• 한국산학기술학회논문지
• /
• 제5권2호
• /
• pp.98-102
• /
• 2004

단일이온교환 프로세스를 도입하여 soda-lime-silicate 유리에 있어서의 이온교환 거동 및 물성변화를 관찰하였다. 온도 및 시간 변화에 따라 K/sup +/ 이온의 침투깊이, 이온교환량은 증가하였으며, 이에 비례하여 밀도, 굴절률도 증가하는 경향을 보였다 이온교환 과정에서 생성된 비가교 산소로 인하여 400nm에서 흡수 현상이 관찰되었으며, 열팽창계수는 구조의 치밀화와 이력현상에 영향을 받았다.

• 한국세라믹학회지
• /
• 제52권2호
• /
• pp.133-136
• /
• 2015

The outward diffusion of $Na^+$ ions in iron-bearing soda lime silicate glass via oxidation heat treatment before the ion exchange process is artificially induced in order to increase the amount of ions exchanged during the ion exchange process. The effect of the addition process is analyzed through measuring the bending strength, the weight change, and the inter-diffusion coefficient after the ion exchange process. The glass strength is increased when the outward diffusion of $Na^+$ ions via oxidation heat treatment before the ion exchange process is added. For the glass subjected to the additional process, the weight change and diffusion depth increase compared with the glass not subjected to the process. The interdiffusion coefficient is also slightly increased as a result of the additional process.

• 한국세라믹학회지
• /
• 제52권2호
• /
• pp.137-139
• /
• 2015

In this study, we examined the influence of molten $KNO_3$ flow on mechanical properties and their deviation when a chemical toughening process was applied to soda lime silicate glass ($Na_2O-CaO-SiO_2$). $KNO_3$ melt flow was controlled using three methods: (1) glass tray rotation, (2) impeller stirring, and (3) natural convection. DOL and hardness were found to be enhanced by tray rotation because this rotation was able to maintain the concentration around the glass surface, in contrast to other methods. However, there did not appear to be a statistically significant difference in the 3-point bending strength for the three flow conditions due to the ground edge condition.

• 한국세라믹학회지
• /
• 제56권5호
• /
• pp.483-488
• /
• 2019

We studied whether chemical strengthening can heal the flaws on soda-lime silicate glass. Artificial surface cracks were introduced on the glass by sharp indentation with various loads of 0.1 to 10 N. Then, the glasses with flaws were treated by ion-exchanging in KNO₃ melt. The change in the dimension of the crack on glass was measured by a digital microscope and a scanning electron microscope. The chemical strengthening treatment enhances the strength of the glass with flaws. It is thought that the melted KNO₃ not only forms the depth of the compressed layer of 7.5 ㎛, but also heals the cracks by infiltrating them and expanding the glass on both sides of the cracks. The critical length (2c) of the cracks on soda-lime glass that can be healed by chemical strengthening is 50 ㎛ or less.

• 한국정보디스플레이학회:학술대회논문집
• /
• 한국정보디스플레이학회 2007년도 7th International Meeting on Information Display 제7권1호
• /
• pp.367-370
• /
• 2007

An EEFL with the sodium free alumino-silicate glass of high K and low $tan{\delta}$, has been investigated. As compared with borosilicate and the soda-lime EEFLs, the luminous efficiency as well as the pinhole stability of new EEFLs improves remarkably without blackening of $NaHg_2$.

• 한국세라믹학회지
• /
• 제52권2호
• /
• pp.123-127
• /
• 2015

Soda-lime silicate (SLS) glass was strengthened by ion exchange for application of thin and lightweight bulletproof windows. The optimal conditions for ion exchanged SLS glass (thickness of 3 and 10 mm) at $480^{\circ}C$ were 10 and 17 min, respectively. The Vickers hardness values of the strengthened SLS glass samples with thicknesses of 3 and 10 mm were $5.9{\pm}0.22$ and $6.7{\pm}0.17GPa$, respectively, which values were about 22% higher than those of parent SLS glass. By laminating a multilayer defense film and polycarbonate sheet with ion exchanged SLS glass, we were able to make a thin and lightweight bulletproof window (24.25 mm, 4.57 kg, $50.06kg/m^2$, $V_{50}$ 901.8 m/s). As a result, the thickness of the bulletproof window was decreased by about 39% from 40 to 24.25 mm. The light transmittance in the visible range satisfied the standard (over 76%) for bulletproof windows.

• 한국세라믹학회지
• /
• 제39권7호
• /
• pp.675-679
• /
• 2002

강화유리를 제조하기 위해서, 디스플레이 기판으로 사용되는 soda-lime-silicate 유리를 대상으로 단일이온교환 특성에 대하여 3점곡강도와 잔류응력을 조사하였다. 단일이온교환을 47$0^{\circ}C$에서 1시간 처리 후, 45$0^{\circ}C$에서 24시간 행하였을 때, 62.5$\times$10$_{6}$ kg/$m^2$의 최대 강도 값을 나타내었다. 또한, 곡강도 측정 후 얻어진 시편의 파단면에 존재하는 잔류응력층을 파괴분석을 통하여 관찰한 결과, 이 잔류응력층이 외부하중에 대한 탄성 변형에너지를 흡수하여 유연성을 증가시킴을 알 수 있었다 또한, 탄성변형에너지 흡수는 만곡변화, 균열가지수 및 취성특성 분석에서도 관찰되었다.

• 공업화학
• /
• 제24권4호
• /
• pp.382-390
• /
• 2013

소다석회 조성의 폐 병유리를 대상으로 효율적인 재활용방안을 찾기 위해서 발포화에 적절한 조성의 조절을 통해 직접 보온단열재 발포유리블럭을 제조할 수 있는 공정을 조사하였다. 폐 병유리의 직접 발포화를 위해 첨가되는 성분 및 조성은, 폐 유리분말 100중량부에 대하여 $SiO_2$ 10중량부, $Na_2SO_4$ 0.5중량부, $B_2O_3$ 3.0중량부, 그리고 발포제로서 카본 블랙류 탄소재 0.3중량부이다. 발포공정은 턴넬키른에서 진행하며, 발포소성 조건은 폐 유리분말의 입도는 -325 mesh, 발포소성온도는 $830{\sim}850^{\circ}C$, 발포시간은 30~35 min이 바람직하다. 상기 조건하에 제조된 발포체는 밀도가 $0.17{\sim}0.21g/cm^3$, 열전도도 $0.06{\pm}0.005kcal/h{\cdot}m{\cdot}^{\circ}C$, 수분 흡수율 1.1~1.5%, 압축강도는 $20{\sim}30kgf/mm^2$의 물성을 나타내었다.

• 한국군사과학기술학회지
• /
• 제13권1호
• /
• pp.114-119
• /
• 2010

There are a number of studies on chemically strengthened glass. Most of them are strengthened in molten salt bath below transformation range of glass. This research is distinguished from the aforementioned studies in that single $KNO_3$ powder was used by employing screen printing technique. In this study soda-lime-silicate(SLS) glasses for bulletproof glass application with various thicknesses were used. The maximum value of the bending strength is 791MPa heat treated at $480^{\circ}C$, which is about 4.3 times higher than the parent glass, which is the highest strength of all soda-lime glasses. In this study, it is also observed that Vickers hardness increased to $657H_v$, which is about 15% higher than the parent glass($568.7H_v$) and fracture toughness was not changed. Depth profiles measured by electron probe micro analyzer(EPMA) showed a correlation between the migrations of $K^+$ ions with bending strength of ion exchanged glasses.

• 오토저널
• /
• 제14권6호
• /
• pp.91-98
• /
• 1992

In the research on the fracture time of soda lime silicate glass under thermal shock, it is shown that the theoretical and experimental fracture times are in good agreement, the suggested method to measure critical stress intensity factor for small three-point bending specimen is useful and the edge temperature before thermal shock on cracked side vs. crack length and fracture time are inversely proportional.