 'Pre-fluorinating/Post-roughening', 'Pre-roughening/ Post-fluorinating'. In this study, particle-binder process was used for in-situ fabrication of hydrophobic coating films. Various O-I hybrid compounds prepared using several kinds of alkoxysilane compounds were used as a binder for silica nanoparticles at particle-binder process. To study effect of fluorine content and weight ratio of particle : binder on the hydrophobicity and surface morphology, Hydrophobic coating films were prepared onto glass substrate at various content of fluorine content of O-I hybrid binder and weight ratio of particle : binder. The coating films prepared using O-I hybrid binder (GPTi-HF10) having 10 wt% of fluorine content showed the highes water contact angle (107.52±1.6°). The coating films prepared at 1:3 weight ratio of GPTi-HF10 : silica nanoparticle exhibited the highest water contact angle (130.84±1.99°).

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09a
• /
• pp.175-176
• /
• 2006

The filling property of the binder treated iron based powder made of atomized iron powder was compared with that of the one made of reduced iron powder. The latter one showed a better filling property than the former one, although the original reduced powder showed a worse flow rate. Changing the particle size distribution of the original atomized powder from wide to narrow like the original reduced iron powder, improved the filling property of the binder treated powder. As a result, the particle size distribution of the original iron powder was found to strongly affect the filling property of the binder treated powder.

• Korean Journal of Materials Research
• /
• v.5 no.2
• /
• pp.232-238
• /
• 1995

The thermal stress distribution of WC and Ni binder phases In WC-26st.%Ni and WC-6wt.%Ni composites has been investigated over the temperature range 100-900 K using a time-of-flight neutron diffractometer. To determine the stress distribution, the breadths of WC and Ni peaks in the reference powder and the composites were analyzed. The peak breadths were corrected for particle size effect using a procedure based on the integral peak breadth method of particle size-strain analysis. The result shows a broad range of strain, and thus stress, is present in the WC and Ni binder phases of the composites. The strain distribution of both phases broadens as the temperature decreases, and some fraction of total strain distribution of the WC phase remains tensile regardless of the temperature. The strain distribution of the WC phase broadens as the binder content increases, and that of Ni binder phase broadens as the binder content decreases, which means the strain distribution broadens as the absolute value of residual stress increase.

• Journal of the Korean Wood Science and Technology
• /
• v.22 no.1
• /
• pp.85-90
• /
• 1994

The flow properties of binder latices for paper coating were investigated, together with dynamic viscoelastic properties of latex films and electron micrographs of latices, under various conditions. The amphoteric latex, binder pigment latex and anionic latex were used in this work. The amphoteric latex has both anionic and cationic functional group on its surface. The binder-pigment with a core-shell structure has dual functions : plastic pigment and binder. The low shear viscosity of binder latices and clay slurry were measured with Brookfield vis cometer. At low-shear rates. the viscosity decreased with increasing particle size of latex. On the amphoteric latex surface, the carboxyl groups are assumed to be fully dissociated over the region of pH 9~12, but the density of negative groups seems to be increased because of the gradual decrease in the degree of dissociation of amino groups. Since the apparent particle size of latex increases with surface charge, the electroviscous effect can be observed. On the anionic latex surface, the charge density is assumed to be nearly constant above pH 8. However, below pH 8 the coagulation of particles could be observed probably because of the decrease in the charge density.

• Journal of Powder Materials
• /
• v.7 no.1
• /
• pp.27-34
• /
• 2000

The fabrication process and mechanical properties of SiC particle prefrrms with high volume fraction ranged 50∼71% were investigated to make metal matrix composites for possible applications as heat sinks in electronic packares. The SiC particle preforms with 50∼71vol% of reinforcement were fabricated by a new modified process named ball milling and pressing method. The SiC particle performs were fabricated by ball milling of SiC particles with single sized of 48${\mu}$m in diameter or two different size of 8${\mu}$m and 48${\mu}$min diameter, with collodal SiO2 as inorgnic binder in distilled water, and the mixed slurries were cold pressed for consolidation into final prefom. The compressive strengths og calcined SiC particle prefoms increased from 20MPa to 155MPa with increasing the content of inorganis binder, temperature and time for calcination. The increase of compressive strength of SiC particle bridge the interfaces of two neighboring SiC particles.

• Journal of the Society of Cosmetic Scientists of Korea
• /
• v.30 no.4 s.48
• /
• pp.543-548
• /
• 2004

For pearl pigments used for splendor or gloss effect of make-up products, especiallv point make-up products like eye-shadow and blusher, we studied the variation of particle size distribution by the grinding time and by the binder used as a binding agent. In this study. high speed mixer was used and the particle sire distribution was measured by using the light scattering method. In case of pearl pigments, its median diameter of $5{\;}{\mu}m$, the particle size was reduced to 4.6 um when it was ground for 120 s. When it was applied for the pearl pigment of $45{\;}{\mu}m$, the particle size was reduced to $27{\;}{\mu}m$. We confirmed that the latter was reduced more largely and the original gloss was reduced too. For the binder, we studied the correlation between particle size of raw material and grinding time. We also investigated the effects of the binder contents on the variation of particle size distribution of products by aggregation of particles.

• Journal of the Korean Ceramic Society
• /
• v.32 no.8
• /
• pp.901-908
• /
• 1995

In aqueous slurry processing of silicon nitride, the interaction of dispersant and binder used as polymeric processing additives on the silicon nitride particle surface was studied to identify the effect of these processing polymeric additives on the ceramic powder processing. The adsoprtion isotherm study of anionic organic molecule as dispersant and nonionic organic molecules as binder of silicon nitricde was studied to investigate the effect of these processing organic additives on the physicochemical properties of silicon nitride particles. As anionic molecule adsorbed onto silicon nitrice surface, the IEP of silicon nitride shifted toward acidic pH and changed the stability of silicon nitride particle. However, the adsorption of binder as nonionic organic molecule onto silicon nitride surface did not changed the IEP but caused the decrease of electrostatic potentials of silicon nitride. These distinctive adsorption behaviors of organic additives on silicon nitride particles can be closely correlated to the stability of silicon nitride particles suspended in aqueous media.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.06a
• /
• pp.330-330
• /
• 2007

Polycrystalline mercuric iodide $HgI_2$) films are being developed as a new detector technology for digital x-ray imaging. The $HgI_2$ is generally vacuum deposited by physical vapor deposition (PVD) process. But the PVD thick deposition has been caused any instability in the biasing due to any defects or cracks. In this work we present a new particle-in-binder (PIB) methodologies used for the $HgI_2$ thick films. These growth techniques can be easily extended to produce much larger film areas. This paper, for the first time, presents results and comparison of polycrystalline $HgI_2$ films derived by various PIB methods. We investigated the structural and morphological properties of the films using X-ray diffraction (XRD) and scanning electron microscopy (SEM) analysis. The films were characterized with respect to their electrical properties and in response to x-ray photons. Physical and electrical results were also compared between conventional polycrystalline PVD and our detectors. Leakage current as low as $350\;pA/cm^2$ at the bias voltage of ~ 200 V has been observed. And high sensitivity and good linearity in the response to x-rays was obtained in the film derived by PIB sedimentation method. Our future efforts will concentrate on optimization of film growth techniques for uniform large area deposition on image readout arrays.

• Journal of Korea Technical Association of The Pulp and Paper Industry
• /
• v.34 no.1
• /
• pp.22-29
• /
• 2002

The coated paper was greatly affected by the basic physical properties of the binder as well as the amount of the coating formula. High glass transition temperature (Tg) of the styrene-butadiene (SB) latex, selected as the binder in our study, gave the high stiffness to the coated paper, but lowered the binding force and print gloss. The average particle size of the SB latex also greatly affected to the coated paper so that the smaller particle size improved the rheological property of the coating formula and increased the binding force and print gloss. Another property of the SBR latex, gel content, was important because when its value was small, the latex was easily deformed at the high temperature and increased air permeability to the coated paper. Therefore, the lower gel content consequently resulted in the higher blistering resistance, especially in the web paper. The larger portion of the SB latex in the coated formula improved the binding force and print gloss, but decreased the ink set-off and ink-trapping to the coated paper. The heavier coating improved optical properties such as opacity, paper gloss and paper smoothness, to the coated paper.

• Journal of the Korean Society of Radiology
• /
• v.3 no.1
• /
• pp.11-15
• /
• 2009

In this study, the basic research verifying possibility of applications as radiology image sensor in Digital Radiography was performed, the radiology image sensor was fabricated using a multi-layer technique to decrease dark current. High efficiency materials in substitution for Amorphous Selenium(a-Se) have been studied as a direct method of imaging detector in Digital Radiography to decrease dark current by using PN junction or Hetero junction already used as solar cell, semiconductor. Particle-In -Binder method is used to fabricate radiology image sensor because it has a lot of advantages such as fabrication convenient, high yield, suitability for large area sensor. But high leakage current is one of main problem in Particle-In -Binder method. To make up for the weak points, multi-layer technique is used, and it is considered that high efficient digital radiation sensor can be fabricated with easy and convenient process. In this study, electrical properties such as leakage current, sensitivity, signal linearity is measured to evaluate multi-layer radiation sensor material.