• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.48 no.6
• /
• pp.462-468
• /
• 1999

Room temperature vulcanizing (RTV) silicone rubber has been widely used to coat porcelain insulators to render water repellency to prevent formation of water film on the surface and thus to suppress the leakage current and consequently flashover. However, the electrical property and the hydrophobicity of RTV silicone rubber coating under outdoor condition may be influenced by many environmental factors. In this studyvarious treatments, such as salt-fog, salt water immerging and UV irradiation were applied to the samples to investigate the change of the electrical property and hydrophobicity. As a result the leakage current increased and contact angle decreased asthe degradation time is longer. But the degraded RTV silicone rubber has recovered its hydrophobicity during the drying time in ambient condition because LMW(Low Molecular Weight) silicone fluid diffused from the bulk to the surface.

• Proceedings of the KIEE Conference
• /
• 1999.07d
• /
• pp.1651-1653
• /
• 1999

Room Temperature Vulcanizing (RTV) Silicone Rubber has been widely used to coat porcelain insulator to prevent formation water filming on insulator surface. and RTV silicone rubber has water repellency to suppress leakage current and consequent flashover. RTV silicone rubber's surface has been degradated by outdoor condition such as dust, salt, and water. etc. ESDD(Equivalent Salt Deposit Density) and leakage currents are increased by polymer surface toughness and degradation. In this paper, we investigated relations of surface toughness, ESDD, and leakage currents.

• Proceedings of the KIEE Conference
• /
• 1998.11c
• /
• pp.866-868
• /
• 1998

Room temperature vulcanizing(RTV)silicone rubber has been widely used to coat porcelain insulators to render water repellency to prevent formation of water filming on the surface and thus to suppress the leakage current and consequent flashover. However, the electrical property and its hydrophobicity of RTV silicone rubber coating under outdoor conditions may be influenced by many environmental factors. In this study various treatments, such as salt-fog, salt water immerging and UV irradiation were applied to samples for investigation the change of the electrical property and hydrophobicity. As a result the leakage current increased and contact angle decreased as the degradation time longer. But the degraded RTV silicone rubber has recovered its hydrophobicity during the drying time in ambient condition because LMW(Low Molecular Weight)silicone fluid diffused from the bulk to the surface.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.07a
• /
• pp.597-600
• /
• 2001

In this paper, we evaluated the effect of accumulated charges on hydrophobicity of room temperature vulcanized(RTV) silicone rubber, which could improve the contamination performance of porcelain insulators, with uv radiation time. Outdoor insulating material could be charged by the corona discharge on field intensified area of insulator and discharge between the water drops. In addition, we performed the accelerated uv radiation on samples and investigated the change of charging decay with time. In this results, it is found that silica-like structure on the surface of RTV silicone rubber was formed by uv treatments and this layer have the characteristic of retaining the charges on surface for a long time. These charges have effects on its hydrophobicity and so adversely effects on contamination performance. Based on our results, we discussed the other degradation mechanism with well known ones.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11b
• /
• pp.266-269
• /
• 2001

This paper investigated the aging characteristic under long-term corona discharge on roan temperature vulcanized silicone rubber, which has been using as a protective coating material for solving the contaminant problem. The applied electrical field is 10kV/cm ac and corona discharge treatment was applied on RTV silicone rubber sheet for maximum 250 hours. With the duration of corona discharge. the diffusible low molecular weight species increased, which was determined the usage of n-hexane extraction method. In addition, the contaminant layer was formed on the treated surface, and then measured the contact angle. We investigated the relation of contact angle and diffusible low molecular weight species. It is found that scissor of main chain PDMS and side chains $(CH_3)$ and the generation of LMW species were occurred by a corona discharge. The improvement of hydrophobicity rate is thought due to the increase of diffusible LMW species.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11a
• /
• pp.266-269
• /
• 2001

This paper investigated the aging characteristic under long-term corona discharge on loon temperature vulcanized silicone rubber, which has been using as a protective coating material for solving the contaminant problem. The applied electrical field is 10kV/cm ac and corona discharge treatment was applied on RTV silicone rubber sheet for maximum 250 hours. With the duration of corona discharge, the diffusible low molecular weight species increased, which was determined the usage of n-hexane extraction method. In addition, the contaminant layer was formed on the treated surface, and then measured the contact angle. We investigated the relation of contact angle and diffusible low molecular weight species. It is found that scissor of main chain PDMS and side chains (CH$_3$) and the generation of LMW species were occurred by a corona discharge. The improvement of hydrophobicity rate is thought due to the increase of diffusible LMW species.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.13 no.7
• /
• pp.598-606
• /
• 2000

In this paper we investigated the relation between the surface degradations and anti-pollution characteristics of Room Temperature Vulcanized(RTV) silicone rubber coating that has different roughness through immersing into saline water. We utilized several analytic techniques such as atomic force microscopy(AFM) scaning electron microscopy(SEM) contact angle Salt Deposit Density(SDD) and average leakage current under the condition of salt fog. It is found that the surface roughness of treated RTV silicone rubber increased and the hydrophobicity of sample surface decreased with increasing the duration o immersion into water due to the erosion of base polymer the melting down alumina trihydrate(ATH) and the diffusion of Low Molecular weight(LMW) fluid. Despite the roughness of surface had been increased by water immersion excellant anti-pollution and recovery characteristics were maintained and SDD saturated to 0.1~0.14mg/cm$^2$. The average leakage current under salt fog increased with surface roughness. Measurement of average leakage current will be helpful to investigate surface degradation and lifetime expectation of RTV silicone coating.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.52 no.8
• /
• pp.359-364
• /
• 2003

Ageing characteristics of RTV coating materials by corona discharge have been studied. The hydrophobicity recovery of RTV coating materials with 300${\mu}{\textrm}{m}$ thickness was identical with a bulk silicone materials. The RTV coating materials hydrophobicity has been almost lost when its were discharged during 40 seconds by corona discharge of 10㎸, and recovered after about 45 hours. The resistivity of RTV coating materials has not been recovered after 45 hours, though after 80 hours the initiation resistivity value has been recovered up to 95%. There was no critical change of compounds(such as Si and Al) on RTV surfaces by the corona discharge treatment until 100 seconds. In the test of arc erosion, it was seen that the coating sample with silicone rubber as a base material have more longer burn-out time than other samples with FRP or glass base.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.05e
• /
• pp.35-39
• /
• 2003

An ageing characteristics of RTV coating materials by corona discharge have been studied. The recovery of a hydrophobicity of RTV coating materials with the thickness of $300{\mu}m$ was in identical with a bulk silicone materials. The hydrophobicity of RTV coating materials has been almost lost when its were discharged during 40 seconds by corona with 10kV, and recovered after about 45 hours. But the resistivity of RTV coating materials has not been recovered after 45 hours, even though after 80 hours the 95% of initiation resistivity value has been recovered. There was no critical compounds(such as Si and Al) changes on RTV surfaces by the corona discharge treatment until 100 seconds. In the test of arc erosion, it was seen that the coating sample with silicone rubber as a base material have more longer bum-out time than other samples with FRP or glass base.

• Proceedings of the KIEE Conference
• /
• 2001.07c
• /
• pp.1337-1339
• /
• 2001

We have investigated the relation between the molecular weight distribution (MWD) of diffusible species and the recovery rate of hydrophobicity of room-temperature vulcanizing (RTV) silicone rubber (SIR) using solvent extraction at various temperatures. It was observed that the extract had a MWD ranging from a few hundreds g/mol to hundreds of thousands g/mol. By measuring the migration of siloxane to the extracted SIR surface through a thin carbon coating, the aspect of migration of diffusible species was observed as a real time plot, and the time constant of the migration was also calculated. According to the time dependence of IR-absorbance, the time constant was increased with the increase of MW of the extracts.