• Clean Technology
• /
• v.24 no.3
• /
• pp.249-254
• /
• 2018

In order to improve the photo conversion efficiency (${\eta}$) of dye-sensitized solar cells (DSSCs), the electrospun $TiO_2$, $SiO_2$, $ZrO_2$ and $SnO_2$ nanofibers were added into the hydrothermally prepared $TiO_2$ nanoparticles for application to a photoelectrode for DSSCs. The $TiO_2$ nanofiber added photoelectrode exhibited a higher photo current density ($J_{sc}$) compared to the bare $TiO_2$ nanoparticles, which is caused from acceleration of the transfer of excited electron from dye molecule due to the nanofiber structure. The DSSCs with $SiO_2$ nanofibers shows a higher open circuit voltage ($V_{oc}$) of 0.67 V and the highest photo conversion efficiency was found to be 6.24%.

• The Journal of Korean Academy of Prosthodontics
• /
• v.47 no.1
• /
• pp.39-45
• /
• 2009

Statement of problem: Recently precalcification treatment has been studied to shorten the period of the implant. Purpose: This study was performed to evaluate the effect of precalcification treatment of $TiO_2$ Nanotube formed on Ti-6Al-4V Alloy. Material and methods: Specimens of $20{\times}10{\times}2\;mm$ in dimensions were polished sequentially from #220 to #1000 SiC paper, ultrasonically washed with acetone and distilled water for 5 min, and dried in an oven at $50^{\circ}C$ for 24 hours. The nanotubular layer was processed by electrochemical anodic oxidation in electrolytes containing 0.5 M $Na_2SO_4$ and 1.0 wt% NaF. Anodization was carried out using a regulated DC power supply (Kwangduck FA, Korea) at a potential of 20 V and current density of $30\;㎃/cm_2$ for 2 hours. Specimens were heat-treated at $600^{\circ}C$ for 2 hours to crystallize the amorphous $TiO_2$ nanotubes, and precalcified by soaking in $Na_2HPO_4$ solution for 24 hours and then in saturated $Ca(OH)_2$ solution for 5 hours. To evaluate the bioactivity of the precalcified $TiO_2$ nanotube layer, hydroxyapatite formation was investigated in a Hanks' balanced salts solution with pH 7.4 at $36.5^{\circ}C$ for 2 weeks. Results: Vertically oriented amorphous $TiO_2$ nanotubes of diameters 48.0 - 65.0 ㎚ were fabricated by anodizing treatment at 20 V for 2 hours in an 0.5 M $Na_2SO_4$ and 1.0 NaF solution. $TiO_2$ nanotubes were composed with strong anatase peak with presence of rutile peak after heat treatment at $600^{\circ}C$. The surface reactivity of $TiO_2$ nanotubes in SBF solution was enhanced by precalcification treatment in 0.5 M $Na_2HPO_4$ solution for 24 hours and then in saturated $Ca(OH)_2$ solution for 5 hours. The immersion in Hank's solution for 2 weeks showed that the intensity of $TiO_2$ rutile peak increased but the surface reactivity decreased by heat treatment at $600^{\circ}C$. Conclusion: This study shows that the precalcified treatment of $TiO_2$ Nanotube formed on Ti-6Al-4V Alloy enhances the surface reactivity.

• Proceedings of the KIEE Conference
• /
• 2002.07c
• /
• pp.1485-1487
• /
• 2002

The 0.96Mg$TiO_3$-0.04Sr$TiO_3$ ceramics with $V_2O_5$(5wt%) were prepared by the conventional mixed oxide method. The structural properties were investigated with sintering temperature by XRD and SEM. According to the X-ray diffraction patterns of the 0.96Mg$TiO_3$-0.04Sr$TiO_3$ceramics with $V_2O_5$(5wt%), the ilmenite $MgTiO_3$ and perovskite $SrTiO_3$ structures were coexisted and secondary phase $MgTi_2O_5$ were appeared. Increasing the sintering temperature, the grain size was increased and three types of grains were exhibited: larger circular grain, small square grain and lapth-shaped grain. In the case of 0.96Mg$TiO_3$-0.04Sr$TiO_3$ ceramics with $V_2O_5$(10wt%), dielectric constant, quality factor and temperature coefficient of resonant frequency were $15.24{\sim}18.55$, $22,890{\sim}42,100$GHz, -24.5${\sim}$+2.414ppm/$^{\circ}C$, respectively.

• Journal of the Korean Ceramic Society
• /
• v.22 no.3
• /
• pp.19-24
• /
• 1985

The phtoelectrochemical porperties of $Nb_2O_5$, $Sb_2O_3$ and $V_2O_5$ doped and pure $SrTiO_3$ ceramic electodes were investigated. Shapes of I-V and I-λ characteristics of the pure $SrTiO_3$ ceramic electrode are similar to those of SrTiO3 single crystal electorde ; the anodic current strats at -0.9V (vs. Ag/AgCI) in 1 N-NaOH aqueous solution and the photoresponse appears at a wavelength of about 390nm and the quantum efficiency is about 3.5% at wavelength of 390nm under 0.5V vs. Ag/AgCl. Photocurrents of $Nb_2O_5$, $Sb_2O_3$ and $V_2O_5$ doped electrodes and $V_2O_5$ doped ceramic electrode appears at wavelength of 390nm and 500nm respectively.

• Proceedings of the Korean Magnetic Resonance Society Conference
• /
• 2000.01a
• /
• pp.24-24
• /
• 2000

• Journal of the Korean Society for Heat Treatment
• /
• v.24 no.1
• /
• pp.31-36
• /
• 2011

$TiO_2$ films were deposited on a glass substrate with RF magnetron sputtering and then surface of $TiO_2$ films were electron beam irradiated in a vacuum condition to investigate the effect of electron bombardment on the thin film crystallization, surface roughness and gas sensitivity for hydrogen. $TiO_2$ films that electron beam irradiated at 450eV were amorphous phase, while the films irradiated at 900 eV show the anatase (101) diffraction peak in XRD pattern. AFM measurements show that the roughness is depend on the electron irradiation energy. As increase the hydrogen gas concentration and operation temperature, the gas sensitivity of $TiO_2$ and $TiO_2$/ZnO films is increased proportionally and $TiO_2$ films that electron beam irradiated at 900 eV show the higher sensitivity than the films were irradiated at 450eV. From the XRD pattern and AFM observation, it is supposed that the crystallization and rough surface promote the hydrogen gas sensitivity of $TiO_2$ films.

• Korean Journal of Materials Research
• /
• v.24 no.4
• /
• pp.207-213
• /
• 2014

Flexible $BaTiO_3$ films as dielectric materials for high energy density capacitors were deposited on polyethylene terephthalate (PET) substrates by r.f. magnetron sputtering. The growth behavior, microstructure and electrical properties of the flexible $BaTiO_3$ films were dependent on the sputtering pressure during sputtering. The RMS roughness and crystallite size of the $BaTiO_3$ increased with increasing sputtering pressure. All $BaTiO_3$ films had an amorphous structure, regardless of the sputtering pressures, due to the low PET substrate temperature. The composition of films showed an atomic ratio (Ba:Ti:O) of 0.9:1.1:3. The electrical properties of the $BaTiO_3$ films were affected by the microstructure and roughness. The $BaTiO_3$ films prepared at 100 mTorr exhibited a dielectric constant of ~80 at 1 kHz and a leakage current of $10^{-8}A$ at 400 kV/cm. Also, films showed polarization of $8{\mu}C/cm^2$ at 100 kV/cm and remnant polarization ($P_r$) of $2{\mu}C/cm^2$. This suggests that sputter deposited flexible $BaTiO_3$ films are a promising dielectric that can be used in high energy density capacitors owing to their high dielectric constant, low leakage current and stable preparation by sputtering.

• Journal of Korean Society for Atmospheric Environment
• /
• v.20 no.4
• /
• pp.451-463
• /
• 2004

The performance of disk-type catalytic filters impregnated by TiO$_2$ or TiO$_2$-3Al$_2$O$_3$ㆍ 2SiO$_2$ supports and V$_2$O$_{5}$ catalyst was evaluated for selective catalytic reduction (SCR) of NO with ammonia as a reductant. XRD, FT -IR, BET and SEM were used to characterize the catalytic filters prepared in this work. Optimal V$_2$O$_{5}$ loading and reaction temperature for V$_2$O$_{5}$/TiO$_2$ catalytic filters were 3-6 wt.% and 350-40$0^{\circ}C$ at GHSV 14,300 $hr^{-1}$ in the presence of oxygen, respectively. With increasing the V$_2$O$_{5}$ loading from 0.5 to 6 wt%, NO conversion increased from 24 to 96% at 40$0^{\circ}C$ and 14.300$hr^{-1}$, and maintained at 80% over in the V$_2$O$_{5}$ loading range of 3-6 wt.% and then dropped at V$_2$O$_{5}$ loading of 7wt.% over. In comparing V$_2$O$_{5}$/ TiO$_2$ and V$_2$O$_{5}$/ TiO$_2$-3Al$_2$O$_3$ㆍ2SiO$_2$ catalytic fillers, which have same 3wt.% V$_2$O$_{5}$ loading, the V$_2$O$_{5}$/ TiO$_2$-3A1$_2$O$_3$ㆍ2SiO$_2$ catalytic filter showed higher activity than V$_2$O$_{5}$/ TiO$_2$ catalytic filter, but higher differential pressure drops owing to its low air permeability. low air permeability.

• The Transactions of The Korean Institute of Electrical Engineers
• /
• v.63 no.9
• /
• pp.1233-1238
• /
• 2014

In this thesis, it is investigated the characteristics of Dye Sensitized Solar Cell (DSSC) according to variation of $TiO_2$ thickness (6, 12, 18, and $24{\mu}m$) and three distinct $TiO_2$ sintering temperatures (350, 450 and $550^{\circ}C$) by XRD, SEM, I-V and UV-Vis spectrophotometer. According to sintering temperature, $TiO_2$ was transformed into the anatase structure at $350^{\circ}C$, rutile structure at $550^{\circ}C$ and further into the two structure at $450^{\circ}C$. With increasing thickness up to $18{\mu}m$ and sintering temperature up to $450^{\circ}C$, respectively, the irradiance rate increased in the range of 9~26 percent and 2.80~5.10 percent. Whereas a further increase to $24{\mu}m$ and $550^{\circ}C$, the irradiance rate decrease in the range of 4~11 percent and 30~47 percent. The conversion efficiency increased in the range of 2.80~5.01 and 3.03~5.01 with increasing thickness up to $18{\mu}m$ and sintering temperature up to $450^{\circ}C$. By contrast, increase to $24{\mu}m$ and $550^{\circ}C$, the conversion efficiency decreased in the range of 3.31~5.01 and 2.80~3.89, respectively. The DSSC that thickness of $TiO_2$ were $18{\mu}m$ and sintered at $450^{\circ}C$ exhibited the most excellent characteristics, in which open-circuit voltage, short-circuit current, Fill Factor and conversion efficiency are 0.69 V, $11.4mA/cm^2$, 0.64 and 5.01%, respectively.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.35 no.1
• /
• pp.24-31
• /
• 2022

This study investigated microstructures, crystal structures, polarization, dielectric and electromechanical properties of 0.76Bi_1/2Na_1/2TiO₃-0.24SrTiO₃ (BNT-24ST)-based piezoceramcs by adding Li₂CO₃ and B₂O₃ (LB) as sintering aids for low-temperature sintering. All samples were successfully synthesized using conventional solid-state reaction method and sintered at 950, 1,000, 1,050, 1,100 and 1,175℃ for 2 hours. Without LB, specimens required sintering temperatures over 1,175℃ for sufficient densification, while the addition of 0.10-mol LB decreased the sintering temperatures down to 950℃. The average grain size and dielectric properties of BNT-24ST-10LB ceramics were enhanced with increasing sintering temperature. We found that the low-temperature sintered BNT-24ST piezoceramics by adding LB showed the d₃₃*value of 402 pm/V at 4 kV/mm after sintering at 1,050℃, which was better than that of high-temperature fired specimens sintered at 1,175℃ without LB (242 pm/V). We believe that the results of this study promise a candidate for low-cost multilayer ceramic actuator applications.