• Title/Summary/Keyword: Vapor-solid reaction

Search Result 37, Processing Time 0.025 seconds

Synthesis of Mullite Whiskers by Vapor-Solid Reaction in the System of Al(OH)3-SiO2-AlF3 (Al(OH)3-SiO2-AlF3계에서 기상-고상반응에 의한 뮬라이트 휘스커 합성)

  • Lee, Hong-Lim;Kang, Jong-Bong
    • Journal of the Korean Ceramic Society
    • /
    • v.43 no.6 s.289
    • /
    • pp.376-382
    • /
    • 2006
  • In the $Al(OH)_3-SiO_2-AlF_3$ system, leaf-shaped fluorotopaz was first formed at $800^{\circ}C$ and mullite whisker was formed at $1,100^{\circ}C$. The mass transportation of Al and Si as gas phase, the fast reaction and growth, and the absence of liquid phase existence in mullite whisker showed that the formation and growth of mullite was from the solid-vapor reaction.

Growth of Nano- and Microstructured Indium Nitride Crystals by the Reaction of Indium Oxide with Ammonia

  • Jung, Woo-Sik;Ra, Choon-Sup;Min, Bong-Ki
    • Bulletin of the Korean Chemical Society
    • /
    • v.26 no.9
    • /
    • pp.1354-1358
    • /
    • 2005
  • Nano- and microstructured indium nitride crystals were synthesized by the reaction of indium oxide ($In_2O_3$) powder and its pellet with ammonia in the temperature range 580-700 ${^{\circ}C}$. The degree of nitridation of $In_2O_3$ to InN was very sensitive to the nitridation temperature. The formation of zero- to three-dimensional structured InN crystals demonstrated that $In_2O_3$ is nitridated to InN via two dominant parallel routes (solid ($In_2O_3$)-to-solid (InN) and gas ($In_2O$)-to-solid (InN)). The growth of InN crystals with such various morphologies was explained by the vapor-solid (VS) mechanism where the degree of supersaturation of In vapor determines the growth morphology and the vapor was mainly by the reaction of $In_2O$ with ammonia and partially by sublimation of solid InN. The pellet method was proven to be useful to obtain homogeneous InN nanowires.

Synthesis of Silicon Carbide Whiskers (I) : Reaction Mechanism and Rate-Controlling Reaction (탄화규소 휘스커의 합성(I) : 반응기구의 율속반응)

  • 최헌진;이준근
    • Journal of the Korean Ceramic Society
    • /
    • v.35 no.12
    • /
    • pp.1329-1336
    • /
    • 1998
  • A twt -step carbothermal reduction scheme has been employed for the synthesis of SiC whiskers in an Ar or a H2 atmosphere via vapor-solid two-stage and vapor-liquid-solid growth mechanism respectively. It has been shown that the whisker growth proceed through the following reaction mechanism in an Ar at-mosphere : SiO2(S)+C(s)-SiO(v)+CO(v) SiO(v)3CO(v)=SiC(s)whisker+2CO2(v) 2C(s)+2CO2(v)=4CO(v) the third reaction appears to be the rate-controlling reaction since the overall reaction rates are dominated by the carbon which is participated in this reaction. The whisker growth proceeded through the following reaction mechaism in a H2 atmosphere : SiO2(s)+C(s)=SiO(v)+CO(v) 2C(s)+4H2(v)=2CH4(v) SiO(v)+2CH4(v)=SiC(s)whisker+CO(v)+4H2(v) The first reaction appears to be the rate-controlling reaction since the overall reaction rates are enhanced byincreasing the SiO vapor generation rate.

  • PDF

New Processing of LED Phosphors

  • Toda, Kenji
    • Transactions on Electrical and Electronic Materials
    • /
    • v.13 no.5
    • /
    • pp.225-228
    • /
    • 2012
  • In order to synthesize LED phosphor materials, we have applied three novel synthesis techniques, "melt synthesis", "fluidized bed synthesis" and "vapor-solid hybrid synthesis", in contrast with the conventional solid state reaction technique. These synthesis techniques are also a general and powerful tool for rapid screening and improvements of new phosphor materials.

Synthesis of Silicon Carbide Whiskers (I) : Reaction Mechanism and Rate-Controlling Reaction (탄화규소 휘스커의 합성(I) : 반응기구의 율속반응)

  • 최헌진;이준근
    • Journal of the Korean Ceramic Society
    • /
    • v.35 no.12
    • /
    • pp.1336-1336
    • /
    • 1998
  • A twt -step carbothermal reduction scheme has been employed for the synthesis of SiC whiskers in an Ar or a H2 atmosphere via vapor-solid two-stage and vapor-liquid-solid growth mechanism respectively. It has been shown that the whisker growth proceed through the following reaction mechanism in an Ar at-mosphere : SiO2(S)+C(s)-SiO(v)+CO(v) SiO(v)3CO(v)=SiC(s)whisker+2CO2(v) 2C(s)+2CO2(v)=4CO(v) the third reaction appears to be the rate-controlling reaction since the overall reaction rates are dominated by the carbon which is participated in this reaction. The whisker growth proceeded through the following reaction mechaism in a H2 atmosphere : SiO2(s)+C(s)=SiO(v)+CO(v) 2C(s)+4H2(v)=2CH4(v) SiO(v)+2CH4(v)=SiC(s)whisker+CO(v)+4H2(v) The first reaction appears to be the rate-controlling reaction since the overall reaction rates are enhanced byincreasing the SiO vapor generation rate.

Hg(0) Removal Using Se(0)-doped Montmorillonite from Selenite(IV)

  • Lee, Joo-Youp;Kim, Yong Jin
    • Bulletin of the Korean Chemical Society
    • /
    • v.34 no.12
    • /
    • pp.3767-3770
    • /
    • 2013
  • Potassium methylselenite ($KSeO_2(OCH_3)$) was reduced to elemental selenium, Se(0), and then doped onto montmorillonite K 10 (MK10) clay to examine the interaction between elemental mercury (Hg(0)) vapor and Se(0) in an effort to understand the possible heterogeneous reaction of Hg(0) vapor and Se(0) solid. The clay was used as a cost-effective support material for uniform dispersion of Se(0). The Se(0)-doped MK10 showed an excellent reaction performance with Hg(0) under an inert nitrogen gas at 70 and $140^{\circ}C$ in our lab-scale fixed-bed system. However, the precursor, $KSeO_2(OCH_3)$-doped MK10 showed a negligible reaction performance with Hg(0), suggesting that the oxidation state of selenium plays a key role in the reaction of Hg(0) vapor and selenium compounds.

Vapor-Phase Chlorination of Chlorobenzene over Solid-Acid Catalysts

  • 장향자;최평호;박상언
    • Bulletin of the Korean Chemical Society
    • /
    • v.16 no.6
    • /
    • pp.507-511
    • /
    • 1995
  • Catalytic chlorination of chlorobenzene was studied in vapor phase using various solid-acid catalysts such as silica-alumina, alumina, zeolite and a modified clay prepared by impregnating bentonite with ferric chloride. The conversions of both chlorine gas and chlorobenzene showed high over silica-alumina, alumina and modified clay catalysts. However relatively large amounts of polychlorinated benzene derivatives were also observed. The active species of catalytic activity in chlorination of chlorobenzene in vapor phase were proved to be as Lewis acid sites by in-situ IR experiments. The strength of Lewis acid sites which were effective for the vapor-phase chlorination seemed to be having Hammett acidity Ho >-3.0. The selectivity to dichlorobenzenes was proved to be high over the zeolite catalyst due to their shape-selective properties. p-Dichlorobenzene or dichlorobenzene selectivities were improved more or less by changing the reaction conditions.

Characterization of Mullite Whiskers Synthesized with Compostion of Al(OH)3-SiO2-AlF3 (Al(OH)3-SiO2-AlF3 조성으로 합성된 뮬라이트 휘스커의 특성평가)

  • Lee, Hong-Lim;Kang, Jong-Bong
    • Journal of the Korean Ceramic Society
    • /
    • v.43 no.5 s.288
    • /
    • pp.320-326
    • /
    • 2006
  • Mullite whiskers were synthesized by a vapor-solid reaction with $Al(OH)_3-SiO_2-AlF_3$. The heat treatment temperature did not affect the shape of mullite whisker but the composition change resulted in different sizes. The first one was $30-50{\mu}m$ in size with the aspect ratio of 60 and above, and the second one was $600{\mu}m$ and below in size with the aspect ratio of 15 and below. The $Al_2O_3$ content in formed mullite whisker was 73.57-80.29 wt%, which is high $Al_2O_3$ content composition. The Young's modulus and the hardness measured by nano-indentation method were 136.7 GPa and 19.81 GPa, respectively.

Fabrication of SiC Converted Graphite by Chemical Vapor Reaction Method (화학적 기상 반응법에 의한 탄화규소 피복 흑연의 제조 (I))

  • 윤영훈;최성철
    • Journal of the Korean Ceramic Society
    • /
    • v.34 no.12
    • /
    • pp.1199-1204
    • /
    • 1997
  • SiC conversion layer was fabricated by the chemical vapor reaction between graphite substrate and silica powder. The CVR process was carried out in nitrogen atmosphere at 175$0^{\circ}C$ and 185$0^{\circ}C$. From the reduction of silica powder with graphite substrate, the SiO vapor was created, infiltrated into the graphite substrate, then, the SiC conversion layer was formed from the vapor-solid reaction of SiO and graphite. In the XRD pattern of conversion layer, it was confirmed that 3C $\beta$-SiC phase was created at 175$0^{\circ}C$ and 185$0^{\circ}C$. Also, in the back scattered image of cross-sectional conversion layer, it was found that the conversion layer was easily formed at 185$0^{\circ}C$, the interface of graphite substrate and SiC layer was observed. It was though that the coke particle size and density of graphite substrate mainly affect the XRD pattern and microstructure of SiC conversion layer. In the oxidation test of 100$0^{\circ}C$, the SiC converted graphites exhibited good oxidation resistance compared with the unconverted graphites.

  • PDF

Morphologically Controlled Growth of Aluminum Nitride Nanostructures by the Carbothermal Reduction and Nitridation Method

  • Jung, Woo-Sik
    • Bulletin of the Korean Chemical Society
    • /
    • v.30 no.7
    • /
    • pp.1563-1566
    • /
    • 2009
  • One-dimensional aluminum nitride (AlN) nanostructures were synthesized by calcining an Al(OH)(succinate) complex, which contained a very small amount of iron as a catalyst, under a mixed gas flow of nitrogen and CO (1 vol%). The complex decomposed into a homogeneous mixture of alumina and carbon at the molecular level, resulting in the lowering of the formation temperature of the AlN nanostructures. The morphology of the nanostructures such as nanocone, nanoneedle, nanowire, and nanobamboo was controlled by varying the reaction conditions, including the reaction atmosphere, reaction temperature, duration time, and ramping rate. Iron droplets were observed on the tips of the AlN nanostructures, strongly supporting that the nanostructures grow through the vapor-liquid-solid mechanism. The variation in the morphology of the nanostructures was well explained in terms of the relationship between the diffusion rate of AlN vapor into the iron droplets and the growth rate of the nanostructures.