This study aimed to evaluate the marginal microleakage of Class V cavities of All-bond 2 (Wet - bonding system), Gluma (Adhesion of resin to exposed collagen fibers), and Scotchbond Multi-purpose(Mild Etching System). Hundred extracted human teeth divided into a control and three experimental groups consisting of eight teeth. The experimental group was further subdivided into All- bond2, Gluma and Scotchbond MP groups, Vitrebond served as the control. The positive control group consisted of specimens filled with resin and with no etching, primer and bonding procesure. Polished specimens underwent temperature changed from $5^{\circ}C$ to $55^{\circ}C$ a thousand times. After thermocycling, speciemens were placed in 2 % methylene blue dye solution for 24 hours in an incubator set at $37^{\circ}C$. The teeth were sectioned buccolingually and the degree of dye penetration was observed with a stereomicroscoped(*20). The following results were obtained. 1. Both the control and the experimental group showed a lower degree of dye penetration on enamel than on dentin margins(p<0.05) 2. Gluma exhibited a statistically significant lower degree of dye penetration than All-bond 2 on enamel margins(p<0.05) Scotchbond MP also exhibited a lower degree of dye penetration than All-bone 2 but was no statistically significant. Gluma and Scotchbond MP exhibited a similar degree of dye penetration. 3. The degree of dye penetration of All-bond 2, Gluma and Scotch bond MP showed no statistically singnificance on enamel margins but was significantly lower than in the control using Vitrebond. 4. All-bond 2 exhibited a statistically significant lower degree of dye penetration than Gluma on dentin margins. All- bond 2 and Scotchbond MP showed a similar degree of dye penetration. 5. The degree of dye penetration of All-bond 2, Gluma and Scotchbond MP showed no statistically significance on dentin margins. There was neither a statistical significance with the control.
The purpose of this study was to investigate the effect of stannous fluoride on the dentin bonding with three kinds of commercially available dentin bonding systems containing different adhesive monomers. Dentin specimens with exposed labial dentin prepared from freshly extracted bovine mandibular anterior teeth were divided into experimental and control groups. The specimens of experimental groups were bonded with dentin bonding systems and composite resins including All bond 2 ㅡ& Bisfil, Scotchbond Multi-Purpose & Z100, and Denthesive II Charisma after 2 % stannous& fluorided application for S minutes and washing for 1 minute. The specimens of control groups were bonded with the same dentin bonding systems and composite resins as used in the experimental groups. After bonded specimens were stored in $37^{\circ}C$ distilled water for 24 hours, the tensile bond strength and cohesive failure rate were measured, and then the pretreated dentin surfaces and the fractured dentin surfaces were examined under scanning electron microscope. The results were as follows : Mean bond strength of stannous fluoride applied groups of All bond 2, Scotchbond MP, and Denthesive II were 2.5MPa, 1.1MPa, and 1.1MPa respectively, and those of control groups were 7.5MPa, 8.1MPa, and 4.6MPa. Bond strength values of stannous fluoride applied groups were significantly lower than those of the control groups(p<0.05). SEM findings of dentin surfaces after stannous fluoride application demonstrated an appearance of partially remained smear layer and smear plugs inspite of pretreatment with 10 % phosphoric aicd or maleic acid solution, and an appearance of smear layer covered surface under Denthesive II priming. But those of control groups commonly showed clean dentin surfaces without smear layer and smear plugs. On SEM observation of the fractured dentin-resin interface, while most of the specimens of stannous fluoride applied groups showed adhesive failure mode, those of All bond 2 and Scotchbond MP control groups showed mainly adhesive-cohesive mixed failure mode, and mainly adhesive failure mode in Denthesive II control group.
Incidence of using esthetic composite resin in the posterior area is increasing but there were lots of inconsistent reports about their microleakage and marginal adaptation. The purpose of this study was to evaluate the differences of microleakage and marginal adaptation according to restorative techniques. 30 cavities with enamel gingival margin were prepared and restored with 3 types of composite resin [Z-100($Scotchbond^{TM}$ MP), AELITEFIL ($Onestep^{TM}$), Her culite XRV(Fuji BOND LC)] in direct technique and another 30 cavities were restored with preformed CR inlays and 3 different modern resin and resin-modified GI cements (Superbond C&B, Choice, Fuji Duet). Samples were chemically stressed in 75% ethanol for 24 hours and were thermocycled (5-$55^{\circ}C$(500 times. The degree of microleakage through proximal and gingival margins was examined by 1 % MB dye and the degree of marginal adaptation by examining the margins via SEM. The following results were obtained ; 1. In direct groups, Herculite XRV [Fuji BOND LC, 35.13 (15.50) %] group showed statistically different, less microleakage than Z-100 [$Scotchbond^{TM}$ MP, 72.91 (16.91 %] group and AELITEFIL [One-step, 93.73 (13.66) %] group (p<0.05). 2. In indirect groups, the degree of microleakage in Mean(S.D.) were: Super bond C & B [39.00 (24.35) %], Choice [57.19 (33.80) %], Fuji Duet [58.22 (40.36) %]. But there was no significant difference. 3. There was no significant difference between resin cement and resin-modified GI cement. 4. There were gaps at the interface with the tooth structure, but no gap was seen at the interface with restoration in all specimens. 5. In direct groups, Herculite XRV(Fuji BOND LC) group made little gap compared with other groups, but 40-$50{\mu}m$ thickness of bonding agent, Fuji BOND LC, looked like a cement used in indirect technique. 6. All indirect groups showed a variety of cement thickness, from less than $20{\mu}m$ to over $100{\mu}m$ and that dimension of buccal/lingual margin was less than that of gingival margin.
본 연구는 total etching (Scotchbond Multi-Purpose; MP) 및 self-etching (Clearfil SE Bond; SE 과 Prompt L-pop LP) 상아질 접착제의 nanoleakage 양상을 관찰하고 열순환 후의 nanoleakage 양상의 변화를 분석하고자 하였다. 30개의 발거된 치아의 교합면 및 협, 설측 법랑질을 제거하였다. 열 순환 시행 여부에 따라 두 군으로 나누어 실험하였으며 각각의 상아질 접착제 도포 후 Z-250으로 교합면을 수복하였다. Silver nitrate용액 및 현상액에 침적 후치아의 협설 방향으로 평행하게 절단하여 SEM으로 관찰하였다. 서로 다른 양상의 nanoleakage가 관찰되었다. MP의 경우는 resin tag 주위로 뚜렷한 은의 침착을 관찰 할 수 있었으며 혼합층 전체 두께에 띠 및 점상으로 흩어져 침착된 은을 관찰 할 수 있었다. SE의 경우는 혼합층의 하층을 따라 은으로 침착된 선을 관찰 할 수 있었으며 혼합층과 adhesive 경계를 따라 무정형의 은 침착물 들을 관찰할 수 있었다. LP의 경우는 혼합층의 하부 및 혼합층 내에 띠 모양으로 은의 침착을 관찰 할 수 있었으며 혼합층의 하부에서는 관찰되지 않고 혼합층의 내부에서만 관찰되는 경우도 있었다. 열순환을 시행한 군에서는 전반적 nanoleakage 양상은 열 순환을 시행하지 않은 군과 유사하였으나 은 침착의 증가를 관찰 할 수 있었다.
Objectives: Rapid polymerization of overlying composite resin causes high polymerization shrinkage stress at the adhesive layer. In order to alleviate the shrinkage stress, increasing the light intensity over the first 5 seconds was suggested as an exponential curing mode by an LED light curing unit (Elipar FreeLight2, 3M ESPE). In this study, the effectiveness of the exponential curing mode on reducing stress was evaluated with measuring microtensile bond strength of three adhesives after the overlying composite resin was polymerized with either continuous or exponential curing mode. Methods: Scotchbond Multipurpose Plus (MP, 3M ESPE), Single Bond 2 (SB, 3M ESPE), and Adper Prompt (AP, 3M ESPE) were applied onto the flat occlusal dentin of extracted human molar. The overlying hybrid composite (Denfil, Vericom, Korea) was cured under one of two exposing modes of the curing unit. At 48h from bonding, microtensile bond strength was measured at a crosshead speed of 1.0 mm/min. The fractured surfaces were observed under FE-SEM. Results: There was no statistically significant difference in the microtensile bond strengths of each adhesive between curing methods (Two-way ANOVA, p > 0.05). The microtensile bond strengths of MP and SB were significantly higher than that of AP (p < 0.05). Mixed failures were observed in most of the fractured surfaces, and differences in the failure mode were not observed among groups. Conclusion: The exponential curing method had no beneficial effect on the microtensile dentin bond strengths of three adhesives compared to continuous curing method.
The purpose of this study was: (1) to compare nanoleakage patterns of a conventional 3-step etch and rinse adhesive system and two experimental hydrophobic adhesive systems and (2) to investigate the change of the nanoleakage patterns after load cycling. Two kinds of hydrophobic experimental adhesives, ethanol containing adhesive (EA) and methanol containing adhesive (MA), were prepared. Thirty extracted human molars were embedded in resin blocks and occlusal thirds of the crowns were removed. The polished dentin surfaces were etched with a 35 % phosphoric acid etching gel and rinsed with water. Scotchbond Multi-Purpose (MP), EA and MA were used for bonding procedure. Z-250 composite resin was built-up on the adhesive-treated surfaces. Five teeth of each dentin adhesive group were subjected to mechanical load cycling. The teeth were sectioned into 2 mm thick slabs and then stained with 50 % ammoniacal silver nitrate. Ten specimens for each group were examined under scanning electron microscope in backscattering electron mode. All photographs were analyzed using image analysis software. Three regions of each specimen were used for evaluation of the silver uptake within the hybrid layer. The area of silver deposition was calculated and expressed in gray value. Data were statistically analyzed by two-way ANOVA and post-hoc testing of multiple comparisons was done with the Scheffe's test. Silver particles were observed in all the groups. However, silver particles were more sparsely distributed in the EA group and the MA group than in the MP group (p < .0001). There were no changes in nanoleakage patterns after load cycling.
Composite resin and glass-ionomer cement can be used for the purpose of repair of defective amalgam restoration. The purpose of this study was to evaluate of shear bond strength of esthetic restorative materials to dental amalgam. The materials used in this study were Photo Clearfil Bright(light curing composite resin), Clearfil F II(chemical curing composite resin), Fuji II LC(light curing glass-ionomer cement), Fuji II (chemical curing glass-ionomer cement), All-Bond 2(intermediary), and Scotchbond Multi-Purpose (intermediary). A total of 120 acrylic cylinders with amalgam were divided into 8 groups After amalgam condensation, all specimens were stored for 48 hours in water at $37^{\circ}C$ and tested with Instron universal testing machine between amalgam and composite resins and glass-ionomer cements. The data were analyzes statiscally by ANOVA and Duncan test. The following results obtained ; 1. The shear bond strength of bonded composite resin to amalgam was higher than bonded glass-ionomer cement(P<.001). 2. The group 4 had highest shear bond strength with 15.45kgf/$cm^2$ and the group 5 had lowest shear bond strenght with 3.26kgf/$cm^2$(P<.001). 3. In the group 3, 4, 5, 6, the group 3, 4 with All-Bond 2 had higher shear bond strength than the group 5, 6 with Scotch bond MP both in light-curing and in chemical curing. 4. Both in composite resin and glass-ionomer cement, chemical curing materials had higher shear bond stength than light curing materials(P<.001).
The purpose of this study was to evlauate the microleakage of 3 dentin bonding agents using different dentin pretreatment method under simulated physilogic pressure in cementing the porcelain laminate veneer. Noncarious 60 human maxillary molars were selected and randomly assigned to 4 groups of 15 each. The group with the margin placed on the enamel was classified as the control and the groups with the margin placed on root surface were subdivided into 3 groups according to the dentin bonding agents used. The group using All Bond 2 was classified as experimental group 1, the group using Scotchbond MP was classified as experimental group 2, and the group using Gluma was classified as experimental group 3. Roots were removed at 3mm below the cementoenamel junction, and reductions of the teeth for the porcelain laminate veneer were done on the mesial 1/2 of the buccal surface of each teeth. The pulp was extirpated and the pulp chamber was cleaned with 37% phosphoric acid for the patency of dentinal tubule. Under simulated physiologic pressure, porcelain laminate veneers were cemented to the teeth using each dentin bonding agent and luting cement. After cementation, all samples were stored at 36t in water for 24 hours and thermocycled for 1500 cycles, then immersed in 0.5% basic fuchsin solution and the teeth were sectioned longitudinally by using diamond saw and the extent of microleakage was measured. The following results were obtained, 1. Microleakage was observed in a few samples of control group but all the samples of experimental groups. 2. The control group showed the less extent of microleakage than the experimental groups. In experimental groups the experimental group 1 & the experimental group 2 showed similiar extent of microleakage and the experimental group 3 showed the greater extent of microleakage than other groups. Conclusively, practicing the porcelain laminate veneers in the clinic, although the margin of the porcelain laminate veneer should be placed on enamel, in the case that it is inevitable to place the margin of the porcelain laminate veneer on the root surface, it is recommened to use dentin bonding agents which use no dentin pretreatment or a dentin pretreatment which can leave the smear plugs.
본 웹사이트에 게시된 이메일 주소가 전자우편 수집 프로그램이나
그 밖의 기술적 장치를 이용하여 무단으로 수집되는 것을 거부하며,
이를 위반시 정보통신망법에 의해 형사 처벌됨을 유념하시기 바랍니다.
[게시일 2004년 10월 1일]
이용약관
제 1 장 총칙
제 1 조 (목적)
이 이용약관은 KoreaScience 홈페이지(이하 “당 사이트”)에서 제공하는 인터넷 서비스(이하 '서비스')의 가입조건 및 이용에 관한 제반 사항과 기타 필요한 사항을 구체적으로 규정함을 목적으로 합니다.
제 2 조 (용어의 정의)
① "이용자"라 함은 당 사이트에 접속하여 이 약관에 따라 당 사이트가 제공하는 서비스를 받는 회원 및 비회원을
말합니다.
② "회원"이라 함은 서비스를 이용하기 위하여 당 사이트에 개인정보를 제공하여 아이디(ID)와 비밀번호를 부여
받은 자를 말합니다.
③ "회원 아이디(ID)"라 함은 회원의 식별 및 서비스 이용을 위하여 자신이 선정한 문자 및 숫자의 조합을
말합니다.
④ "비밀번호(패스워드)"라 함은 회원이 자신의 비밀보호를 위하여 선정한 문자 및 숫자의 조합을 말합니다.
제 3 조 (이용약관의 효력 및 변경)
① 이 약관은 당 사이트에 게시하거나 기타의 방법으로 회원에게 공지함으로써 효력이 발생합니다.
② 당 사이트는 이 약관을 개정할 경우에 적용일자 및 개정사유를 명시하여 현행 약관과 함께 당 사이트의
초기화면에 그 적용일자 7일 이전부터 적용일자 전일까지 공지합니다. 다만, 회원에게 불리하게 약관내용을
변경하는 경우에는 최소한 30일 이상의 사전 유예기간을 두고 공지합니다. 이 경우 당 사이트는 개정 전
내용과 개정 후 내용을 명확하게 비교하여 이용자가 알기 쉽도록 표시합니다.
제 4 조(약관 외 준칙)
① 이 약관은 당 사이트가 제공하는 서비스에 관한 이용안내와 함께 적용됩니다.
② 이 약관에 명시되지 아니한 사항은 관계법령의 규정이 적용됩니다.
제 2 장 이용계약의 체결
제 5 조 (이용계약의 성립 등)
① 이용계약은 이용고객이 당 사이트가 정한 약관에 「동의합니다」를 선택하고, 당 사이트가 정한
온라인신청양식을 작성하여 서비스 이용을 신청한 후, 당 사이트가 이를 승낙함으로써 성립합니다.
② 제1항의 승낙은 당 사이트가 제공하는 과학기술정보검색, 맞춤정보, 서지정보 등 다른 서비스의 이용승낙을
포함합니다.
제 6 조 (회원가입)
서비스를 이용하고자 하는 고객은 당 사이트에서 정한 회원가입양식에 개인정보를 기재하여 가입을 하여야 합니다.
제 7 조 (개인정보의 보호 및 사용)
당 사이트는 관계법령이 정하는 바에 따라 회원 등록정보를 포함한 회원의 개인정보를 보호하기 위해 노력합니다. 회원 개인정보의 보호 및 사용에 대해서는 관련법령 및 당 사이트의 개인정보 보호정책이 적용됩니다.
제 8 조 (이용 신청의 승낙과 제한)
① 당 사이트는 제6조의 규정에 의한 이용신청고객에 대하여 서비스 이용을 승낙합니다.
② 당 사이트는 아래사항에 해당하는 경우에 대해서 승낙하지 아니 합니다.
- 이용계약 신청서의 내용을 허위로 기재한 경우
- 기타 규정한 제반사항을 위반하며 신청하는 경우
제 9 조 (회원 ID 부여 및 변경 등)
① 당 사이트는 이용고객에 대하여 약관에 정하는 바에 따라 자신이 선정한 회원 ID를 부여합니다.
② 회원 ID는 원칙적으로 변경이 불가하며 부득이한 사유로 인하여 변경 하고자 하는 경우에는 해당 ID를
해지하고 재가입해야 합니다.
③ 기타 회원 개인정보 관리 및 변경 등에 관한 사항은 서비스별 안내에 정하는 바에 의합니다.
제 3 장 계약 당사자의 의무
제 10 조 (KISTI의 의무)
① 당 사이트는 이용고객이 희망한 서비스 제공 개시일에 특별한 사정이 없는 한 서비스를 이용할 수 있도록
하여야 합니다.
② 당 사이트는 개인정보 보호를 위해 보안시스템을 구축하며 개인정보 보호정책을 공시하고 준수합니다.
③ 당 사이트는 회원으로부터 제기되는 의견이나 불만이 정당하다고 객관적으로 인정될 경우에는 적절한 절차를
거쳐 즉시 처리하여야 합니다. 다만, 즉시 처리가 곤란한 경우는 회원에게 그 사유와 처리일정을 통보하여야
합니다.
제 11 조 (회원의 의무)
① 이용자는 회원가입 신청 또는 회원정보 변경 시 실명으로 모든 사항을 사실에 근거하여 작성하여야 하며,
허위 또는 타인의 정보를 등록할 경우 일체의 권리를 주장할 수 없습니다.
② 당 사이트가 관계법령 및 개인정보 보호정책에 의거하여 그 책임을 지는 경우를 제외하고 회원에게 부여된
ID의 비밀번호 관리소홀, 부정사용에 의하여 발생하는 모든 결과에 대한 책임은 회원에게 있습니다.
③ 회원은 당 사이트 및 제 3자의 지적 재산권을 침해해서는 안 됩니다.
제 4 장 서비스의 이용
제 12 조 (서비스 이용 시간)
① 서비스 이용은 당 사이트의 업무상 또는 기술상 특별한 지장이 없는 한 연중무휴, 1일 24시간 운영을
원칙으로 합니다. 단, 당 사이트는 시스템 정기점검, 증설 및 교체를 위해 당 사이트가 정한 날이나 시간에
서비스를 일시 중단할 수 있으며, 예정되어 있는 작업으로 인한 서비스 일시중단은 당 사이트 홈페이지를
통해 사전에 공지합니다.
② 당 사이트는 서비스를 특정범위로 분할하여 각 범위별로 이용가능시간을 별도로 지정할 수 있습니다. 다만
이 경우 그 내용을 공지합니다.
제 13 조 (홈페이지 저작권)
① NDSL에서 제공하는 모든 저작물의 저작권은 원저작자에게 있으며, KISTI는 복제/배포/전송권을 확보하고
있습니다.
② NDSL에서 제공하는 콘텐츠를 상업적 및 기타 영리목적으로 복제/배포/전송할 경우 사전에 KISTI의 허락을
받아야 합니다.
③ NDSL에서 제공하는 콘텐츠를 보도, 비평, 교육, 연구 등을 위하여 정당한 범위 안에서 공정한 관행에
합치되게 인용할 수 있습니다.
④ NDSL에서 제공하는 콘텐츠를 무단 복제, 전송, 배포 기타 저작권법에 위반되는 방법으로 이용할 경우
저작권법 제136조에 따라 5년 이하의 징역 또는 5천만 원 이하의 벌금에 처해질 수 있습니다.
제 14 조 (유료서비스)
① 당 사이트 및 협력기관이 정한 유료서비스(원문복사 등)는 별도로 정해진 바에 따르며, 변경사항은 시행 전에
당 사이트 홈페이지를 통하여 회원에게 공지합니다.
② 유료서비스를 이용하려는 회원은 정해진 요금체계에 따라 요금을 납부해야 합니다.
제 5 장 계약 해지 및 이용 제한
제 15 조 (계약 해지)
회원이 이용계약을 해지하고자 하는 때에는 [가입해지] 메뉴를 이용해 직접 해지해야 합니다.
제 16 조 (서비스 이용제한)
① 당 사이트는 회원이 서비스 이용내용에 있어서 본 약관 제 11조 내용을 위반하거나, 다음 각 호에 해당하는
경우 서비스 이용을 제한할 수 있습니다.
- 2년 이상 서비스를 이용한 적이 없는 경우
- 기타 정상적인 서비스 운영에 방해가 될 경우
② 상기 이용제한 규정에 따라 서비스를 이용하는 회원에게 서비스 이용에 대하여 별도 공지 없이 서비스 이용의
일시정지, 이용계약 해지 할 수 있습니다.
제 17 조 (전자우편주소 수집 금지)
회원은 전자우편주소 추출기 등을 이용하여 전자우편주소를 수집 또는 제3자에게 제공할 수 없습니다.
제 6 장 손해배상 및 기타사항
제 18 조 (손해배상)
당 사이트는 무료로 제공되는 서비스와 관련하여 회원에게 어떠한 손해가 발생하더라도 당 사이트가 고의 또는 과실로 인한 손해발생을 제외하고는 이에 대하여 책임을 부담하지 아니합니다.
제 19 조 (관할 법원)
서비스 이용으로 발생한 분쟁에 대해 소송이 제기되는 경우 민사 소송법상의 관할 법원에 제기합니다.
[부 칙]
1. (시행일) 이 약관은 2016년 9월 5일부터 적용되며, 종전 약관은 본 약관으로 대체되며, 개정된 약관의 적용일 이전 가입자도 개정된 약관의 적용을 받습니다.