• Fashion & Textile Research Journal
• /
• v.21 no.1
• /
• pp.96-103
• /
• 2019

The objective of this study is to analyze the development trends of aerogel daily clothing through market research, and to discuss the main points of future aerogel application in daily clothing. Market research on daily clothing has been conducted by collecting relevant information on the internet and analyzing the content of the information. We summarized the market research results in three aspects: the daily clothing brand using aerogel, the aerogel composite used in daily clothing, and the property of aerogel daily clothing. From these results, it can be seen that the development of aerogel daily clothing is becoming active and specialized. But there are still many difficulties due to lack of development experience. One problem is that the application methods of aerogel composite in current aerogel daily clothing are similar. Another problem is that the analysis of consumer reviews can only provides a rough understanding of the property of aerogel daily clothing. Therefore, further application research of aerogel composite in the field of daily clothing through scientific evaluation is required. It is expected to improve the performance of the aerogel daily clothing and increase the utilization of aerogel composite by conducting the further application research.

• Korean Journal of Materials Research
• /
• v.30 no.4
• /
• pp.155-159
• /
• 2020

Nanoporous silica aerogel insulation material is both lightweight and efficient; it has important value in the fields of aerospace, petrochemicals, electric metallurgy, shipbuilding, precision instruments, and so on. A theoretical calculation model and experimental measurement of equivalent thermal conductivity for nanoporous silica aerogel insulation material are introduced in this paper. The heat transfer characteristics and thermal insulation principle of aerogel nano are analyzed. The methods of SiO₂ aerogel production are compared. The pressure range of SiO₂ aerogel is 1Pa-atmospheric pressure; the temperature range is room temperature-900K. The pore diameter range of particle SiO₂ aerogel is about 5 to 100 nm, and the average pore diameter range of about 20 ~ 40 nm. These results show that experimental measurements are in good agreement with theoretical calculation values. For nanoporous silica aerogel insulation material, the heat transfer calculation method suitable for nanotechnology can precisely calculate the equivalent thermal conductivity of aerogel nano insulation materials. The network structure is the reason why the thermal conductivity of the aerogel is very low. Heat transfer of materials is mainly realized by convection, radiation, and heat transfer. Therefore, the thermal conductivity of the heat transfer path in aerogel can be reduced by nanotechnology.

• Textile Coloration and Finishing
• /
• v.25 no.4
• /
• pp.279-286
• /
• 2013

Application properties of ultra light weight silica aerogel toward polyurethane membranes were investigated. From the results of pre-milling process of the silica aerogel, the solvent for dispersion of the aerogel was determined for methyl ethyl ketone and its content in the solvent was determined by 30%. Using this aerogel dispersion, the polyurethane membranes were prepared according to the mixing amount of silica aerogel and various properties of the membranes were investigated. As results, the optimum mixing amount of silica aerogel inside polyurethane membranes was decided at 11%, because the improvement of light weight property, air permeability, and moisture vapor permeability were improved upto 11% of silica aerogel content, maintaining the water penetration resistance almost unchanged.

• Journal of the Korean Applied Science and Technology
• /
• v.27 no.3
• /
• pp.282-289
• /
• 2010

In preparation of silica aerogel-based hybrid coating materials, the combination of hydrophobic aerogel with organic polar binder material is shown to be very limited due to dissimilar surface property between two materials. Accordingly, the surface modification of the aerogel would be required to obtain compatibilized hybrid coating sols with homogeneous dispersion. In this study, the surface of silica aerogel particles was modified by using both surfactant adsorption and heat treatment methods. Four types of surfactants with different molecular weights and HLB values were used to examine the effect of chain length and hydrophilicity. The surface property of the modified aerogel was evaluated in terms of visible observation for aerogel dispersion in water, water contact angle measurement, and FT-IR analysis. In surface modification using surfactants, the effects of surfactant type and content, and mixing time as process parameter on the degree of hydrophilicity for the modified aerogel. In addition, the temperature condition in modification process via heat treatment was revealed to be significant factor to prepare aerogel with highly hydrophilic property.

• Journal of the Korean Society of Clothing and Textiles
• /
• v.33 no.5
• /
• pp.701-710
• /
• 2009

This study was conducted to develop excellent insole with good thermal insulation using new materials. We investigated that aerogel/fiber composite can be used as padding materials of shoes by comparing surface shape, moisture regain, water vapor permeability, thermal insulation and compression rate of insole materials tried with nonwoven fabric padding materials and insole sold in market. The results are as follows. Surface shapes were shown that the most appropriate material for sealing aerogel/fiber composite was high density fabric as per size of particle of aerogel. Moisture regain of aerogel/fabric composite was better than nonwoven fabric padding samples. However, when compared to insole sold in market, its moisture regain was worse than those of insole merchandises. Water vapor permeability was higher in material padded with nonwoven fabric than materials padded with aerogel/fiber composite in all three kinds of sealing fabrics. Thermal conductivity of aerogel/fabric composite was lower than nonwoven fabric material regardless of sealing fabrics. Thermal insulation of aerogel/fiber composite was higher than padding material of nonwoven fabric regardless of sealing fabrics. Compression rate of nonwoven (SP1) was higher than that of aerogel/fiber composite (SP2). Compressive elastic recovery rate of SP1 was also higher than that of SP2, which its compression rate and compressive elastic recovery rate were both poor. As the above result, ultra porous aerogel/fiber composite were proved to be material of good thermal insulation with lower thermal conductivity and also compression rate was proved to be low. Therefore, we can say that aerogel/fiber composite have high possibility to be used as insole materials for cold winter shoes requiring good thermal insulation protection.

• Journal of the Microelectronics and Packaging Society
• /
• v.26 no.2
• /
• pp.23-29
• /
• 2019

Thermally expandable microsphere and aerogel composite was prepared by chemical compositization. Microsphere can produce synergies with aerogel, especially an enhancement of mechanical property. Through condensation between sulfonated microsphere and hydrolyzed silica sol, chemically-connected composite aerogel could be prepared. The presence of hydroxyl group on the sulfonated microsphere was observed, which was the prime functional group of reaction with hydrolyzed silica sol. Silica aerogel-coated microsphere was confirmed through microstructure analysis. The presence of silicon-carbon absorption band and peaks from composite aerogel was observed, which proved the chemical bonding between them. A relatively low thermal conductivity value of $0.063W/m{\cdot}K$ was obtained.

• Journal of Ceramic Processing Research
• /
• v.20 no.1
• /
• pp.30-34
• /
• 2019

Copper (Cu)-incorporated silica aerogel was synthesized by a sol-gel process with two-step drying process for color modification. The microstructure of the silica aerogel was not affected significantly by the Cu concentration and an amorphous structure was maintained without any crystalline impurity phases. The textural properties of the silica aerogels investigated by using N2 adsorption-desorption isotherms exhibited the typical features of mesoporous materials. The pore size and porosity were not changed significantly even with the incorporation of Cu up to 1.5 M, which indicates negligible variation of thermal insulating properties. However, the color of the aerogel changed from white and light greenish to dark greenish with increasing Cu content. The color change of the silica aerogel was due to the modification of the electron energy band structure of silica by the Cu atomic levels. Therefore, the color of the silica aerogel powders could be manipulated by incorporating Cu without degrading the thermal insulating properties.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.16 no.10
• /
• pp.6816-6822
• /
• 2015

In this study, silica aerogel-glass wool composites were developed for improvement of thermal conductivity and overcoming the water adsorption of glass wool boards. Silica aerogel-glass wool composites were prepared by glass wool and silica aerogel with liquid binder. Mixtures with binder were composed of CMC (carboxymethyl cellulose) and silica aerogel for glass wool board. Silica aerogel-glass wool composite boards were had $0.065g/cm^3$ density by impregnation silica aerogel where from origin glass wool board at $0.048g/cm^3$ density. Thermal conductivity of silica aerogel-glass wool composites were 0.0315 W/mK (up to 7.4% thermal resistance) and fire penetration time came to 362 seconds (up to 2.7 times stronger than origin glass wool board). In addition, hydrophobic aerogel characteristics prevented the adsorption of water onto silica aerogel-glass wool composite boards that was good for lightweight.

• Journal of Energy Engineering
• /
• v.21 no.1
• /
• pp.43-46
• /
• 2012

A fluidized bed drying approach was utilized to the synthesis of water glass based silica aerogel powders. The effects of the fluidized bed drying conditions such as the superficial velocity and temperature of hot air and bead size as well as bead/wet-gel ratio, on the physical properties such as tapping density and productivity of the aerogel powders were systematically investigated. The experimental results showed that the amount of beads mixed with wet-gels in the fluidized bed column has the most profound impact on the fluidization efficiency, greatly enhancing the yield of the aerogel powders up to 98% with a proper bead/wet-gel weight ratio as compared to 72% without using beads. No significant change was observed in the tapping density over a wide range of the fluidized drying condition. Consequently the fluidized bed drying approach shows a good promise as an alternative route for the large-scale production of the aerogel powders.

• Journal of the Korean Wood Science and Technology
• /
• v.38 no.3
• /
• pp.205-212
• /
• 2010

This study was carried out to investigate the characterization of aerogel made by holocellulose, the thermal properties of the aerogel, and its shapes and porous structures. The aerogel was made by holocellulose through the gelation in alkali hydroxide-urea solution and freeze drying processes. Holocellulose aerogel had porous structure such as net or sponge. The density of holocellulose aerogel was 0.04 g/$cm^3$, and the specific surface area 145.3 $m^2$/g. Although thermal degradation occurred in the range of $210{\sim}350^{\circ}C$, significant thermal degradation occurred at low temperature with low heating rate, Micropore volume was sharply increased with low heating rate. Holocellulose aerogel char obtained by carbonization with $900^{\circ}C$ and $0.5^{\circ}C$/min. heating rate had the highest surface area, 656.7 $m^2$/g. The deformed and irregular structures of holocellulose aerogel chars due to the thermal degradation were observed in SEM.