• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2004년도 추계학술발표대회 개요집
• /
• pp.174-176
• /
• 2004

The duplex stainless clad vessel with 38m & over thickness shall be performed to PWHT based on the ASME code. In this case, it is well-known that precipitators such as carbides and sigma($\sigma$) phase are formed at gram boundary between ferrite and austenite phase. Therefore, a weld test for simulating this situation has been planned and performed by 3309LMo71-1 for barrier layer and E2209Tl-1 for 2nd & over layer and then carried out to investigate the overlaid weld metal. Based on the test results, it could be concluded that PWHT should be carried out after the completion of 1st(barrier) layer and then 2 & over layer should be applied.

• Journal of Welding and Joining
• /
• 제19권5호
• /
• pp.506-511
• /
• 2001

Weld overlay has been developed to improve the property of material surface which is used in the severe environment. Weld overlay is the process which uses an arc heat and welds different composition of alloy on the substrate for the improvements of heat resistance and wear resistance. Weld overlay has a lot of advantages which are high hardness, good processing efficiency, easy controlling of layer thickness, good quality and low cost. In this study, weld overlay was performed by MAG welding on the base metal(SS400) with filler metal which contain composite powders(Cr+C+Mn+Mo+NbC) and solid wire(JIS-YGW11). Characterization of hardness and wear resistance were analyzed by EDS, EPMA, XRD and observations of microstructure were performed to investigate characteristics of overlays. The experimental results of overlaid specimens manufactured with Cr+C+Mn+Mo+NbC powders were obtained as fellows. ${\alpha}-phase$, M(Fe, Cr)3C and NbC of overlays were increased with decreasing the wire feed rates and increasing powder feed rates. Also the hardness of overlays were increased and the specific wear were decreased.

• Journal of Welding and Joining
• /
• 제13권1호
• /
• pp.103-114
• /
• 1995

Plasma Transferred arc(PTA) hard facing process has been developed to obtain an overlay weld metal having excellent wear resistance. The effect of Ti, TiSi$_{2}$ and TiC powders addition on the surface of Aluminum alloy 5083 has been investigated with PTA process. This paper describes the result of test the performance of the overlay weld metal. The result can be summarized as follows 1. Intermetallic compound is formed on surface of base metal in Ti or TiSi$_{2}$ powder but the reaction with surface of base metal is little seen in TiC powder. 2. In formation of composite layer on aluminum alloy surface by plasma transferred arc welding process, high melting ceramics like TiC powder is excellent. 3. The multipass welding process is available for formation of high density of powder. But the more number of pass, the less effect of powder, it is considered, and limits of number of pass. 4. By increasing area fraction of TiC powder on Al alloy surface, in especially TiC powder the hardness increase more than 40% area fraction and 88% shows about Hv 700.