• Steel and Composite Structures
• /
• v.42 no.4
• /
• pp.553-568
• /
• 2022

This paper explored the viability of utilising titanium alloy bolts in the construction industry through an experimental programme, where a total of sixty-six titanium alloy (Ti/6Al/4V) bolts were tested under axial tension, pure shear and combined tension and shear. In addition, a series of Charpy V-notch specimens machined from titanium alloy bolts, conventional high-strength steel bolts, austenitic and duplex stainless steel bolts were tested for impact toughness comparisons. The obtained experimental results demonstrated that the axial tensile and pure shear capacities of titanium alloy bolts can be reasonably estimated by the current design standards for steel structures (Eurocode 3, AS 4100 and AISC 360). However, under the combined tension and shear loading conditions, significant underestimation by Eurocode 3 and unsafe predictions through AS 4100 and AISC 360 indicate that proper modifications are necessary to facilitate the safe and economic use of titanium alloy bolts. In addition, numerical models were developed to calibrate the fracture parameters of the tested titanium alloy bolts. Furthermore, a design-based selection process of titanium alloy bolts in the structural applications was proposed, in which the ultimate strength, ductility performance and corrosion resistance (including galvanic corrosion) of titanium alloy bolts was mainly considered.

• Journal of the Korean Society of Industry Convergence
• /
• v.22 no.2
• /
• pp.105-110
• /
• 2019

Most titanium alloy waste with cutting oil was discarded without recycling process so that it can be caused by metal and oil fires. However, there is no fire management system and studies on the titanium or titanium alloy waste in spite of high fire risk. The purpose of this experimental study is to identify the fire risk of the titanium alloy waste with cutting oil. We collected the 120g waste which was made in the biomedical titanium alloy cutting process. The waste was burned and conducted thermal image analysis with infrared camera. The experimental results which illustrated the process, characteristics, and trends of fire are presented. Firstly, the cutting oil was burned and partially the titanium alloy waste was burned. The maximum temperature of the fire was more than $650^{\circ}C$ in some specific spots. These results means when a lot of titanium alloy waste with cutting oil was ignited, this fire could connect the titanium fire. In other words, the fire has a flammable liquid fire and combustible metal fire at the same time. The experimental study could be used fire prevention, response, and investigation of the titanium alloy waste.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.1 no.1
• /
• pp.55-62
• /
• 2002

This investigation reports the grinding characteristics of titanium alloy(Ti-6AI-4V). Grinding experiments were performed at various grinding conditions. The grinding forces were measured to investigate the grindability of titanium alloy with the five different wheels including Green carbide, Alumina, Resin Diamond, Resin CBN and Vitrified CBN. To investigate the grinding characteristics of titanium alloy grinding force, force ratio, specific grinding energy and grinding-ratio were measured. Surface roughness was also measured with tracer and the ground surfaces were observed with SEM Residual stress measurement was conducted on the X-Ray Diffractometer. Force ratio of grinding of titanium alloy was very lower than that of grinding of SKD-11 Surface roughness with Resin Diamond wheel was a little larger and rougher surface than that with other wheels Grinding ratio of titanium alloy was a little lower than that of other materials. Grinding ratio of titanium alloy with Diamond wheel was almost six times larger than that With CBN wheel. As a result of five different wheels, the most excellent wheel in grinding of Titanium alloy was Resin Diamond wheel.

• Proceedings of the Korean Society of Machine Tool Engineers Conference
• /
• 2000.10a
• /
• pp.349-354
• /
• 2000

A use of Titanium alloy as a structural material is increasing lately. Among those titanium alloys, Ti-6A1-4V alloy is the most popular one with taking 2/3 of it's market. Also, Ti-6A1-4V alloy can get the stability of organization and product measure, and the evaluation of the cutting ability and the mechanical characteristics. The point in titanium alloy work is on how treat the heat generated during grinding. Because the heat conductivity of titanium alloy is unnegligibly low, the grinding heat is accumulated in workpiece, and it cause the increasing of grinding grits' wear and the rough grinding surface. So, these characteristics in grinding of titanium alloy will change the mechanical characteristics of the titanium alloy. From this study, the mechanical characteristics of annealed Ti-6A1-4V alloy after grinding was concerned with checking out the bending strength values, and the factor of the change and the difference was analyzed after analyzing the surface roughness and the image from SEM.

• The Journal of Korean Academy of Prosthodontics
• /
• v.39 no.3
• /
• pp.297-305
• /
• 2001

Statement of problem. There have been previous studies about instability according to screw material by means of calculating preload in tightening screw or recording of the torque necessary to loosen screw after tightening screw. Purpose. The purpose of this study was to evaluate screw joint stability through the analysis of fitness at the mating thread surfaces between implant and screw after tightening screws made of different materials. Material and methods. In this study, screws were respectively used to secure a cemented abutment to a hexlock implant fixture; teflon coated titanium alloy screw and titanium alloy screw(Steri-Oss), gold-plated gold-palladium alloy screw and titanium alloy screw(Implant Innovation), gold screw and titanium screw(AVANA Dental Implant System). Each abutment screw was secured to the implant with recommended torque value using a digital torque controller. Each screw was again tightened after 10minutes. All samples were cross sectioned with sandpaper and polished. Then samples were evaluated with an scanning electron microscope analysis. Results. In titanium alloy screw, irregular contact and relatively large gap was present at mating thread surface. Also in teflon-coated titanium screw, incomplete seating and only partially contact was present at the mating thread surface. In gold-plated gold-palladium alloy screw, relatively close and tight contact without the presence of large gap was present by existing of gold coating at the mating thread surfaces. In gold alloy screw, relatively small gap between the mating components was seen. Conclusions. This result suggested that gold plated gold-palladium alloy screw and gold alloy screw achieved a greater degree of contact at the mating thread surfaces compared to titanium alloy screw and teflon-coated titanium alloy screw.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.8 no.4
• /
• pp.20-27
• /
• 2009

The characteristics of titanium alloy as a relatively advanced material is low density, avirulent and, superior corrosive resistant, therefore the use of titanium alloy is increasing lately in aerospace and mechanical technologies, precision machinery, electronics industry, petro-chemical industries and biomedical areas. In these days, the titanium alloy product is required various surface qualities of not only smooth surface but also rough surface depending on usages. The purpose of this experimental research is to find the optimum surface roughness of titanium alloy of Ti-6Al-4V, by micro abrasive blasting as depending variable conditions of working pressure, nozzle size, working time, stand of distance and power particle size.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2001.04a
• /
• pp.1076-1079
• /
• 2001

This investigation reports the grinding characteristics of titanium alloy(Ti-6Al-4V). Grinding experiments were performed at various grinding conditions. The grinding forces and grinding force ratio were measured to investigate the grindability of titanium alloy with the Diamond and CBN wheel. To investigate the grinding characteristics of titanium alloy grinding force ratio and grinding ratio were measured. Surface profile of wheel was also measured with tracer and the ground surfaces and chip were observed with SEM. Grinding-ratio of titanium alloy was much lower than that of other materials. Grinding-ratio of titanium alloy with Diamond wheel was almost six times larger than that with CBN wheel.

• Transactions of Materials Processing
• /
• v.19 no.4
• /
• pp.230-235
• /
• 2010

Titanium alloy sheets have excellent specific strength and corrosion resistance as well as good performance at high temperature. Recently, titanium alloys are widely employed not only for aerospace parts but also for bio prothesis and motorcycle. However, the database is insufficient in the titanium alloy for press forming process. In this study, the effect of temperature on the forming limit diagram was investigated for Ti-6Al-4V titanium alloy sheet through the Hecker‘s punch stretching test at elevated temperature. Experimental results obtained in this study can provide a database for the development of press forming process at elevated temperature of Ti-6Al-4V titanium alloy sheet. From the experimental studies it can be concluded that the formability of Ti-6Al-4V titanium alloy sheet is governed by the ductile failure for the testing temperature. The formability of Ti-6Al-4V titanium alloy sheet at $700^{\circ}C$ increases about 7 times compared with that at room temperature.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2009.05a
• /
• pp.152-157
• /
• 2009

Titanium alloy sheets have excellent specific strength and corrosion resistance as well as good performance at high temperature. Recently, titanium alloys are widely employed not only aerospace parts but also bio prothesis and motorcycle. But the database is insufficient of the titanium alloy for press forming process. In this study, the effect of temperature on the forming limit diagram was investigated for Ti-6Al-4V titanium alloy sheet through the Hocker's punch stretching test at elevated temperature. Experimental results obtained in this study can provide a database for development of press forming process at elevated temperature of Ti-6Al-4V titanium alloy sheet. From the experimental studies it can be concluded that the formability of Ti-6Al-4V titanium alloy sheet is governed by the ductile failure for the testing temperature below and vice versa neck-induced failure above the recrystalization temperature $0.5T_m$. The formability of Ti-6Al-4V titanium alloy sheet at $750^{\circ}C$ increases about 7 times compared with that at room temperature.

• Clean Technology
• /
• v.19 no.2
• /
• pp.75-83
• /
• 2013

In the present paper, we review recycling and applications of titanium binary alloy scraps. The recycling techniques are to successfully prepare low oxygen content ingots using hydrogen plasma arc melting (HPAM) and to produce low oxygen content titanium alloy powders by Hydrogenation-dehydrogenation (HDH) and Deoxidation in solid state (DOSS) process. In addition, as applications of the titanium binary alloy scraps, Ti based solid-solution carbide powders, which would be used for producing Ti based solid-solution cermets with high toughness, were prepared using the titanium binary alloy scraps. These results confirmed that the titanium alloy scraps could be recycled and refined using the HPAM. The resulting oxygen content of the titanium alloy powders were below 1,000 ppm after powderizing. Finally, we had confirmed that the refined titanium alloy powders were able to be utilized as raw materials for preparing the toughened cermets.