• Journal of the Korean Institute of Gas
• /
• v.9 no.1 s.26
• /
• pp.21-25
• /
• 2005

This paper was studied on the corrosion behavior of STS 304 for gas boiler in the condensed water, the electrochemical polarization test of STS 304 for gas boiler in the condensed water was carried out. And the corrosion behavior of STS 304 was considered. The main results are as following: 1) As corrosion environment is acidified from neutrality, the polarization resistance of STS 304 decreases and the corrosion potential is less noble. 2) The corrosion reaction mechanism of STS 304 is cathodic control. 3) As corrosion environment is acidified, the passive potential range of STS 304 decreases. Also, the passive current density of STS 304 increases.

• Journal of Advanced Marine Engineering and Technology
• /
• v.35 no.1
• /
• pp.68-74
• /
• 2011

This papers investigated the mechanical characteristics and the weldability of identical as well as dissimilar welding by GTAW for STS 304 and STS 316L. It is applied to double wall gas pipe of duel fuel engine for LNG carrier. Consequently, the weldability of dissimilar and identical welded zone of STS 304 decreased compared to base metal significantly. The result of microstructure observation for welded zone, a degree of acicular ferrite in welding zone for STS 304 presented more than STS 316L. The hardness of welding zone for STS 304 presented higher value than that for STS 316L by this effect.

• Korean Journal of Acupuncture
• /
• v.24 no.1
• /
• pp.59-63
• /
• 2007

Objectives : To discuss the biocompatibility of stainless steel for using acupuncture needles. Results and Conclusions : It is widely assumed that stainless steel is one of the good corrosion-resistant materials and is safe for human body, Most of metal acupuncture needles are made of STS304 and STS316 in light of human body safety: STS304 in more differences between STS304 and STS316 in light of human body safety: STS304 is more vulnerable to oxidation than STS316. A variety of literature survey showed that although STS316 is more corrosion-resistant than STS304 there is no evidence supporting the hypothesis that STS304 has the potential danger to human body, Further study would be necessary to draw more decisive conclusion.

• Journal of the Korean institute of surface engineering
• /
• v.49 no.1
• /
• pp.26-31
• /
• 2016

In this paper, the characteristics of a cavitation-erosion damage behavior on the STS 304 and hot-dip aluminized STS 304 under cavitation environment in sea water solution was investigated. The electrochemical experiments were carried out by potential measurement, anodic/cathodic polarization test, Tafel analysis, and also galvanostatic experiment in current density variables for the samples. The apparatus of cavitation-electrochemical experiment was manufactured in compliance with modified ASTM G-32 standard, with the conditions of sea water temperature of $25^{\circ}C$ and the measurement, amplitude of $30{\mu}m$. The damage behavior was analyzed by an observation of surface mophologies and a measurement of damage depth by a scanning electron microscope(SEM) and a 3D microscope, respectively, after electrochemical test. After polarization experiment under cavitation environment, much higher damage depths for the hot-dip aluminized STS 304 were observed comparing to the untreated STS 304. In addition, higher corrosion current density in hot-dip aluminized STS 304 presented than that of untreated STS 304 as a result of Tafel analysis.

• Journal of the Korean Society of Safety
• /
• v.31 no.4
• /
• pp.9-14
• /
• 2016

STS304L of membrane structure has been used for a LNG storage tank and has exposed long time under the cryogenic temperature. The purposes of this study are to evaluate the mechanical properties of base and used materials for STS304L of membrane. The tensile and high cycle fatigue tests were investigated for STS304L of membrane used over 20 years at room temperature and $-162^{\circ}C$. In addition, the test of base STS304L was performed in order to compare with used material properties. The chemical composition and phase change were investigated from EDS and XRD. From results of tensile test, yield and ultimate tensile strengths of used STS304L are smaller than those of base STS304L. S-N curves were obtained from fatigue tests at both temperatures. Also, P-S-N curves were presented with statistical method recommend by JSME-S002. Fractography was conducted for analysis of fracture mechanisms.

• Journal of Fisheries and Marine Sciences Education
• /
• v.19 no.3
• /
• pp.323-328
• /
• 2007

This paper was studied on the effect of the specific resistance of water on corrosion characteristics of STS 304 for gas boiler. The electrochemical polarization test of STS 304 for gas boiler was carried out. And the polarization resistance, uniform corrosion, corrosion behavior by impressed potential and corrosion sensitivity of STS 304 with specific resistance were considered. The main results are as following: 1) With being low the specific resistance of water, the polarization resistance and corrosion potential of STS 304 decreases, while corrosion current density increases. 2) Under constant impressed potential, the corrosion sensitivity of STS 304 is large with being low the specific resistance due to synergy effect of Cl ion.

• Journal of the Korean institute of surface engineering
• /
• v.51 no.4
• /
• pp.218-223
• /
• 2018

In this study, we proposed a new ultrasonic-chemical decontamination process for decontaminating radioactive corrosion products during the maintenance of reactor coolant pump (RCP). The actual decontamination process was reproduced in the laboratory. And the corrosion characteristics of stainless steel (STS), constituting the RCP interior parts, were examined. The weight-loss measurment and polarization experiment were carried out in order to determine the corrosion characteristics of STS 304 and STS 415 by repeated decontamination processes. The STS 304 presented a little corrosion damage, which was almost indistinguishable from visual observation. The weight-loss rate of STS 304 was also significantly lower. On the other hand, STS 415 showed severe corrosion damage on its surface, greater weight-loss rate and higher corrosion current density than STS 304.

• Journal of the Korean Institute of Gas
• /
• v.9 no.4 s.29
• /
• pp.6-10
• /
• 2005

This paper was studied on the damage behavior of stainless steel (STS 304) for gas boiler with specific resistance. The electrochemical polarization test of STS304 for gas boiler was carried out. And the anodic polarization and damage aspect, such as pitting corrosion, was considered. With being low specific resistance, the passive current density of STS 304 increases, passive region and pitting potential is low. Also, the patting aspect of STS304 In specific resistance $74{\Omega}{\cdot}m$ water little appears, the pitting number increases and the damage behavior, such as pitting aspect, gradually grow bigger with being low specific resistance.

• Journal of Welding and Joining
• /
• v.9 no.4
• /
• pp.28-39
• /
• 1991

The change of microstructure in the bonded interlayer and mechanical properties of the joints were investigated during Transient Liquid Phase Diffusion Bonding(TLP bonding) of STS304/SM17C and STS304/SM45C couples using Ni base amorphous alloys added boron and prepared alloy as insert metal. Main experimental results obtained in this study are as follows: 1) Isothermal solidification process was completed much faster than theoretically expected time, 14ks at 1473K temperature. Its completion times were 3.6ks at 1423K, 2.5ks at 1473K and 1.6ks at 1523K respectively. 2) As the concentration of boron in the insert metal increased, the more borides were precipitated near bonded interlayer and grain boundary of STS304 side during isothermal solidification process, its products were $M_{23}P(C,B)_6}_3)$ The formation of grain boundary during isothermal solidification process was completed at structural carbon steel after starting the solidfication at STS304 stainless steel. 4) The highest value of hardness was obtained at bonded interface of STS304 side. The desirable tensile properties were obtained from STS304/SM17C, STS304/SM45C using MBF50 and experimentally prepared insert metal with low boron concentration.

• Journal of the Korean Society for Heat Treatment
• /
• v.34 no.4
• /
• pp.171-178
• /
• 2021

In the present study, we comparatively investigated the microstructures of two hot-rolled stainless steel clad plates; STS 304L - low carbon steel A516-70N and STS 316L - A516-70N. The STS 304L/A516-70N clad plate (Clad_304L_Ni) had a Ni-interlayer between stainless steel and carbon steel and a 90 ㎛ thick deformation band of unrecrystallized austenite grains on the stainless steel. The STS 316L/A516-70N clad plate (Clad_316L) had no interlayer and almost fully recrystallized austenite grains. Clad_304L_Ni exhibited the thinner a decarburized layer in carbon steel and a total carburized layer in stainless steel than Clad_316L. However, a severely carburized layer in stainless steel was thicker for Clad_304L_Ni than Clad_316L. Hardness profiles near the interface of clad plates matched well with microstructures at locations where the hardness values were measured.