• Proceedings of the KSR Conference
• /
• 2007.11a
• /
• pp.852-858
• /
• 2007

The durability of carbon/epoxy composites under salt water environment was investigated through salt water spray tester. Salt water environment was obtained through salt spray and salt immersion. 5% NaCl solution was used for salt water as natural salt water. Mechanical test was performed to obtain tensile properties, flexural properties, and shear properties of carbon/epoxy composite over 12 months under salt water environment. Dynamic mechanical analyzer was used to investigate thermal analysis properties such storage modulus, loss modulus, and tan ${\delta}$. Also FT/IR test was conducted to investigate a change in chemical structure. According to the results, mechanical properties were found to be slowly degraded as a function of exposure times. Regarding to thermal analysis properties, storage modulus was insensitive to exposure times, but loss modulus was shown to be slightly decreased. Although the shape and location of peak in FT/IR were not much changed, the intensity of peak in FT/IR was affected on exposure times. We also found that salt water immersion was more severe to the durability of carbon/epoxy composite rather than salt water spray.

• Proceedings of the KSR Conference
• /
• 2005.05a
• /
• pp.391-396
• /
• 2005

Salt water spray test and salt water immersion test were experimentally conducted in order to investigate the durability of fiber reinforced composites under salt water environment. The specimens were made of glass fabric reinforcement and phenolic resin. Mechanical test was performed to obtain mechanical properties such as tensile properties, flexural properties, and shear properties by varying with exposure times. Also dynamic mechanical test and FTIR were conducted to investigate a change in chemical structure as well as thermal analysis properties such as storage shear modulus, loss shear moduls, and tan ${\delta}$. According to the results, salt water environment has effected on mechanical properties and thermal analysis properties and especially the durability of glass fabric/phenolic composites were severely affected on salt water immersion environment rather than salt water spray environment.

• Proceedings of the Korean Society of Marine Engineers Conference
• /
• 2006.06a
• /
• pp.271-272
• /
• 2006

Zinc confers high corrosion resistance by acting as a sacrificial anode, and a zinc coating improves the appearance of steel. Chromate conversion coating (CCC) films are still one of the most efficient surface treatments for steel. Although such films can self-repair via the dissolution of Cr(VI), dissolved Cr(VI) have adverse effects on humans, and the environment. Therefore, we examined the corrosion protection property and morphology of colloidal silica conversion films as an alternative to CCC films. The corrosion behavior was investigated in 3% NaCl solution using electrochemical techniques, including electrochemical impedance spectroscopy, open circuit potential, and the salt spray test(SST). Corrosion was implied by the appearance of red rust on the specimen surface. In corrosion resistance at 3% NaCl solution, red rust appeared at 15-20, 55-70, and 83-98 days on Zn-electroplated steel, colloidal silica conversion-coated specimens, and CCC-coated specimens, respectively. In the salt spray test, the colloidal silica film provided better corrosion protection than CCC films, i.e., red rust appeared at 96 hours on the Zn-electroplated steel sheet, at 432 hours with the CCC films, and at 888 hours with silica conversion coating.

• Proceedings of the Korean Society of Environment and Ecology Conference
• /
• 2009.10a
• /
• pp.77-80
• /
• 2009

• Composites Research
• /
• v.23 no.1
• /
• pp.44-50
• /
• 2010

In this paper, two different experiments, namely, salt water spray and salt water immersion, were performed to reproduce the contact of composites with the seawater for three kinds of woven fabric composite material systems which would be used for the WIG(wing in ground effect)craft. After aging 140 days in the salt water environment, material properties of carbon/epoxy and glass/epoxy composite such as tensile, compressive and shear stiffness and strength, and inter-laminar shear strength (ILSS) were measured. By comparing baseline material properties with degraded ones, the effects of the salt water environment on the composite mechanical properties were evaluated. From the experiments, it was confirmed that the difference in aging conditions had very small influence on composite properties. And it was found that tensile strength of carbon/epoxy composites showed little degradation, but much more degradation was observed in glass/epoxy composites. And large degradations on matrix dominant properties were observed. The salt water could damage the fiber-matrix interface, matrix properties and the glass fiber.

• Composites Research
• /
• v.18 no.4
• /
• pp.27-34
• /
• 2005

Salt water spray and immersion tests were experimentally conducted for over 6 months to investigate the durability of glass fabric/phenolic composites under salt water environment. Mechanical properties such as tensile properties, flexural properties, and shear properties were evaluated and thermal analysis properties such as storage shear modulus, loss shear moduls, and tan 6 were obtained through a DMA. A change in chemical structures was analyzed through a FTIR. According to the results, mechanical properties and thermal analysis properties were sensitive to salt water environment and these properties began to degrade in increasing in exposure times. However, tensile and flexural moduli started to decrease and then slightly increase as increasing in exposure times due to plasticization and crosslinking in matrix as well as physical swelling in composites. Beyond a certain exposure times, these properties began to decrease as further increasing in exposure times. Also the shape and location of peaks in FTIR curves were insensitive to exposure times, but the intensity of peaks would be. finally we found that the durability of glass fabric/phenolic composites were affected on salt water immersion environment rather than salt water spray environment.

• Proceedings of the Korean Society of Marine Engineers Conference
• /
• 2006.06a
• /
• pp.265-266
• /
• 2006

The chemical conversion coating formed on magnesium alloy investigated for low cost and harmless in environment by using the colloidal silica as the main component. The film formed in 298 K is thick, the film, which was thought combination of Si-O, was formed. The film formed in 313 K is thinner than that in 298 K. The quantity of film formed at high temperature such as 333 K and 353 K is smaller than dissolved quantity. At the anodic polarization experiment, corrosion resistance in sealing by hot water after chemical conversion treatment in basic solution condition get worse than that in comparison with basic solution condition. In salt spray test, the ratio of black rust on specimen that did not conducted chemical conversion treatment was five times or more compared with those of chemical conversion treated specimen. The film thickness of chemical conversion coating produced by alkali treatment process is thinner than in comparison with that of specimen produced in basic chemical conversion treatment solution condition. It is thought, however, that it showed good corrosion resistance during salt spray test because the area of microcracks is small.

• Journal of Bio-Environment Control
• /
• v.28 no.4
• /
• pp.454-460
• /
• 2019

The purpose of this study is to analyze the distribution characteristics of mist spray particle size by devising a rotary mist spraying device to develop the evaporative salt water desalination system. The rotary mist spraying device was consisted of a BLDC sirocco fan, a spinning fan, a fan fixed shaft and a salt water supply device etc. In this study we analyzed the characteristics of spray particle size and distribution according to the variation of sirocco fan surface roughness(Ra, ${\mu}m$), revolutions(rpm) and salt water flow rate(mL/min). When sirocco fan surface roughness(Ra) was in the range of $0.27{\sim}7.65{\mu}m$, the spray particle size was $0.117{\sim}1.360{\mu}m$. And then more than 90% of spray particles were found to be less than $0.50{\mu}m$. When sirocco fan surface roughness(Ra) was in the range of $12.70{\sim}22.84{\mu}m$, the spray particle size was $2.51{\sim}184.79{\mu}m$ and more than 98% of spray particles were found to be less than $13.59{\mu}m$. To analyze the effect of fan rotation speed on the size and distribution of spray particles, when surface roughness Ra was fixed $0.27{\mu}m$ and fan rotation speed and salt water flow rate was respectively changed at 3,800~5,600 rpm and 2.77~8.28 mL/min, spray particle size was $0.314{\sim}0.541{\mu}m$. And when salt water flow rate was 9.74 mL/min and fan rotation speed was 3,800~5,200 rpm, spray particle size was in the range of $29.29{\sim}341.46{\mu}m$ and in case of 5,600 rpm more than 98.23% of spray particles were in the range of $2.51{\sim}13.59{\mu}m$.

• Corrosion Science and Technology
• /
• v.17 no.5
• /
• pp.211-217
• /
• 2018

Natural degradation of grounding-electrode in soil environment should be monitored for several decades to predict the lifetime of the grounding electrode for efficient application and management. However, long-term studies for such electrodes have many practical limitations. The conventional accelerated corrosion test is unsuitable for such studies because simulated soil corrosion process cannot represent the actual soil environment. A preliminary experiment of accelerated corrosion test was conducted using existing test standards. The accelerated corrosion test that reflects the actual soil environment has been developed to evaluate corrosion performances of grounding-electrodes in a short period. Several test conditions with different chamber temperatures and salt spray were used to imitate actual field conditions based on ASTM B162, ASTM B117, and ISO 14993 standards. Accelerated degradation specimens of copper-bonded electrodes were made by the facile method and their corrosion performances were investigated. Their corrosion rates were calculated to $0.042{\mu}m/day$, $0.316{\mu}m/day$, and $0.11{\mu}m/day$, respectively. These results indicate that accelerated deterioration of grounding materials can be determined in a short period by using cyclic test condition with salt spray temperature of $50^{\circ}C$.

• Journal of the Korean Society for Railway
• /
• v.11 no.4
• /
• pp.357-363
• /
• 2008

This study investigates the durability of carbon/epoxy composites for use on train car bodies under a salt water spray environment. Salt water solution with 5% NaCl, similar to natural salt water, was used for the salt water environmental tests. The specimens were obtained from a composite panel consisting of an epoxy matrix reinforced with T700 carbon fabric. The specimens were exposed to the salt water environment for up to 12 months. Mechanical tests were performed to obtain tensile properties, flexural properties, and shear properties. Dynamic mechanical analysis was used to measure such thermal properties as storage modulus, loss modulus, and tan $\delta$. Also FT/IR tests were conducted to investigate changes in chemical structure with exposure. The results revealed that fiber-dominated mechanical properties were not affected much by exposure time, but matrix-dominated mechanical properties decreased with increasing exposure time. Storage modulus was not very sensitive to exposure time, but glass transition temperature was affected, slightly decreasing with increasing exposure time. Although the peak intensity of FT/IR curves was affected slightly by exposure time, the peak shape and peak location of FT/IR curves were not noticeably changed. Carbon/epoxy composites used for this study were relatively stable to the salt water environment.