• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.26 no.4
• /
• pp.330-334
• /
• 2013

We developed a package of remote phosphor structure having blue LED chips and phosphors physically separated, and the characteristics were evaluated according to different classifications of phosphor coatings. Remote phosphor was produced by screen printing coating on glass substrate with phosphor content rated paste and heat treatment. After mounting Remote phosphor, which has been classified according to number of coatings, on top of blue LED chips, luminous flux, luminous efficacy, CCT and CRI were measured. The measurement results showed the most suitable characteristics of white LED package as a general light source when the content rate of phosphor in Remote phosphor was 80 wt.% with 3 layers of coatings and thickness over $12{\mu}m$.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1999.11a
• /
• pp.590-593
• /
• 1999

$Y_2SiO_5$:Ce was considered as blue phosphor for field emission display because it had an excellent resistance against brightness saturation. But unfortunately It hadn't a sufficient brightness to be applied to FED. In this experiment It-$In_2O_3$, MgO and $SiO_2$ were coated onto $Y_2SiO_5$:Ce phosphor in order to improve the cathodoluminance(CL properties. The coating structures were identified to be the crystalline phases of $In_2O_3$ and MgO respectively. They had fine particle-like shape and were distributed on the surface of $Y_2SiO_5$:Ce phosphor. It was found that the CL efficiency of $Y_2SiO_5$:Ce phosphors were decreased after coatings with In20:j and MgO in voltage range from 500 V to 5 kV. But the brightness of $Y_2SiO_5$:Ce phosphor was increased after coating of 5 0 2 . And also the aging test showed that $In_2O_3$ coating improved the life time of $Y_2SiO_5$:Ce phosphor.

• Journal of the Korean Society of Visualization
• /
• v.18 no.3
• /
• pp.61-68
• /
• 2020

Thermographic phosphor (TP) thermometry is a noncontact optical measurement method and has been applied in many fields such as combustion and heat transfer. However, due to the limitation of bonding technology and measurement method, most TP thermometry studies were conducted only on the air environment with water-soluble binders. In this paper, a temperature measurement technology in water using TP is proposed by coatings of manganese activated magnesium fluorogermanate (Mg4FGeO6:Mn4+, MFG) with Polydimethylsiloxane (PDMS). Four MFG-PDMS coatings with different thicknesses were prepared. The lifetime of MFG was not affected by the thickness of the coating as a result of the experiment and analysis of phosphor intensity using a photomultiplier tube. To measure the surface temperature field of an immerged body in water, a cylinder-type cartridge heater was coated with MFG doped PDMS. Transient surface temperature field was successfully measured even the initial temperature is higher than the boiling point of water.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 1999.05a
• /
• pp.46-46
• /
• 1999

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.26 no.8
• /
• pp.614-619
• /
• 2013

Recently, remote phosphor is reported for white LED enhancing of phosphor efficiency compared with conventional phosphor-based W-LED. In this study, Remote phosphor was produced by screen printing coating on glass substrate with phosphor contents rated paste and heat treatment. The paste consists of phosphor, lowest softening glass frit and organic binders. Remote phosphor can be well controlled by varying the phosphor content rated paste. After mounting remote phosphor on top of blue LED chip, CCT, CRI, and luminance efficiency were measured. The measurement results showed that CCT, CRI, and luminance efficiency were 6,645, 68, and 1,16l m/W in phosphor 80 wt.% remote phosphor sintered at $600^{\circ}C$.

• Proceedings of the Polymer Society of Korea Conference
• /
• 2006.10a
• /
• pp.233-233
• /
• 2006

[ $Y_{2}O_{2}S:Eu$ ], a red phosphor, coated with silica nanoparticles or nanocomposites composed of silica nanoparticles and polymeric materials such as PMMA and PVP was prepared via sol-gel process. Samples were prepared from four different methods coded P1, P2, P3, and P4. P1 includes a conventional sol-gel process and a dip-coating method while P2 has the same procedure with P1 except that nanocomposites containing both silica nanoparticles and polymer prepared by sol-gel process were used as coating materials. In P3 method, phosphors were dispersed in a solution containing silica precursor, i.e., TEOS and then polymerization was performed to coat onto the phosphors surface while P4 followed the same procedure with P3 except that a solution containing both TEOS and organic monomer were used in preparing coating materials. Among various coating methods examined in this study, uniform coating of phosphor could be achieved by using method P4, i.e., phosphor surface coating in a solution containing hydrophobic monomer and TEOS. Furthermore, $Y_{2}O_{2}S:Eu$ red phosphor coated with nanocomposite composed of PMMA matrix and silica nanoparticles exhibited enhanced PL intensity and long-term stability.

• Korean Journal of Materials Research
• /
• v.10 no.8
• /
• pp.558-563
• /
• 2000

$Y_2SiO_5:Ce$ phosphor was coated with $In_2O_3$, $Al_2O_3$ and $SiO_2$ and then their cathodoluminance(CL)proper-ties required in field emission display were investigated. It was found that luminance efficiency and aging p개perty of $Y_2SiO_5:Ce$ phosphor was decreased with $In_2O_3$coating. For the case of coating, the luminance intensity was in blue phosphor was dramatically increased with $SiO_2$ coating. And also the aging property of $Y_2SiO_5:Ce$ Phosphor coated with $SiO_2$ was significantly improved compared to non-coated sample.

• Macromolecular Research
• /
• v.17 no.11
• /
• pp.907-911
• /
• 2009

To improve the moisture stability of the $CaS:Eu^{2+}$ red phosphor, surface coatings with silica nanoparticles were performed using five different methods, i.e., $P_1$, $P_2$, $P_3$, $P_4$, and $P_5$. The phosphors were coated with silica nanoparticles using a dip coating method ($P_1$) and sol-gel method ($P_2$). The phosphors were coated using a solution containing silica nanoparticles and poly(1-vinyl-2-pyrrolidone), PVP, $(P_3$). The phosphors were also coated with silica nanoparticles by reacting with the 1-vinyl-2-pyrrolidone (VP) monomer ($P_4$) or by reacting with mixtures containing VP and tetraethylorthosilicate ($P_5$). A decrease in the photoluminescence (PL) intensity was observed regardless of the coating methods. However, the moisture stability of the phosphors was enhanced by the coating when aged in a temperature-controlled humidity chamber. Among these methods, the $P_4$ (or $P_5$) method exhibited the greatest increase in moisture stability of the phosphors. The coated phosphors showed a relatively constant intensity with aging time, whereas the uncoated phosphor showed a decrease.

• Journal of the Korean institute of surface engineering
• /
• v.41 no.4
• /
• pp.169-173
• /
• 2008

The objective of this study is to coat the $SiO_2$ layer uniformly on the ZnS:Cu phosphors by using Sol-Gel method. From results of SEM micrographs observation, XRD and XPS analysis, it could be confirmed that $SiO_2$ layer was relatively well coated on ZnS:Cu particles. $Ag_2S$ was used as a decoding chemical to analyze the dense and uniform coating performance of $SiO_2$ layer on phosphor particles. It could be concluded that phosphors synthesized from our two step replacement method showed strong blue peak comparing to other method and rather weak green peak also. Obtained particle size of phosphors were about 20m diameter. Luminescence properties of the phosphors were examined by photoluminescence spectra at the excitation wavelength of 270 nm.

• Current Optics and Photonics
• /
• v.1 no.4
• /
• pp.284-288
• /
• 2017

In order to investigate the ultraviolet-excited photoluminescence properties of phosphor coatings and their relationship to thickness, Lumogen coatings with different thicknesses were deposited on quartz substrates and charge-coupled device chips by thermal evaporation. The variation of the film thickness affected the crystallite size, surface roughness and fluorescence signal. It was found that the Lumogen coating with the thickness of 420 nm has the largest luminescent signal and conversion efficiency, and the corresponding coated charge-coupled devices had the maximum quantum efficiency in the ultraviolet. These results provided one key parameter for improving the sensitivity of Lumogen coated charge-coupled devices to ultraviolet light.