• 한국윤활학회:학술대회논문집
• /
• 한국윤활학회 2001년도 제34회 추계학술대회 개최
• /
• pp.172-178
• /
• 2001

Using dislocation pileup theory, the near surface crack initiation life was calculated. The crack initiation life calculted in the previous study is not a real life strictly and just for the cracking in substrate. In this study, two life equations which can be applied for each near-surface and substrate were used for a comparative study. The downward tendency of life at near surface and substrate was similar and the crack initiation life at near-surface was much shorter than the life in substrate. The improvement of the crack initiation life equations which were proposed by W. Cheng was discussed.

• 한국안전학회지
• /
• 제18권4호
• /
• pp.39-43
• /
• 2003

An experimental study was conducted to develop and understanding of fracture behavior of ceramic thermal barrier coating when subjected to a thermal shock loading. The thermal loading was applied using a 1.5kW $CO_2$ laser. In the experiments, beam-shaped specimens were subjected to a high heat flux for 4sec and cooling of 7sec in air. The interface crack length was increased as the crack density, the surface pre-crack legth and the coating thickness were increased. The center surface crack length was increased as the maximum surface temperature got higher and the surface pre-crack length for shorter.

• 한국정밀공학회지
• /
• 제27권3호
• /
• pp.80-88
• /
• 2010

A simple computational model for modeling of subsurface crack growth under cyclic contact loading is presented. In this model, it is assumed that the initial fatigue crack will initiate in the region of the maximum equivalent stress at certain depth under the contacting surface. The position and magnitude of the maximum equivalent stress are determined by using the equivalent contact model, which is based on the Hertzian contact conditions with frictional forces. The virtual crack extension method is used for simulation of the fatigue crack growth from the initial crack up to the formation of the surface pit due to contact fatigue. The relationships between the stress intensity factor and crack length are then determined for various combinations of equivalent contact radii and loadings.

• Journal of Welding and Joining
• /
• 제13권2호
• /
• pp.42-52
• /
• 1995

In the evaluation of aging degradation on the structural materials based on the fracture mechanics, the detection and size prediction of defect are very important. Aiming at nondestructive detection and size prediction ol defect with high accuracy and resolution, therefore, an lnduced Current Focusing Potential Drop(ICFPD) technique has been developed. The principle of this technique is to induce a focusing current at an exploratory region by an induction wire flowing an alternating current(AC) that is a constant ampere and frequency. Defects are assessed with the potential drops that are measured the induced current on the surface of metallic material by the potential pick-up pins. In this study, the lCFPD technique was applied for evaluating the location and size of the surface crack and blind crack made in plate specimens, and also for detecting the defects existing in valve, a field component, that were developed by SCC etc. during the service. The results of this present study show that surface crack and blind crack are able to defect with potential drop. these cracks are distinguished with the distribution of potential drop, and the crack depths can be estimated with each normalized potential drop that are parameters estimating the depth of each type crack. In the field component, the defects estimated by experiment result correspond with those in the cutting face of the measuring point within a higher sensitivity.

• 한국해양공학회지
• /
• 제7권2호
• /
• pp.68-78
• /
• 1993

Fatigue crack shape variation by a residual stress during crack growth and life predition are studied. An analytical method is presented to predict the influence of a residual stress due to heattreatment on crack shape variations. Computer simulation results using this me thod are graphically shown that crack growth rate to surface direction are decreased due to compressive residual stress exisiting in surface area. These results are commpared with experimental results. The fatigue life is also predicted by computer simulation of crack aspect ratio variation which is based on the surface crack length increment per unit cycle calculated from a-N diagram. Predited life is about 12 percent lower than experimental life.

• 한국정밀공학회:학술대회논문집
• /
• 한국정밀공학회 2001년도 춘계학술대회 논문집
• /
• pp.1052-1055
• /
• 2001

In micro-drilling of brittle materials including glass, cracks occur at the exit surface. In drilling glass, the main type of crack is cone crack. Cone crack is generated by thrust force acting at the bottom surface of the workpiece. Cone crack size could be reduced by changing cutting conditions, but cone crack still existed. Two methods were proposed to prevent crack formation and perfect hole shapes were obtained. One method is attaching two glass plates with water and the other method is constraining two glass plates. The proposed methods eliminated tensile stress acting on the exit surface of glass and prevented crack propagation.

• 한국윤활학회:학술대회논문집
• /
• 한국윤활학회 2000년도 제32회 추계학술대회 정기총회
• /
• pp.72-79
• /
• 2000

In case of rough contact fatigue, the accurate calculation of surface tractions is essential to the prediction of crack initiation life. Accurate Surface tractions influencing shear stress amplitude can be obtained by contact analysis based on tile morphology of contact surfaces. In this study, to simulate rough contact under sliding condition, gaussian rough surface generated numerically in the previous study was used and to calculate crack initiation life in the substrate, dislocation pileup theory was used.

• 한국음향학회지
• /
• 제10권3호
• /
• pp.13-18
• /
• 1991

본 연구에서는 취약한 고체의 표면에 존재하는 crack에 탄성표면파를 입사 시켰을 때 발생하는 반사계수를 측정하여 파괴응력을 해석하는 방법을 연구 분석하였다. Crack이 존재하는 취약한 고체에서의 파괴응력은 임계응력확대계수와 정규화된 최대응력확대계수의 함수로써 나타나며, 이 때 정규화된 최대응력확대계수는 탄성표면파의 반사계수를 측정하여 구할 수 있었다. 실험을 위하여 Pyrex glass원판 중앙에 깊이가 0.5mm~0.9mm인 crack을 제작하였고, SAW wedge transducer를 피치캐치(pitch-catch) 모드로 구성하여 반사계수를 측정하고 파괴응력값을 산출하였으며 UTM(Universal Testing Machine)으로 측정한 값과 비교 분석하였다.

• 대한기계학회논문집A
• /
• 제20권10호
• /
• pp.3126-3134
• /
• 1996

In this paper, to examine the propagation of inclined surface crack due to frictional heating, analytic model is considered as the semi-infinite elastic body subjected to the thermo-mechanical loading of an asperity moving with a high speed. Considering the moving of frictional heat source and convection on a semi-infinite surface having inclined crack, theoretical analysis was carried out to estimate the propagation characteristics of thermo-mechanical crack. Numerical results showed that stress intensity factor $K_\prod/P_0\sqrt{c}$ is increasing with increasing velocity and frictional coefficient, inclined degree, decreasing crack length and the maximum value of it is positioned at the trailing edge. So it is shown that the propagation probability of surface crack is high at the trailing edge of contact area as increasing velocity and frictional coefficient, inclined degree, as decreasing crack length.

• 대한기계학회논문집
• /
• 제12권4호
• /
• pp.781-789
• /
• 1988

본 연구에서는 용접성이 좋고 강도도 적당하며 부식에 대한 저항성이 좋아 해 양구조물 및 용접구조용재로서 널리 사용되고 있는 5083-H113 Al 합금을 준비하고 이 재료의 균열형태에 따른 피로균열진전거동을 밝히기 위하여 관통균열과 포면균열의 진 전거동에 미치는 응력비의 영향을 균열닫힘과 함께 검토하였다.