Influences of microstructure on high-cycle fatigue (HCF) limit of high carbon $(>0.7wt.\;\%)$ steel filaments used for tires have been investigated. A series of the fatigue tests was carried out depending on carbon content by using Hunter-type tester at a frequency of 60 Hz at a tension/compression stress of 900 to 1500 MPa. Microstructural changes of the filaments were identified in the lateral direction by using transmission electron microscopy (TEM). It was found that the mechanical properties, such as fatigue limit and tensile strength, were improved with increasing carbon content, which was mainly attributed to decreased lamellar spacing and cementite thickness. However, the fatigue ratio, which is defined as the ratio of the fatigue limit to the tensile strength, was reduced in a higher carbon range of 0.8 to $0.9\;wt.\%$, while the fatigue ratio was nearly constant in a lower carbon range of 0.7 to $0.8\;wt.\%$. Overall mechanical properties of the filaments, depending on carbon content, have been discussed in terms of the microstructural parameter change of lamellar spacing and cementite thickness. In addition, the variation of cementite morphology on the fatigue crack propagation of high carbon $(0.9wt.\;\%)$ filaments will be discussed.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2008.05a
• /
• pp.454-457
• /
• 2008

Effects of patenting temperature on bending fatigue resistance of pearlitic steel filaments were investigated experimentally. The fatigue resistance of steel filaments was carried out by using hunter machine, specially designed for ultra fine-sized steel wires, in the controlled conditions. The transmission electron microscopy (TEM) was used for observing the overall microstructure. It revealed that the fatigue resistance as well as tensile strength increased together with increase of patenting temperature from 510 to $600^{\circ}C$, while the endurance ratio ($\sigma_e/\sigma_{TS}$) of filaments decreased. It is believed that this variation of mechanical properties with change of patenting temperature should be strongly influenced by the change of microstructure. The bending fatigue properties of steel filaments were discussed based on microstructural parameters.