• Journal of the Korea institute for structural maintenance and inspection
• /
• v.20 no.5
• /
• pp.85-92
• /
• 2016

The eight mixes and artificial soil aggregates were prepared for evaluating the practical application of lightweight foamed concrete as soil aggregates. The main parameter was unit binder content ranged between from 100 to $800kg/m^3$. In lightweight foamed concrete, flow, slurry and dried density, and compressive strength at different ages were measured. In Artificial soil aggregates crushed from lightweight foamed concrete, particle size distribution, pH, coefficient of permeability, cation exchange capacity(CEC), and ratio of carbon to nitrogen(ratio of C/N), were measured. The test results showed that flow, slurry and dried density, and compressive strength at different ages of lightweight foamed concrete increased with the increasing of unit binder content. Compressive strength at age of 28, of lightweight foamed concrete with unit binder of more than $500kg/m^3$, was more than 4 MPa. The ammonium phosphate immersion time of more than age of 3, was effective to decrease pH of artificial soil aggregates. In addition, artificial soil aggregates was evaluated as high class in terms of cation exchange capacity(CEC), while satisfied with value of ratio of carbon to nitrogen(ratio of C/N) recommended by landscape specification.

• Journal of the Korea Concrete Institute
• /
• v.12 no.1
• /
• pp.79-88
• /
• 2000

Usually, the expansive additives is used to prevent the occurrence of drying shrinkage in concrete. However it may sometimes be over-added in field due to the insufficient cognition of constructor's, which may cause the serious problems in concrete structures. In this study the experiments are performed to present the expansion properties of concrete by varying the water to binder ratios, unit contents of expansive additives and curing conditions. By the results, the strength showed an increase with the addition of expansion additives from 30kg/㎥ up to 50kg/㎥, and a great decrease by contraries if the larger amount are added. Also the more the expansion additives were used, the more length change occurred in concrete. In view of the curing conditions, the concrete by air cured appeared a little expansion even the unit expansion additives increased, which showed an opposite inclination of that with standard curing. This could be explained by the less occurrence of hydration in air condition which also lead to the little expansion of concrete. Hence the expansion concrete to be cured in water or moisture condition became an especial important thing. concrete using expansive additives showed that high expansion was taken place with the rise of temperature.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.7 no.3
• /
• pp.235-242
• /
• 2019

The objective of this study is to modify the mixture proportions of concrete that were developed for section enlargement strengthening elements using a specially designed binder composed of 5% ultra-rapid hardening cement, 10% polymer, and 85% ordinary portland cement in order to assign the self-compaction property to such concrete. The self-compaction abilities of concrete were estimated by the performance criteria specified in JSCE and EFNARC provions. Test results showed that the increase in the unit binder content at the consistent water-to-bider ratio led to increase in viscosity of fresh concrete but did not exhibit the decrease in the fluidity due to a greater viscosity. The mixture proportioning of self-compaction section enlargement concrete could be considered at the following conditions: unit binder contents of $430kg/m^3{\sim}470kg/m^3$ and fine aggregate-to-total aggregate ratios of 40%~46% at the water-to-binder ratio of 38%.

• Journal of the Korean Applied Science and Technology
• /
• v.36 no.1
• /
• pp.153-164
• /
• 2019

To develop a high performance SCR catalyst which has better specific surface area, lightness of weight and fast temperature response than those of existing commercial SCR catalyst, metal foam type SCR catalysts were prepared by washcoating with vanadium, tungsten and binder. The de-NOx performance test of the prepared catalysts was carried out on atmospheric micro-test unit at lab. scale according to space velocity variation and temperature change, and the characteristics of them were analyzed by Porosimeter, SEM(scanning electron microscope), EDX(energy dispersive x-ray spectrometer), ICP(inductively coupled plasma) and Stereomicroscope. The NOx reduction performance decreased as the space velocity increased and was found to be the best at 3.5 wt.% contents of the vanadium and tungsten. It was found that the larger amount of binder was added, the worse the NOx reduction performance was, which was considered to be that the number of active sites of the prepared catalyst surface was occupied by the binder. We found that the amount of binder to be added to prepare the catalyst should be properly controlled by the condition of coated catalyt surface.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.12 no.1
• /
• pp.53-62
• /
• 2024

In this paper, an experimental study on the strengths and material properties of concrete manufactured by using coal gangue, as a fine aggregate was conducted. Experimental parameters included coal gangue aggregate contents as a replacement of fine aggregate by 50 % and 100 % (by volume) and fly ash contents. The water-binder ratio was fixed at 0.38. In addition, 30 % of the OPC binder was replaced with fly ash in some mixtures. Test of the unit weight, compressive, split tensile, and flexural tensile strength of concrete were performed and test results were analyzed. Unit weight, compressive strength, split tensile strength, and flexural tensile strength decreased as the coal recycled aggregates increased. In addition, TGA and SEM experiments, which are microstructure experiments, were conducted to analyze thermogravimetric analysis and ITZ by section.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.11a
• /
• pp.497-500
• /
• 2008

This research carries out experiments for hydration exothermic rate and adiabatic temperature rise of concrete to examine the characteristics of the hydration heat of high flowing self-compacting concrete with a normal strength. As a result of the hydration exothermic rate experiment, the high flowing self-compacting concrete that used Lime stone powder and fly ash as polymers shows that its hydration heat amount reduces due to the reduction of unit cement. The result measured the adiabatic temperature rise of concrete presents that high flowing self-compacting concrete having lots of binder contents has a good performance in temperature reduction due to the effect of polymer and that triple adding high flowing self-compacting concrete has a similar temperature rise speed with conventional concrete. As a result of the research, high flowing self-compacting concrete shows a better temperature reduction performance for the binder content per unit than conventional concrete. In addition, it is judged that triple adding high flowing self-compacting concrete with a specified concrete strength 30 MPa is more beneficial in temperature reduction and early hydration heat than double adding high flowing self-compacting concrete.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1998.10a
• /
• pp.386-391
• /
• 1998

Recently, high performance concrete developed has a good quality at fresh and hardened state, but high binder contents results in spending much money on manufacturing and many cracks by drying and autogenous shrinkage. Therefore, in this paper, not only prevention of cracks caused by drying and autogenous shrinkage, but improvement of quality and accmplishment of economy by applying F.A(fly ash), S.F(silica fume) and CSA(calcium sulfa aluminate) expansive additives as an inorganic admixtures in W/B 35% are discussed. According to the experimental results, when 5% of CSA Expansive additives and 15:5 (F.A:S.F)are replaced at unit cement content, high performance concrete with both good compensation of drying and autogenous shrinkage at hardened state is accomplished.

• Journal of The Korean Society of Agricultural Engineers
• /
• v.51 no.6
• /
• pp.97-103
• /
• 2009

This study was performed to evaluate the strength and durability properties of recycled polymer concrete using unsaturated polyester resin and recycled aggregates. Unsaturated polyester resin, natural and recycled aggregates and fly ash were used. The mix proportions were determined to satisfy the requirement for the workability and slump according to aggregate sizes (5-10 and 5-25 mm) and unit binder contents (10% and 12%). Tests for the compressive and flexural strength, freezing and thawing and durability for 20% sulfuric solution were performed. The compressive and flexural strength of recycled polymer concrete were in the range of 85~97 MPa and 17.9~20.8 MPa, respectively. The strengths of recycled polymer concrete using recycled aggregate have similar or slightly decreased compared to polymer concrete using natural aggregate. After 300 cycles of freezing and thawing, weight decrease ratio and durability factor of recycled polymer concrete were in the range of 0.13~1.42% and 94~99, respectively.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2005.11a
• /
• pp.599-602
• /
• 2005

In this research, the characteristics of the strength development and chloride attack resistance on the concrete using high early strength cement by steam curing temperature condition were studied. As a result, It is observed that the early strength(16hr) is increasing and the strength of 28 days is decreasing, according as the rising of the steam curing temperature without the kinds of base cement(OPC and high early strength cement). On the other hand, it is observed that the more the contents of the unit binder(base cement + GGBF) is abundant, the more the steam curing temperature can be reduced in case of the high early strength. Also, the chloride attack resistance is improved according as the amount of GGBF is increased with the kinds of base cement(OPC and high early strength cement).

• Advances in concrete construction
• /
• v.14 no.1
• /
• pp.1-13
• /
• 2022

Due to the physical-chemical characteristics of some bottom ash (BA), there are technical, economic and environmental limitations to find a destination that will add value to it. In Brazil, this residue is eventually used for filling coal extraction pits or remains in sedimentation ponds, creating a susceptible panorama to environmental issues. The geopolymers binders are one of the alternatives to the proper use high amounts of these materials. In this work, geopolymeric binder pastes were produced with BA mixed to activators with different alkali contents (expressed as %Na₂O), as well as the incorporation of soluble silicates (Ms content). The production of binary geopolymeric pastes based on the use of two industrial wastes: fluid catalytic cracking (FCC) and aluminum anodizing sludge (AAS), was also assessed. The content in mass of BA/FCC and BA/AAS ranged from 100/0, 90/10; 80/20 and 70/30. Systems with soluble silicates as activator in a molar ratio SiO₂/Na₂O of 1.0 (Ms = 1.0) and Na₂O content of 15%, showed the best results of mechanical strength (42 MPa at day 28^th). The improvement is up to 5X when compared to NaOH based systems. For systems with partial replacement of BA of 10% of AAS and 20% of FCC (80/20), the presence of soluble silicates was also effective to increase compressive strength.