• 열처리공학회지
• /
• 제36권1호
• /
• pp.33-39
• /
• 2023

In this study, the effect of mixing condition of raw material powders possessing various particle size and particle size distribution on thermite reaction efficiency was investigated. When fine raw powders are used, rather the reaction yield tends to decrease due to agglomeration. In contrast, coarse raw powders make deteriorate the contact area between raw material powders containing Al reducing agent. To ensure the optimal thermite reaction efficiency, it is required to optimize a mixture condition of raw material powders prior to thermite reaction. From the current experiment, the maximum thermite reaction efficiency is 77%, which came from Nb₂O₅ + NiO +Al mixtures with size distribution from 9.25 to 22.63 ㎛.

• Transactions on Electrical and Electronic Materials
• /
• 제11권5호
• /
• pp.234-237
• /
• 2010

Nanoenergetic materials were synthesized and the thermite reaction between the CuO nanowires and the deposited nano-Al by Joule heating was studied. CuO nanowires were grown by thermal annealing on a glass substrate. To produce nanoenergetic materials, nano-Al was deposited on the top surface of CuO nanowires. The temperature of the first exothermic reaction peak occurred at approximately $600^{\circ}C$. The released heat energy calculated from the first exothermic reaction peak in differential scanning calorimetry, was approximately 1,178 J/g. The combustion of the nanoenergetic materials resulted in a bright flash of light with an adiabatic frame temperature potentially greater than $2,000^{\circ}C$. This thermite reaction might be utilized to achieve a highly reliable selective area crystallization of amorphous silicon films.

• 한국분말재료학회지
• /
• 제30권4호
• /
• pp.332-338
• /
• 2023

Thermite welding is an exceptional process that does not require additional energy supplies, resulting in welded joints that exhibit mechanical properties and conductivity equivalent to those of the parent materials. The global adoption of thermite welding is growing across various industries. However, in Korea, limited research is being conducted on the core technology of thermite welding. Currently, domestic production of thermite powder in Korea involves recycling copper oxide (CuO). Unfortunately, controlling the particle size of waste CuO poses challenges, leading to the unwanted formation of pores and cracks during thermite welding. In this study, we investigate the influence of powder particle size on thermite welding in the production of Cu-thermite powder using waste CuO. We conduct the ball milling process for 0.5-24 h using recycled CuO. The evolution of the powder shape and size is analyzed using particle size analysis and scanning electron microscopy (SEM). Furthermore, we examine the thermal reaction characteristics through differential scanning calorimetry. Additionally, the microstructures of the welded samples are observed using optical microscopy and SEM to evaluate the impact of powder particle size on weldability. Lastly, hardness measurements are performed to assess the strengths of the welded materials.

• 화약ㆍ발파
• /
• 제33권3호
• /
• pp.21-28
• /
• 2015

본 연구의 목적은 연속적 폭굉속도(VOD) 측정시스템을 이용하여 상용 테르밋 반응 혼합제의 연속적인 연소전파거동을 측정하기 위한 방법을 제안하기 위함이다. 두 종류의 상용 VOD 센서(VOD PROBEROD-OS, VOD PROBEROD-HS)와 자체개발한 VOD 센서(VOD PROBEROD-ES)를 기존 연속적 VOD 측정시스템에 적용하여 테르밋 반응과정에서 발생하는 연소전파속도(VOC)를 측정한 결과, 자체 개발한 VOD PROBEROD-ES 센서만 정상적인 연속적 연소전파거동을 보여주었다. 결과적으로, 철재튜브 내 장전된 테르밋 반응 혼합제는 기폭점으로부터 100mm 이내에서 약 200m/s의 연소전파속도를 보였으며, 100mm와 300mm 구간에서 급작스럽게 증가하여 음속의 2배에 가까운 VOC를 나타내었다. 그 이후 서서히 증가하여 최종적으로 800m/s까지 증가하는 경향을 보였다. 이러한 결과는 테르밋 반응 혼합제를 이용하여 정상적인 VOC나 위력을 기대하기 위해서는 철재튜브 등으로 완전히 구속된 상태에 길이 300mm 이상 장전하여야 함을 의미한다.

• 한국세라믹학회지
• /
• 제33권7호
• /
• pp.832-838
• /
• 1996

Thermite reaction products of MgO and Al were added to MgO-C refractory to improve the properties of corrosion against the attack of slag, oxidation and mechanical spalling. Corrosion rate of MgO-C-MgAl2O4 spinel refractory at the ratio of 3.3(CaO/SiO2) slag was smaller than that of MgO-C and MgO-C-Al refractory. The excellent corrosion resistance of the MgO-C-MgAl2O4 spinel refractory against the slag attack was appeared by Al and MgAl2O4 spinel with high melting point and corrosion resistance and the high thermal conductivity and low thermal expansion of AIN. Hot M.O.R at 140$0^{\circ}C$ and the resistance of oxidation weight loss at 90$0^{\circ}C$ were 210kg/cm2 and -12% respectively.

• 한국응용과학기술학회지
• /
• 제28권2호
• /
• pp.135-139
• /
• 2011

In order to make high-purity ferro-manganese from $Mn_3O_4$ waste dust, the application of aluminothermite process to the reduction of the waste dust was investigated. The mixture from $Mn_3O_4$ dust as metallic source and Al metal powder as the reductant ignited, and reduced with an extremely intense exothermic reaction. The rapid propagation of the aluminothermite reaction occurred spontaneously and stably by ignition of the mixture. The Manganese having some alloy elements emerged as liquids due to the high temperatures reached up to about $2,500^{\circ}C$ and separated from the liquid by their differences of specific gravity. The result of thermite reaction showed the fact that can be obtained high purity ferro-manganese which have over about 90% of manganese content and lower impurities such as C, P, S than those of KS D3712 specification. The recovery of manganese from $Mn_3O_4$ dust was lower level of about 65% than about 75% from manganese ore by electric furnace process, that is due to spatter loss because of its extremely intense thermite reaction. But it will be improved by the process designed to provide CaO as the cooler or to use the Al metal powder having larger particle size distribution.

• 한국추진공학회지
• /
• 제20권5호
• /
• pp.40-50
• /
• 2016

현재 적용되고 있는 에너지화 가소제는 $-NO_2$, $-ONO_2$ 및 $-N_3$와 같은 에너지화 활성 그룹을 포함하고 있어서 충격, 쇼크, 열 등 외부환경에 상당히 민감하여 복합화약의 둔감 안정성을 취약하게 한다. 본 연구에서는 민감한 에너지화 활성 그룹이 아니라 근본적으로는 비활성 그룹으로 복합화약의 민감도에는 영향을 미치지 않지만, 복합화약의 반응 시에 테르밋반응에 의해 추가적인 에너지를 발생할 수 있는 불소계 반응성 가소제를 적용한 폴리우레탄 결합제를 클릭반응으로 합성하고 나노 알루미늄과의 테르밋반응에 대한 열적 특성을 고찰하였다.

• 한국세라믹학회지
• /
• 제32권1호
• /
• pp.11-16
• /
• 1995

High reaction heat evolved from the oxidation of Al was used to synthesize SiC, which might be difficult to be formed by SHS. Al2O3-SiC composite powder was easily manufactured using KNO3 as an ignition and reaction catalyst. Unreacted Si and C were observed after reaction dependent upon the composition of starting powders, reaction atmosphere and relative densities of compacted bodies. The unreacted carbon could be removed by calcining at $600^{\circ}C$ and the remaining Si could be removed by dissolving in NaOH solution. The final powder particles were smaller than 1${\mu}{\textrm}{m}$ in size.

• 한국분말재료학회지
• /
• 제26권3호
• /
• pp.220-224
• /
• 2019

The aluminum (Al)/copper oxide (CuO) complex is known as the most promising material for thermite reactions, releasing a high heat and pressure through ignition or thermal heating. To improve the reaction rate and wettability for handling safety, nanosized primary particles are applied on Al/CuO composite for energetic materials in explosives or propellants. Herein, graphene oxide (GO) is adopted for the Al/CuO composites as the functional supporting materials, preventing a phase-separation between solvent and composites, leading to a significantly enhanced reactivity. The characterizations of Al/CuO decorated on GO(Al/CuO/GO) are performed through scanning electron microscopy, transmission electron microscopy, and energy dispersive X-ray spectroscopy mapping analysis. Moreover, the functional bridging between Al/CuO and GO is suggested by identifying the chemical bonding with GO in X-ray photoelectron spectroscopy analysis. The reactivity of Al/CuO/GO composites is evaluated by comparing the maximum pressure and rate of the pressure increase of Al/CuO and Al/CuO/GO. The composites with a specific concentration of GO (10 wt%) demonstrate a well-dispersed mixture in hexane solution without phase separation.

• 자원리싸이클링
• /
• 제21권3호
• /
• pp.21-27
• /
• 2012

이전의 연구에서는 $Mn_3O_4$ 분진으로부터 고순도 훼로망간를 얻기 위해, Al 테르밋법이 검토되었다. 그 결과는 Mn 함유율이 약 93% 이상이고, KS D3712 규격 이하의 낮은 C, P, S의 불순물을 함유한 고순도 페로망간을 얻을 수 있음 보여주었다. 본 연구에서는 제조 코스트가 Al 분말보다 저렴한 Si 분말이 $Mn_3O_4$ 분진의 테르밋 반응법의 환원제로 검토되었다. 그 결과 환원제로 Si 분말을 단독으로 첨가할 경우는 착화가 불안정하여 테르밋 반응이 일어나지 않았으나, 환원제로 Si 분말과 Al 분말을 동시에 첨가할 경우는 C, P, S의 불순물 함유율이 매우 낮은 고순도 페로망간을 얻을 수 있었다.