• Applied Chemistry for Engineering
• /
• v.8 no.4
• /
• pp.637-639
• /
• 1997

Samples of $YTa_7O_{19}$ doped with $Tm^{3+}$ were prepared using the solid state reaction method to investigate their photoluminescence characteristics. The samples were identified by XRD and SEM, and the optical measurement was also carried out. Under 359 nm excitation, $YTa_7O_{19}$ doped with $Tm^{3+}$ exhibited a narrow-band blue emission, at about 455 nm. The maximum emission intensity was obtained at $YTa_7O_{19}$ doped with 0.12 mole $Tm^{3+}$. This revealed the concentration quenching of emission intensity.

• The Korean Journal of Ceramics
• /
• v.3 no.1
• /
• pp.43-46
• /
• 1997

Thulium (Tm) has been incorporated into $YAlO_3$ and $YTa_7O_{19}$ host materials to obtain blue phosphors. $Tm^{3+}$-doped $YAlO_3$ and $YTa_7O_{19}$ phosphors were prepared by the conventional solid state reaction method. According to the results of excitation and emission spectra measured at room temperature, the blue emission intensity of $Tm^{3+}$-doped $YTa_7O_{19}$, peaking at 455 nm was much higher than that of $Tm^{3+}-doped\; YAlO_34, peaking at 458 nm. The maximum of relative intensity of $Tm^{3+}-doped\; YAlO_3\; and\; YTa_7O_{19}$ was obtained at the doping concentration of 0.016 and 0.120 mol% $Tm^{3+}$, respectively. These emission spectra revealed the concentration quenching effect.