• Korean Journal of Materials Research
• /
• v.13 no.7
• /
• pp.420-423
• /
• 2003

Coatings of TiCrN ion-plated on a steel substrate was oxidized at $800^{\circ}C$ in air, and their oxidation mechanism was presented. During oxidation, substrate elements and Ti and Cr in the coating always diffused outwardly to form the oxide scale. Simultaneously, oxygen from the atmosphere diffused inward1y to react with Ti and Cr to form $TiO_2$and $Cr_2$$O_3$, respectively. Also, the counter-diffusion of cations and oxygen resulted in some oxygen dissolution in the unoxidized TiCrN coating, and Fe dissolution in the oxide scale. When the Ti content in the coating was high, the $TiO_2$-forming tendency was strong, while when the Cr content was high, the $Cr_2$$O_3$-forming tendency was strong.

• Journal of the Korean institute of surface engineering
• /
• v.54 no.5
• /
• pp.285-293
• /
• 2021

High-entropy TiAlCrSiN nano-composite coating was designed to improve mold life for high temperature liquid molding. Alloy design, powder fabrication and single alloying target fabrication for the high-entropy nano-composite coating were carried out. Using the single alloying target, an arc ion plating method was applied to prepare a TiAlCrSiN nano-composite coating had a 30 nm TiAlCrSiN layers are deposited layer by layer, and form about 4 ㎛-thickness of multi-layered coating. TiAlCrSiN nano-composite coating had a high hardness of about 39.9 GPa and a low coefficient of friction of less than about 0.47 in a dry environment. In addition, there was no change in the structure of the coating after the dissolution loss test in the molten metal at a temperature of about 1100 degrees.

• Journal of the Korean institute of surface engineering
• /
• v.43 no.6
• /
• pp.278-282
• /
• 2010

In this research, the friction and wear characteristic behaviors of coating materials of TiAlN and CrAlN were investigated. The wear test was conducted in air and un-lubricated state using the reciprocating friction wear tester. Temperature were 50 and $120^{\circ}C$, and load were 3, 7, and 11 kgf for tests. By comparing the coefficient of friction and observing the wear microstructure, the friction and wear characteristic behaviors of TiAlN and CrAlN coating layers on SKD61 were investigated. The coefficient of friction of CrAlN coating was lower than that of TiAlN at all conditions. Therefore, CrAlN was suggested to be more advantageous coating than TiAlN for the extrusion mold of aluminum.

• Korean Journal of Materials Research
• /
• v.14 no.8
• /
• pp.558-564
• /
• 2004

In order to improve the low hardness and low wear resistance of Ti-6Al-4V alloy, plasma carburization treatment and CrN film coating were carried out. Effects of the plasma carburization and CrN coating were analyzed and compared with the non-treated alloy by mechanical and creep tests. After plasma carburization and CrN coating treatments, the carburized layer was about 150 ${\mu}m$ in depth and CrN coated layer was about 7.5 ${\mu}m$ in thickness. Hardness value of about $H_{v}$ 402 of the non-treated alloy was improved to $H_{v}$ 1600 and 1390 by plasma carburization and CrN thin film coating, respectively. Stress exponent(n) was decreased from 9.10 in CrN coating specimen to 8.95 in carburized specimen. However, the activation energy(Q) was increased from 242 to 250 kJ/mol. It can be concluded that the static creep deformation for Ti-6Al-4V alloy is controlled by the dislocation climb over the ranges of the experimental conditions.

• Corrosion Science and Technology
• /
• v.22 no.4
• /
• pp.232-241
• /
• 2023

The mechanical properties of the hydrogen valve responsible for supplying and blocking hydrogen gas in a hydrogen fuel cell electric vehicle (FCEV) were researched. Mechanical properties by hydrogen embrittlement were investigated by coating chromium nitride (CrN) and titanium nitride (TiN) on aluminum alloy by arc ion plating method. The coating layer was deposited to a thickness of about 2 ㎛, and a slow strain rate test (SSRT) was conducted after hydrogen embrittlement to determine the hydrogen embrittlement resistance of the CrN and TiN coating layers. The CrN-coated specimen presented little decrease in mechanical properties until 12 hours of hydrogen charging due to its excellent resistance to hydrogen permeation. However, both the CrN and TiN-coated specimens exhibited deterioration in mechanical properties due to the peeling of the coating layer after 24 hours of hydrogen charging. The specimens coated at 350 ℃ presented a significant decrease in ultimate tensile strength due to abnormal grain growth.

• International Journal of Ocean System Engineering
• /
• v.2 no.2
• /
• pp.106-115
• /
• 2012

In the present study, TiN and CrN films were coated by arc ion plating equipment onto aluminum alloy substrate, A2024. The film thickness was about 4.65 ${\mu}m$. TiN and CrN films were analyzed by X-ray diffraction and energy dispersive X-ray equipments. The Young's modulus and the micro-Vickers hardness of aluminum substrate were modified by the ceramic film coatings. The difference in Young's modulus between substrate and coating film would affect on the wear resistance. The critical load, Lc, was 75.8 N for TiN and 85.5 N for CrN. It indicated from the observation of optical micrographs for TiN and CrN films that lots of cracks widely propagated toward the both sides of scratch track in the early stage of MODE I. TiN film began to delaminate completely at MODE II stage. The substrate was finally glittered at MODE III stage. For CrN film, a few crack can be observed at MODE I stage. The delamination of film was not still occurred at MODE II and then was happened at MODE III. This agrees with critical load measurement which the adhesive strength was greater for CrN film than for TiN film. Consequently, it was difficult for CrN to delaminate because the adhesive strength was excellent against Al substrate. The wear process, which the film adheres and the ball transfers, could be enhanced because of the increase in loading. The wear weight of ball was less for CrN than for TiN. This means that the wear damage of ball was greater for TiN than for CrN film. It is also obvious that it was difficult to delaminate because the CrN coating film has high toughness. The coefficient of friction was less for CrN coating film than for TiN film.

• Journal of the Korean institute of surface engineering
• /
• v.42 no.6
• /
• pp.272-275
• /
• 2009

The purpose of this study is to show the friction and wear characteristic behaviors of TiN and CrN coated SKD61 which is applied to Al 6xxx extrusion mold material. The friction and wear characteristic behaviors of both coating layers were investigated by the reciprocating friction wear tester under atmospheric pressure and un-lubricated state. The processing parameters in this study were temperature (50 and $120^{\circ}C$) and load (3, 5, and 11 kgf). This study was carried out while comparing the coefficient of friction and microstructure of TiN and CrN coating layers on SKD61. The coefficient of friction of CrN became lower than that of TiN at all conditions. Therefore, CrN was suggested to be more advantageous than TiN for extrusion mold.

• Proceedings of the Korea Committee for Ocean Resources and Engineering Conference
• /
• 2000.04a
• /
• pp.164-169
• /
• 2000

The remote measurement system(RMS) as a new experimental method is limited in its application to crack measurements at elevated temperatures because of the oxide layer on the specimen surface. Since TiAlN and Cr coating layers have a high resistance to oxidation and wear, this paper proposed a TiAlN and Cr coating technique for specimens to facilitate the measurement of crack growth behavior using RMS. To investigate the effects of the coating layer, tension and fatigue tests were carried out at room temperature and at 538$^{\circ}C$, using specimens of 1Cr-1Mo-0.25V steel. From the experimental results, it was found that the mechanical properties of the TiAlN and Cr coated specimens were similar to those of the substrate. Accordingly, the TiAlN and Cr coated layer had hardly any influence on the fatigue crack propagation.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.21 no.6
• /
• pp.235-239
• /
• 2011

TiCrN layers (Ti : Cr = 20 : 80 and 5 : 95 wt%) were deposited on Inconel 617 and the effect of TiCrN coating on the high temperature stability of Inconel 617 up to $1000^{\circ}C$ was examined. XRD analysis and microstructural observation showed that vigorous and inhomogenous Cr diffusion to the surface was suppressed by TiCrN layer compare to the uncoated Inconel 617. This led to a distinctive enhancement in thermal oxidation resistance of Inconel 617.

• Transactions of Materials Processing
• /
• v.31 no.1
• /
• pp.11-16
• /
• 2022

In this paper, wear characteristics of PVD coatings were compared on the die surface for cold stamping of MART1470 steel sheet with the finite element analysis and the pin-on-disc wear test. Three types of PVD coatings (CrN, TiAlCrN, and MoS2TiCr(W)N) were considered for the tool surface made of STD11 material. The stamping process of an auto-body part was analyzed with the finite element method. Ranges of process variables for the wear test such as contact pressure, relative speed, and sliding distance were predicted from analysis results. In order to quantitatively analyze wear characteristics of each coating, the amount of wear was measured and compared according to process variables with the pin-on-disc wear test. The influence of each process variable was investigated and the wear characteristics of the three coating layers were quantitatively compared. It was confirmed that the wear characteristics of MoS₂TiCr(W)N coating were better than those of CrN and TiAlCrN. It was noted that the proposed prediction approach could predict and respond to the wear phenomenon occurring in the stamping process.