• Korean Journal of Metals and Materials
• /
• v.50 no.11
• /
• pp.855-859
• /
• 2012

Samples with compositions of 80 wt% Mg-14 wt% Ni-6 wt% $Fe_2O_3$ and 80 wt% Mg-14 wt% Ni-6 wt% Ti were prepared by mechanical grinding under hydrogen (reactive mechanical grinding). Their hydrogen absorptions during reactive mechanical grinding were examined. TGA and BET analysis were employed to investigate the hydrogen storage properties of the prepared alloys. TGA analysis of the $Mg-14Ni-6Fe_2O_3$ showed an absorbed hydrogen quantity of 6.91 wt% while that of Mg-14Ni-6Ti was 2.59 wt%. BET analysis showed that the specific surface areas of $Mg-14Ni-6Fe_2O_3$ and Mg-14Ni-6Ti after reactive mechanical grinding were $264m^2/g$ and $64m^2/g$, respectively. The larger absorbed hydrogen quantity and the larger specific surface area of $Mg-14Ni-6Fe_2O_3$ after RMG than those of Mg-14Ni-6Ti after RMG showed that the effects of $Fe_2O_3$ addition are much stronger than those of Ti addition during reactive mechanical grinding.

• Transactions of the Korean hydrogen and new energy society
• /
• v.14 no.4
• /
• pp.321-326
• /
• 2003

We tried to improve the $H_2$-sorption properties of Mg by mechanical grinding under $H_2$ (reactive grinding) with CoO. The sample Mg+10wt.%CoO as prepared absorbs 1.25wt.% hydrogen and the activated sample absorbs 2.39wt.% hydrogen for 60min at 598K, $11.2barH_2$. The reactive grinding of Mg with CoO increases the $H_2$-sorption rates by facilitating nueleation(by creating defects on the surface of the Mg particles and by the additive), by making cracks on the surface of Mg particles and reducing the particle size of Mg and thus by shortening the diffusion distances of hydrogen atoms. Hydriding-dehydriding cycling increases the $H_2$-sorption rates by making cracks on the surface of Mg particles and reducing the particle size of Mg.

• Korean Journal of Metals and Materials
• /
• v.50 no.12
• /
• pp.949-953
• /
• 2012

$MgH_2$ was employed as a starting material instead of Mg in this work. A sample with a composition of 94 wt% $MgH_2-6$ wt% Ni (called $MgH_2-6Ni$) was prepared by reactive mechanical grinding. The hydriding and dehydriding properties were then examined. An $MgH_2-Ni$ hydrogen storage alloy that does not require an activation process was developed. The alloy was prepared in a planetary ball mill by grinding for 4 h at a ball disc revolution speed of 250 rpm under a hydrogen pressure of about 12 bar. The sample absorbed 3.74 wt% H for 5 min, 4.07 wt% H for 10 min, and 4.41 wt% H for 60 min at 573 K under 12 bar $H_2$, and desorbed 0.93 wt% H for 10 min, 1.99 wt% H for 30 min, and 3.16 wt% H for 60 min at 573 K under 1.0 bar $H_2$. $MgH_2-6Ni$ after reactive mechanical grinding contained ${\beta}-MgH_2$ (a room temperature form of $MgH_2$), Ni, ${\gamma}-MgH_2$ (a high pressure form of $MgH_2$), and a very small amount of MgO. Reactive mechanical grinding of Mg with Ni is considered to facilitate nucleation, and to reduce the particle size of Mg. $Mg_2Ni$ formed during reactive mechanical grinding also increases the hydriding and dehydriding rates of the sample.

• Korean Journal of Metals and Materials
• /
• v.50 no.5
• /
• pp.383-387
• /
• 2012

The activation of Mg-10 wt%$Fe_2O_3$ was completed after one hydriding-dehydriding cycle. Activated Mg-10 wt%$Fe_2O_3$ absorbed 5.54 wt% H for 60 min at 593 K under 12 bar $H_2$, and desorbed 1.04 wt% H for 60 min at 593 K under 1.0 bar $H_2$. The effect of the reactive grinding on the hydriding and dehydriding rates of Mg was weak. The reactive grinding of Mg with $Fe_2O_3$ is believed to increase the $H_2$-sorption rates by facilitating nucleation (by creating defects on the surface of the Mg particles and by the additive), by making cracks on the surface of Mg particles and reducing the particle size of Mg and thus by shortening the diffusion distances of hydrogen atoms. The added $Fe_2O_3$ and the $Fe_2O_3$ pulverized during mechanical grinding are considered to help the particles of magnesium become finer. Hydriding-dehydriding cycling is also considered to increase the $H_2$-sorption rates of Mg by creating defects and cracks and by reducing the particle size of Mg.

• Transactions of the Korean hydrogen and new energy society
• /
• v.22 no.6
• /
• pp.787-793
• /
• 2011

A 76.5wt%Mg - 23.5wt%Ni (Mg-23.5Ni) sample was prepared by reactive mechanical grinding (RMG) and its hydriding and dehydriding properties were then investigated. Activation of the Mg-23.5Ni sample was completed only after two hydriding (under 12 bar $H_2$) - dehydriding (under 1.0 bar $H_2$) cycles at 593K. The reactive mechanical grinding of Mg with Ni is considered to facilitate nucleation and shorten diffusion distances of hydrogen atoms. After hydriding - dehydriding cycling, the Mg-23.5Ni sample contained Mg2Ni phase.

• Korean Journal of Metals and Materials
• /
• v.50 no.5
• /
• pp.375-381
• /
• 2012

Magnesium prepared by mechanical grinding under $H_2$ (reactive mechanical grinding) with transition elements or oxides showed relatively high hydriding and dehydriding rates when the content of additives was about 20 wt%. Ni was chosen as a transition element to be added. $Fe_2O_3$ was selected as an oxide to be added. Ti was also selected since it was considered to increase the hydriding and dehydriding rates by forming Ti hydride. A sample $Mg-14Ni-3Fe_2O_3-3Ti$ was prepared by reactive mechanical grinding, and its hydrogen storage properties were examined. This sample absorbs 4.02 wt% H for 5 min, and 4.15 wt% H for 10 min, and 4.42 wt% H for 60 min at n = 2. It desorbs 2.46 wt% H for 10 min, 3.98 wt% H for 30 min, and 4.20 wt% H for 60 min at n = 2. The effects of the Ni, $3Fe_2O_3$, and Ti addition, and hydriding-dehydriding cycling were discussed.

• Korean Journal of Materials Research
• /
• v.24 no.3
• /
• pp.129-134
• /
• 2014

Pure $MgH_2$ was milled under a hydrogen atmosphere (reactive mechanical grinding, RMG). The hydrogen storage properties of the prepared samples were studied at a relatively low temperature of 423 K and were compared with those of pure Mg. The hydriding rate of the Mg was extremely low (0.0008 wt% H/min at n = 4), and the $MgH_2$ after RMG had higher hydriding rates than that of Mg at 423 K under 12 bar $H_2$. The initial hydriding rate of $MgH_2$ after RMG at 423 K under 12 bar $H_2$ was the highest (0.08 wt% H/min) at n = 2. At n = 2, the $MgH_2$ after RMG absorbed 0.39 wt% H for 5 min, and 1.21 wt% H for 60 min at 423K under 12 bar $H_2$. At 573 K under 12 bar $H_2$, the $MgH_2$ after RMG absorbed 4.86 wt% H for 5 min, and 5.52 wt% H for 60 min at n = 2. At 573 K and 423 K under 1.0 bar $H_2$, the $MgH_2$ after RMG and the Mg did not release hydrogen. The decrease in particle size and creation of defects by reactive mechanical grinding are believed to have led to the increase in the hydriding rate of the $MgH_2$ after RMG at a relatively low temperature of 423 K.

• Korean Journal of Metals and Materials
• /
• v.50 no.1
• /
• pp.64-70
• /
• 2012

Samples of pure Mg, 76.5 wt%Mg-23.5 wt%Ni, and 71.5 wt%Mg-23.5 wt%Ni-5 wt%$Fe_2O_3$ were prepared by reactive mechanical grinding and their hydriding and dehydriding properties were then investigated. The reactive mechanical grinding of Mg with Ni is considered to facilitate nucleation and to shorten diffusion distances of hydrogen atoms. After hydriding-dehydriding cycling, the 76.5 wt%Mg-23.5 wt%Ni and 71.5 wt%Mg-23.5 wt%Ni-5 wt%$Fe_2O_3$ samples contained $Mg_2Ni$ phase. In addition to the effects of the creation of defects and the decrease in particle size, the addition of Ni increases the hydriding and dehydriding rates by the formation of $Mg_2Ni$. Expansion and contraction of the hydride-forming materials (Mg and $Mg_2Ni$) with the hydriding and dehydriding reactions are also considered to increase the hydriding and dehydriding rates of the mixture by forming defects and cracks leading to the fragmentation of particles. The reactive mechanical grinding of Mg-Ni alloy with $Fe_2O_3$ is considered to decrease the particle size.

• Journal of Ceramic Processing Research
• /
• v.20 no.6
• /
• pp.609-616
• /
• 2019

The optimum powder to ball ratio was examined, which is one of the important conditions in reactive mechanical grinding processing. Yttria (Y2O3)-stabilized zirconia (ZrO2) (YSZ), Ni, and graphene were chosen as additives to enhance the hydriding and dehydriding rates of Mg. Samples with a composition of 92.5 wt% Mg + 2.5 wt% YSZ + 2.5 wt% Ni + 2.5 wt% graphene (designated as Mg-2.5YSZ-2.5Ni-2.5graphene) were prepared by grinding in hydrogen atmosphere. Mg-2.5YSZ-2.5Ni-2.5graphene had a high effective hydrogen-storage capacity of almost 7 wt% (6.85 wt%) at 623 K in 12 bar H2 at the second cycle (n = 2). Mg-2.5YSZ-2.5Ni-2.5graphene contained Mg2Ni phase after hydriding-dehydriding cycling. Mg-2.5YSZ-2.5Ni-2.5graphene had a larger quantity of hydrogen absorbed for 60 min, Ha (60 min), than Mg-2.5Ni-2.5graphene and Mg-2.5graphene. The addition of YSZ also increased the initial dehydriding rate and the quantity of hydrogen released for 60 min, Hd (60 min), compared with those of Mg-2.5Ni-2.5graphene. Y2O3-stabilized ZrO2, Ni, and graphene-added Mg had a higher initial hydriding rate and a larger Ha (60 min) than Fe2O3, MnO, or Ni and Fe2O3-added Mg at n = 1.

• Korean Journal of Metals and Materials
• /
• v.50 no.6
• /
• pp.463-468
• /
• 2012

A 71.5 wt%Mg-23.5 wt%Ni-5 wt%$Fe_2O_3$ (Mg-23.5Ni-$5Fe_2O_3$) sample was prepared by a quite simple process, reactive mechanical grinding, and its hydriding and dehydriding properties were then investigated. The reactive mechanical grinding of Mg with Ni and $Fe_2O_3$ is considered to facilitate nucleation and shorten the diffusion distances of the hydrogen atoms. After the hydriding-dehydriding cycling, the Mg-23.5Ni-$5Fe_2O_3$ sample contained $Mg_2Ni$ phase. Expansion and contraction of the hydride-forming materials (Mg and $Mg_2Ni$) with the hydriding and dehydriding reactions are also considered to increase the hydriding and dehydriding rates of the mixture by forming defects and cracks leading to the fragmentation of the particles. The temperature dependence of the hydriding rate of the sample is discussed.