• 한국전기전자재료학회논문지
• /
• 제18권1호
• /
• pp.68-74
• /
• 2005

In this work, polymerization conditions of the gel polymer electrolyte (GPE) were studied to obtain better electrochemical performances in a lithium-ion polymer battery. When the polymerization temperature and time of the GPE were 70$^{\circ}C$ and 70 min, respectively, the lithium polymer battery showed excellent a rate capability and cycleability. The TMPETA (trimethylolpropane ethoxylate triacrylate)/TEGDMA (triethylene glycol dimethacrylate)-based cells prepared under optimized polymerization conditions showed excellent rate capability and low-temperature performances: The discharge capacity of cells at 2 Crate showed 92.1 % against 0.2C rate. The cell at -20 $^{\circ}C$ also delivered 82.4 % of the discharge capacity at room temperature.

• Nuclear Engineering and Technology
• /
• 제14권2호
• /
• pp.70-77
• /
• 1982

전자선을 이용하여 저밀도 폴리에틸렌을 가교시킬때의 삼관능성 단위체와 산화방지제의 효과를 검토하였다. 가교촉진제로서는 삼관능성 단량체인 Trimethylolpropane triacrylate(TMPTA), Trimethylolpropane trimethacrylate(TMPTM)과 Triallyl cyanurate(TAC)가 사용되었고, 산화방지제로서는 Irganox 1010(Pentaerythritol-tetrakist[3-(3,5-di-t-butyl-4-hydroxyphenyl)-propionate]), Santo-nox R(4,4'-Thio-bis(3-methyl-6-t-butylphenol)), Nocrac D(N-phenyl-$\beta$-naphthylamine)와 Bisphenol A(4,4'-Iso-propylidene bisphenol)가 사용되었다. 삼관능성 단위체중에서 TMPTA가 폴리에틸렌의 가교도를 제일 크게 높였으며 또한 산화안정성도 부여했다. 산화방지제중에서 Nocrac D가 폴리에틸렌에 가장 적당한 것으로 나타났다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2004년도 하계학술대회 논문집 Vol.5 No.1
• /
• pp.511-514
• /
• 2004

본 연구에서는 trimethylolpropane triacrylate(TMPTA)를 사용한 겔폴리머전해질의 전기화학적 특성에 대하여 조사하였다. 겔고분자전해질의 상온 이온전도도는 약 $5.0{\times}10^{-3}S{\cdot}cm^{-1}$이었으며, 온도가 높아짐에 따라 이온전도도는 증가하였다. TMPTA계 겔고분자전해질은 4.5V(vs. $Li/Li^+$)까지의 전위영역에서 우수한 전기화학적 안정성을 나타내었으며, TMPTA계 겔고분자전해질을 적용한 리튬이온폴리머전지의 고율 및 저온 방전특성은 양호하였다. 또한 사이클수명도 200 사이클이 진행된 후에도 초기용량의 약 94%라는 높은 용량유지율을 나타내었다.

• 접착 및 계면
• /
• 제20권1호
• /
• pp.15-22
• /
• 2019

Polybutadiene diol (PBD)과 isophorone diisocyanate (IPDI)의 반응을 통하여 이관능 우레탄 아크릴레이트 올리고머 (PB-UAO)를 합성하고, 여기에 삼관능 아크릴레이트 모노머 (Tris(2- acryloyloxyethyl) isocyanurate (TAOEIC), 또는 Trimethylolpropane triacrylate (TMPTA) 또는 Pentaerythritol triacrylate(PETA)), 단관능 아크릴레이트 모노머 (Stearyl Acrylate) 그리고 광개시제를 혼합한 후 이형필름 위에 코팅하고 자외선 경화를 통하여 감압 점착 필름을 제조하였다. 삼관능 아크릴레이트 모노머의 구조 및 함량에 따른 감압 점착제의 박리강도, 인장강도, 신율, 열안정성 및 흡습 특성의 변화를 고찰하였다. 삼관능 아크릴레이트 모노머의 함량이 증가할수록, 그리고 분자량이 작을수록 감압 점착 필름의 박리강도, 연신율 및 흡습율은 감소하는 경향을 보였으며, 인장강도 및 열안정성은 증가하는 것을 확인하였다.

• 접착 및 계면
• /
• 제5권4호
• /
• pp.1-8
• /
• 2004

다이싱 테이프에 사용되는 UV경화형 점착제를 아크릴 공중합체를 butyl acrylate, acrylic acid, methyl methacrylate를 용액 중합을 통해 중합한 뒤, trimethylolpropane triacrylate를 블렌딩하여 제조하였다. 제조된 점착제는 UV 조사량에 따라 접착력, 유리전이온도 ($T_g$)를 측정하였는데 UV 조사량이 증가할수록 접착력은 급격하게 감소하였고 $T_g$도 증가하였다. 웨이퍼 표면에 점착 샘플을 부착하여 UV 조사 후 박리하여 표면을 관찰한 결과 점착잔류물을 남기지 않았다.

• Korean Chemical Engineering Research
• /
• 제50권4호
• /
• pp.621-626
• /
• 2012

본 연구에서는 마이크로 기공의 중공구를 유기 고분자 수지와 복합화한 유/무기 하이브리드 물질을 제조하여 우수한 단열 성능을 갖는 코팅유리를 개발하고자 하였다. 유기 고분자 물질로는 투명성과 접착성이 우수한 6관능기의 우레탄 아크릴레이트(UP118), 3관능기의 trimethylolpropane triacrylate (TMPTA), 2관능기의 1,6-hexanediol diacrylate (HDDA), 광 개시제(Irgacure184) 등으로 구성된 자외선 경화형 수지를 사용하였다. 유리 및 실리카 중공구를 고분자 수지에 각각 10~40 vol%까지 첨가하여 얻어진 코팅 졸을 투명유리에 바(bar)코팅 방식으로 박막을 형성시킨 후 자외선 경화를 통해 최종 코팅유리를 제조하였다. 마이크로 중공구의 종류 및 함량이 제조된 코팅유리의 광 투과율, 열전도도, 접착성 및 표면 경도에 미치는 영향을 조사하였다. 복합물 코팅유리는 중공구가 과량 첨가되어도 우수한 접착성(5B)을 유지하였으며, 단열 성능은 각 중공구가 20 vol%만 함유되어도 뚜렷하게 향상된 결과를 나타냈다. 또한 실리카 중공구(SP)를 단열 재료로 사용하였을 경우 광 투과율 80 %의 투명 코팅유리를 얻을 수 있었다.

• 청정기술
• /
• 제23권2호
• /
• pp.148-157
• /
• 2017

To prepare UV-curable polyurethane-acrylate oligomer, NCO-terminated urethane prepolymers with trimethylolpropane, [TMP; 0 (0), 0.1 (0.021) and 0.2 (0.043) mole (mole fraction)] as crosslinkable tri-functional chain extender were end-capped with pentaerythritol triacrylate [PETA; 2.0 (0.400), 1.7 (0.354) and 1.4 (0.304) mole (mole fraction)] with one hydroxyl group/three vinyl functionalities. The stable as-formulated UV-curable polyurethane-acrylates [stable mixtures of PETA-capped oligomer/reactive acrylic monomer diluents without/with heptadecafluorodecyl methacrylate (PFA; 0, 6 and 9 wt%)] were formed up to 0.2 (0.043) mole (mole fraction) of TMP content in the prepolymer, while homogeneous-mixing failed at 0.3 (0.068) mole (mole fraction), in which the crosslink density in NCO-terminated urethane prepolymer was too high to enable the formation of stable mixture. This study examined the effect of TMP/PETA molar ratio and heptadecafluorodecyl methacrylate (PFA) content (wt%) on the properties of UV-cured polyurethane-acrylates as marine antifouling coating materials. The properties of UV-cured polyurethane-acrylate were found to be significantly dependent on the crosslinkable TMP/PETA ratio and PFA content. With the increasing of the TMP and PFA contents, the contact angles increased, and consequently the surface tension decreased. The adhesion of algae/barnacles to PFA contained film samples were found to be sufficiently weak to allow their easy removal. These results suggest that the UV-cured samples containing PFA have strong potential as coating materials for antifouling applications.

• Korean Chemical Engineering Research
• /
• 제51권5호
• /
• pp.597-601
• /
• 2013

본 연구는 액적기반 미세유체 장치를 이용하여 단분산성 마이크로캡슐의 간단한 제조방법에 관한 것이다. 본 연구에서 제시한 제조 방법은 이중액적을 생성시키기 위해 기존의 복잡한 표면처리가 필요한 이중 유화과정을 대신하여 하나의 교차점을 가진 단일공정을 사용하고자 한다. 먼저, 분산상은 광중합이 가능한 ethoxylated trimethylolpropane triacrylate (ETPTA) 단량체와 fluorocarbon (FC-77) 오일을 사용하고 연속상은 poly(vinyl alcohol) (PVA) 수용액을 사용하였으며, 미세유체 채널 내부로 흘려 주면 하나의 교차점에 흐름이 집중되어 균일한 이중액적을 생성한다. 생성된 이중액적은 광중합을 통해 마이크로캡슐을 제조한다. 상기 방법은 ETPTA 유체의 부피유속을 조절하여 이중액적의 껍질두께 제어가 가능하고 연속상인 물의 부피유속을 조절하여 전체 직경을 제어할 수 있다. 더 나아가, 본 시스템을 사용하여 다양한 물질들을 함입한 마이크로캡슐을 제작할 수 있으며, 약물전달시스템의 응용 기술에 활용될 것으로 예측된다.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2000년도 하계학술대회 논문집 C
• /
• pp.2077-2080
• /
• 2000

We studied about electrical, chemical and mechanical characteristics of XLPE by dicumyl peroxide(DCP) and trimethylolpropane triacrylate(TMPTA) content ratio. DCP content was changed from 1.0 to 2.5phr increasing 0.5phr. TMPTA content was changed 0.5 to 1.5phr increasing 0.5phr. Thermal analysis (DSC) was carried out in order to observe tendency of 79 according to DCP and TMPTA content. In experimental results, content DCP 2.0phr and TMPTA 1.0phr has highest breakdown strength. Content DCP 2.0phr and TMPTA 0.5phr has lowest dielectric constant. Tendency of Tg did not affected by DCP and TMPTA content. Breakdown strength and Specific inductive capacity was measured.

• 반도체디스플레이기술학회지
• /
• 제13권1호
• /
• pp.35-41
• /
• 2014

UV curable transparent hard coating materials have been developed to improve the mechanical and optical properties of PET substrate. The coating materials were synthesized using various urethane acrylate oligomers, monomers, photo initiators, and leveling agents. The materials were coated on PET substrates and UV cured. The hard coated PET films were shown to have the good scratch resistance and transparency. When the urethane acrylate oligomer with more functional groups was introduced into the coating solution, the mechanical and optical properties were improved. However the higher concentration of 9-functional oligomer resulted in the decrease of workability. The addition of trimethylolpropane ethoxylate$(EO/OH)_9$ triacrylate(TMPETA) to coating solution improved the workability and properties. As a result, the UV cured film from the formulation of urethane acrylate oligomer with 9-functional groups, TMPETA as a monomer, IRACURE 754 as a photo initiator and BYK-340 as a leveling agent showed the best mechanical and optical properties in this study.