• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.27 no.3
• /
• pp.363-371
• /
• 2003

This study is mainly concerned with phenomenon of cavitation-erosion on the several materials and corrosive liquids which were applied with vibrator(suggested by ASTM G 32, 20KHz, 50$mu extrm{m}$). The maximum erosion rate by cavitation erosion in both of distilled water and sea water appeared to be proportioned to their hardness and tensile strength. Cavitation weight loss and rate of cast iron in sea water condition were greater(approximately 3 times) than that in distilled water condition, however in case of stainless steel and brass the cavitation weight loss of composite materials were not so different in both of their conditions. Cavitation weight loss of composite materials were shown as below on this test, Duratough DL : Weight loss in sea-water condition were greater (approximately 2.3 times) than it's distilled water condition. The main tendency of cavitation erosion for metals appeared that small damaged holes causing by cavitation erosion was observed with radial pattern. On the other hand, the tendency for composites appeared that small damaged holes were observed randomly.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 1999.11a
• /
• pp.227-233
• /
• 1999

This study is mainly concerned with phenomenon of cavitation-erosion on the several materials and corrosive liquids which were applied with vibrator (suggested by ASTM G-32, 20KHZ, 24{$mu}m$).The main results obtained are summarized as follows ; (1) The maximum erosion rate by cavitation erosion in both of fresh-water and sea-water appeared to be proportioned to their hardness and tensile strength. (2) Cavitation weight loss and rate of cast iron in sea-water condition were greater (approximately 3 times) than that in distilled-water condition, however in case of stainless and brass the cavitation weight loss and their rates were not so different in both of their conditions. (3) Cavitation weight loss of composite materials were shown as below on this test, DuraTough DL : Weight loss in sea-water condition were greater (approximately 2.3 times) than it's fresh-water condition. (4) As the result of observation with digital camea of specimens, the main tendency of cavitation erosion for metals, was that small damaged holes causing by cavitation e개sion was appeared with radial pattern, and composites materials was that small damaged holes were appeared randomly.