• Journal of the Korean Society of Marine Environment & Safety
• /
• v.3 no.2
• /
• pp.13-21
• /
• 1997

This paper describes the effectiveness of laser pulse shaping in eliminating weld defects such as porosity, cracks and undercuts in pulsed Nd:YAG Laser welding. A large porosity was formed in a keyhole mode of deep penetration weld metal of any stainless steel. Solidification cracks were present in Type 303 with about 0.3%s. The conditions for the formation of porosity were determined in further detail in Type 316. With the objectives of obtaining a fundamental knowledge of formation and prevention of weld defects, the fusion and solidification behavior of a molten puddle was observed during laser spot welding of Type 310S. through high speed video photographing technique. It was deduced that cellular dendrite tips grew rapidly from the bottom to the surface, and consequently residual liquid remained at the grain boundaries in wide regions and enhanced the solidification cracking susceptibility. Several laser pulse shapes were investigated and optimum pulse shapes were proposed for the reduction and prevention of porosity and solidification cracking.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.2 no.1
• /
• pp.98-107
• /
• 1998

There are many weld defects such as surface crack, lack of fusion, and imcomplete penetration in the butt joint of the existing steel bridges. The crack-like defects may significantly reduce the fatigue life of the structure. This paper presents the procedure and the results of the fatigue assessment of the butt joints with weld defect in the existing steel girder bridge. The butt joints with imcomple penetration were instrumented with strain gages to determine the stress histogram under normal traffic. Based on the measured stress histogram the crack propagation analyses were performed for the fatigue assesment. By using the suggested procedure and methodology, one can decide the time of periodic inspection and the necessity of repair of the butt joints with serious weld defects in the existing steel bridge.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.18 no.10
• /
• pp.34-41
• /
• 2019

Warpage and weld line are two major cosmetic defects in the injection molding process. These defects are very sensitive to uncontrollable parameters within the process. The optimization of the design variables can be treated with the use of robust designs. Therefore, in order to minimize the warpage and weld line, a special design method to diminish defects is required. In this study, a new robust design method using designer preference to achieve the optimal robust design conditions in the injection molding process is proposed. The effectiveness of the proposed method is shown with an example of the part of warpage and weld line.

• Journal of Ocean Engineering and Technology
• /
• v.24 no.4
• /
• pp.38-46
• /
• 2010

The wall thinning phenomenon of pipes was simulated as metal loss due to erosion and corrosion. Such wall thinning defects in the pipes of power plants are a very important safety consideration. In this study, we analyzed wall thinning defects that occurred by weld bead of weld zone of boost pump recirculation pipe. From the results of the analysis of pipe failures, numerical analysis was performed by Fluent v6.3.26 using the standard k-$\varepsilon$ model of the weld bead shape, such as an elliptical or a spherical shape, on the inner wall of the pipe. Using the results obtained, we showed the overlap effect by cavitations corrosion and erosion-corrosion at the bottom of the wall-thinning defect.

• Journal of Welding and Joining
• /
• v.34 no.4
• /
• pp.55-61
• /
• 2016

During laser overlap welding of galvanized steel sheets, explosion of weld pool by the high pressure zinc vapor induces weld defects like porosity and blowhole. In this study, laser 2-pass welding was implemented to prevent the weld defects. Through the 1st pass welding, zinc layers on the faying surfaces were removed when proper heat input was applied. Excessive heat input could result in explosion even during the 1st pass welding and insufficient heat input could not remove enough region of zinc layer for the 2nd pass welding. Coating weights of $45g/m^2$ and $60g/m^2$ were considered and for both cases sound welds without weld defects could be achieved. In spite of 2-pass welding, softening of weld and heat affected zone was not observed and Zn coating was not diluted into the weld metal.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.11 no.5
• /
• pp.129-136
• /
• 2012

On this study, $CO_2$ gas, net of Ar gas, and mixed gas in solid wire(AWS ER 70S-6) and flux cored wire(AWS E71T-1) were used to weld on Mild steel(SS400). After the progress, the status changes of the welds in Mild steel(SS400) were investigated with compositional changes. For stable experiments, welding was conducted using the automatic feeder. Radiation testing, hardness testing, chemical composition analysis and penetrated cross-section were measured. Through these experiments, shapes of penetrated cross-section, chemical composition changes, and weld defects according to the variation of welding gas were known. Weld defects and weld cross-sectional shapes by the variation of the welding voltage were also detected.

• Design & Manufacturing
• /
• v.9 no.2
• /
• pp.30-33
• /
• 2015

In injection molding, many kinds of defects have occurred because of a characteristic of plastics injection molding. Weld line is one of the defects is formed when separated melt fronts recombine together during the mold filling stage. That is one of problems in injection molding. Weld lines in the appearance of plastics parts can deteriorate visible quality. And most importantly, the local mechanical strength in the weld line area can be significantly weaker. It could be one of the most problems for structural applications. In this study, the mold available two-shot-molding of same polymers have been designed, and a series of experiment about tensile strength in weld line area has been conducted using Taguchi's design of experiment to optimize injection molding conditions decreasing of weld strength and find out a factors affected weld strength in two-shot- molding.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.23 no.7 s.166
• /
• pp.1065-1074
• /
• 1999

This study proposes the analysis and evaluation method of time series ultrasonic signal using the chaotic feature extraction for ultrasonic pattern recognition. Features extracted from time series data using the chaotic time series signal analysis quantitatively welding defects. For this purpose analysis objective in this study is fractal dimension and Lyapunov exponent. Trajectory changes in the strange attractor indicated that even same type of defects carried substantial difference in chaoticity resulting from distance shills such as 0.5 and 1.0 skip distance. Such differences in chaoticity enables the evaluation of unique features of defects in the weld zone. In experiment fractal(correlation) dimension and Lyapunov exponent extracted from 6dB ultrasonic defect signals of weld zone showed chaoticity. In quantitative chaotic feature extraction, feature values(mean values) of 4.2690 and 0.0907 in the case of porosity and 4.2432 and 0.0888 in the case of incomplete penetration were proposed on the basis of fractal dimension and Lyapunov exponent. Proposed chaotic feature extraction in this study enhances ultrasonic pattern recognition results from defect signals of weld zone such as vertical hole.

• Journal of Welding and Joining
• /
• v.15 no.3
• /
• pp.88-98
• /
• 1997

Welding defects, such as porosity and spike, have sometimes occurred in deep penetration electron beam welds. These defects are known to be one of the serious problem in electron beam welds. So, effects of active parameters ($a_b$) on bead shape and occurrence of defects in electron beam welds of heavy section 9%Ni steel plates were investigated. Partial penetration welding in flat position, and deep penetration welding of 10 ~ 28mm depth were investigated in this study. It is desirable to select low accelerating voltage and above the surface focus position $a_b$$\geq$1.2 at which a wine-cup shaped bead is obtained to avoid the welding defects such as spike and root porosity. When the accelerating voltage of electron beam was low (90kV), active parameter ($a_b$) did not influence on the bead width, penetration depth and weld defects significantly. However, in case of high voltage ($\geq$120kV), active parameter ($a_b$) was sensitively associated with penetraton depth and weld defects, i.e. when the active parameter (($a_b$) was in the range of 0.6 to 1.0, the depth of penetration was always over the target (23mm), while the depth of penetration was dramatically decreased with further increase of active parameter ($a_b$). The weld defects were decreased with the increase of active parameter $a_b$ resulting in the decrease of energy density of the focused beam in the root part of fusion zone.

• Proceedings of the Korean Institute of Intelligent Systems Conference
• /
• 1997.10a
• /
• pp.189-193
• /
• 1997

Generally, though we use the vision sensor or arc sensor in welding process, it is difficult to define the welding parameters which can be applied to the weld quality control. Especially, the important parameters is Arc Voltage, Welding Current, Welding Speed in arc welding process and they affect the decision of weld bead shape, the stability of welding process and the decision of weld quality. Therefore, it is difficult to determine the unique relationship between the weld bead geometry and the combination of various welding condition. Due to the various difficulties as mentioned, we intend to use Fuzzy Logic and Neural Network to solve these problems. Therefore, the combination of Fuzzy Logic and Neural network has an effect on removing the weld defects, improving the weld quality and turning the desired weld bead shape. Finally, this system can be used under what kind of welding process adequately and help us make an estimate of the weld bead shape and remove the weld defects.