• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.15 no.2
• /
• pp.190-197
• /
• 2002

In this thesis, ZnO varistors with various formulation, such as A∼E, were fabricated according to ceramic fabrication method. The microstructure, electrical properties, and surge characteristics of ZnO varistors were investigated according to ZnO varistors with various formulation. In the microstructure, A∼E\`s ZnO varistor ceramics sintered at 1130$\^{C}$ was consisted of ZnO grain(ZnO), spinel phase (Zn$\_$2.33/Sb$\_$0.67/O$\_$4/), Bi-rich phase(Bi$_2$O$_3$) and intergranuler phase, wholly. Lightning impulse residual voltage of A, B, C and E\`s ZnO varistors suited standard characteristics, below 12kV at current of 5kA. On the contrary, D\`s ZnO varistor exhibited high residual voltage as high reference voltage. In the accelerated aging test, leakage current and watt loss of B, C and D\`s ZnO varistors increases abruptly with stress time under the first a.c. stress(115$\^{C}$/3.213kV/300h). Consequently, C varistor exhibited a thermal run away. On the contrary, leakage current and watt loss of A and C\`s ZnO varistors which show low initial leakage current exhibited constant characteristics. After high current impulse test, A\`s ZnO varistor has broken the side of varistor but impulse current flowed. On the contrary, E\`s ZnO Varistor exhibited good discharge characteristics which the appearance of varistor was not wrong such as puncture, flashover, creaking and other significant damage. After long duration impulse current test, E\`s ZnO varistor exhibited good discharge characteristics which the appearance of varistor was not wrong such as puncture, flashover, creaking and other significant damage. After high current impulse test and long duration impulse current test, E\`s ZnO varistor exhibited very good characteristics which variation rate of residual voltage is 1.4% before and after test.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1998.06a
• /
• pp.343-346
• /
• 1998

Degradation characteristics of the Pr-based ZnO varistor with $Y_2O_3$content (0.0-4.0 mol!%j were investigated. It was appeared that the variation of the J-E characteristics in the reverse direction before and after the applied stress with increasing $Y_2O_3$ content was larger than that of the forward direction but the variation was extrernly small. For all varistor, the leakage current with the stress time during the applied stress somewhat increased initialy but afterthat was almost constant or slightly decreased. The overall varistor voltage and nonlinear coefficient were less than 5%. Especially, in the case of Pr-based ZnO varistor containing 2.0 mol% to 4.0 mol% $Y_2O_3$, the variation of breakdown voltage and nonlinear coefficient was less than 1% and 5%. respectively. As a result, they showed good stability.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.07b
• /
• pp.629-633
• /
• 2002

The degradation behaviour of ZPCCL-based varistor ceramics composed of 97.5 mol%ZnO-0.5 mol% $Pr_6O_{11}-1.0$ mol% $Cr_2O_3-0.5$ mol% $La_2O_3$ was investigated under various DC accelerated aging streses. The varistor ceramics sintered for 1 h exhibited excellent nonlinearity, in which the nonlinear exponent is 81.6 and the leakage current is $0.2{\mu}A$. It was found that this varistor ceramics possess high stability, in which the variation rates of varistor voltage, nonlinear exponent, and leakage current are -1.14%, -3.7%, and 85.0%, respectively, against DC accelerated aging stress. On the contrary, the varistor ceramics sintered for 2 h also exhibited high nonlinearity and stability, but they were bad characteristics, compared with the varistor ceramics sintered for 1 h.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1999.05a
• /
• pp.312-316
• /
• 1999

I-V characteristics of Praseodymium-based ZnO varistor doped with $Nd_2O_3$ in the range 0.0-2.0mol% sintered at 130$0^{\circ}C$ and 135$0^{\circ}C$ were investigated. In the all sides, ZnO varistors sintered at $1300^{\circ}C$ exhibited much better varistor characteristics than that at 135$0^{\circ}C$. All ZnO varistors doped with $Nd_2O_3$ sintered at $1300^{\circ}C$ exhibited good varistor characteristics but particularly ZnO varistor doped with l.Omol% $Nd_2O_3$ exhibited the best characteristics, which the nonlinear is 65.2 and the leakage current is 4.5pA. It is estimated that ZnO varistor doped with l.Omol% $Nd_2O_3$ will begin to be sufficiently used as basic composition to fabricate a good varistor.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.07b
• /
• pp.1106-1110
• /
• 2003

The electrical characteristics of $A{\sim}C's$ ZnO varistors fabricated according to variable sintering condition, which sintering temperature is $l130^{\circ}C$ and speeds of pusher are A: 2mm/min, B: 4mm/min, C: 6 mm/min, respectively, were investigated. The varistor voltage of $A{\sim}C's$ ZnO varistors sintered at $1130^{\circ}C$ increased in order A < B $A{\sim}C's$ ZnO varistors exhibited below 2mA at rated voltage. Lightning impulse residual voltage of A's ZnO varistor suited standard characteristics, which is 3.85kV at 2.5kA, 4.4kV at 5kA and 5.16kV at 10kA. After multi lightning impulse residual voltage test of A's ZnO varistor exhibited good discharge characteristics which ZnO varistor reveals no evidence of puncture, flashover, cracking in visual examination. After high current impulse test of A's ZnO varistor exhibited good discharge characteristics, which variation rate of residual voltage is 0.4% before and after test, and revealed no evidence.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.19 no.9
• /
• pp.862-867
• /
• 2006

Bi-based nano-varistors and micro-varistors fabricated with each ZnO nano-powder and micro-powder were studied about characteristics on the surge capability in this study. ZnO nano-varistors were sintered in air at $1050^{\circ}C$ for 2 hr. The voltage-current and residual voltage properties of ZnO nano-varistor were compared with their of ZnO micrio-varistor. As a result of these properties, our ZnO nano-varistor has about 3 times at operating voltage as compared with conventional ZnO varistor fabricated with micro-powder and the residual voltage was 8.06 kV at nominal discharge current 101kA in the lighting impulse current test. And then the residual voltage rate 1.72 of our nano-varistor has had better performance than the 1.79 of micro-varistor because ZnO nano-varistor has shown much quick response property because of increasing effective cross-section area. Also, to analysis surge capability took thermal images for pyrexia temperature distribution with each of the varistors after operating varistors. Nano-varistor doesn't have shown local overheating and can confirm accurate temperature grade on the surface of its.

• Proceedings of the KIEE Conference
• /
• 1999.07e
• /
• pp.2161-2163
• /
• 1999

Generally, ZnO varistors have dynamic characteristics that the cut-off voltage increases as the time to crest of the varistor current decreases. Dynamic characteristics of ZnO varistor are the most important factor in region of the steep front discharge current particularly. Also, V-I characteristics of ZnO varistor have hysterisis loop in time domain and frequency dependency. This paper deals with ZnO varistor numerical equation and modeling method which takes the behavior of varying clamping voltage into consideration during the time to crest, in range of $1{\mu}m{\sim}50{\mu}m$, of impulse current applied to a ZnO varistor. The simulated results by the proposed model are compared with experimental results for each of the impulse current.

• Transactions on Electrical and Electronic Materials
• /
• v.15 no.6
• /
• pp.348-352
• /
• 2014

In light of the sure protection function, the most important factors of a varistor are the clamping voltage ratio and degradation characteristics. The degradation characteristics of Pr/Co/Cr/Er co-doped zinc oxide varistors were investigated by impulse currents (0.4~2.1 kA) stress for the specified content of $Er_2O_3$ (0.5 and 2.0 mol%). The varistor doped with 2.0 mol% $Er_2O_3$ exhibited the best clamp characteristics, with the clamp voltage ratio (K) in the range of K = 1.63~1.88 at the impulse currents of 5-50 A. However, the varistor doped with 0.5 mol% exhibited excellent electrical stability, with variation rates for the breakdown field, for the nonlinear coefficient, and for the leakage current density of -6.9%, -12.6%, and -14.3%, respectively, after application of an impulse current of 2.1 kA. In contrast, the varistor doped with 2.0 mol% was destroyed after application of an impulse current of 1.2 kA.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.11 no.10
• /
• pp.842-848
• /
• 1998

The stability of paraseodymium-based zinc oxide varistor consisting of Zn-Pr-Co-Cr-Y oxide was investigated according to yttria additives under different stress conditons, such as 0.8V\ulcorner\ulcorner/373K/12h and 0.85V\ulcorner\ulcorner/393K/12h. Wholly, all varistor after the stress showed nearly symmetric and stable I-V characteristics. Particularly, in the case of 2.0mol% and 4.0mol% yttria-added varistor showing a good I-V characteristics, the varation rate of varistor voltage were less 1% and that of nonlinear coefficient were about degree of 5%, and what is remarkable, leakage current with increasing stress time during the applied stress was almost constant. It the light of these facts, it is estimated that varistor constituents having 2.0mol% and 4.0mol% yittria, respectively, will be utilized to various application fields.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.11a
• /
• pp.552-556
• /
• 2002

The microstructure and electrical characteristics of A~C's ZnO varistors fabricated according to variable sintering condition, which sintering temperature is $1130^{\circ}C$ and speeds of pusher are A: 2mm/min, B: 4mm/min, C: 6mm/min, respectively, were investigated. In the microstructure, A~C's ZnO varist-ors fabricated variable sintering condition was consisted of ZnO grain(ZnO), spinel phase$(Zn_{2.33}Sb_{0.67}O_4)$ Bi-rich $phase(Bi_{2}O_{3})$, wholly. Varistor voltage of A~C's ZnO varistors sintered at $1130^{\circ}C$ increased in order A < B < C's ZnO varistors. C's ZnO varistor exhibited good characteristics that nonlinear exponent is 31.70. Leakage current of A~C's ZnO varistors exhibited below 2mA at rated voltage. Lightning impulse residual voltage of A's ZnO varistor suited standard characteristics, which is 3.85kV at 2.5kA, 4.4kV at 5kA and 5.16kV at 10kA. After multi lightning impulse residual voltage test of A's ZnO varistor exhibited good discharge characteristics which ZnO varistor reveals no evidence of puncture, flashover, cracking in visual examination. After high current impulse test of A's ZnO varistor exhibited good discharge characteristics, which variation rate of residual voltage is 0.4% before and after test, and revealed no evidence.