• 한국결정성장학회지
• /
• 제15권6호
• /
• pp.269-275
• /
• 2005

Ni/Ni-aluminide//Ti/Ti-aluminide 경사기능 층상 복합재료를 박막 hot press법을 이용하여 제작하였다. NiAl과 $TiAl_3$ 금속간화합물 층이 자전고온합성반응을 통해 비교적 두껍게 형성되었고, 얇고 연속적인 $Ni_3Al$과 TiAl 층이 고상 확산을 통해 형성되었다. 파괴저항은 하중 방향이 crack arrester인 경우가 금속 층이 균열의 성장을 방해하기 때문에 crack divider 방향인 경우보다 높다. $Ni_3Al$과 NiAl 금속간화합물 층은 각각 벽개파괴와 입계파괴 거동을 보였고, $TiAl_3$층의 파괴 형태는 입내벽개파괴이었다. Ni/Ni-aluminide 층에서 관찰되는 기공과 금속 층과 금속간화합물 층의 미결합 부위가 낮은 파괴저항의 원인으로 판단된다. Acoustic emission (AE) 원파형 해석을 통해 제작된 복합재료의 파괴특성을 고찰하였다.

• The Korean Journal of Ceramics
• /
• 제4권1호
• /
• pp.43-46
• /
• 1998

We have investigated the formation and thermal stability of cobalt aluminide(CoAl) thin films on GaAs. In order to obtain cobalt-aluminide thin films, we deposited a multilayer of Co/Al on GaAs, and subsequently annealed the samples at 80$0^{\circ}C$ for 30 min. After annealing, single-phase cobalt aluminide was produced showing a flat and uniform interface with GaAs. which indicates that cobalt aluminide (CoAl) is thermally stable with GaAs. In addition, the adherence and mechanical properties of the as-deposited, and annealed Co/Al multilayer structure on GaAs are compatible with those required for device fabrication processes. The electrical property of the CoAl/GaAs contact shows rectifying characteristics, indicating that the diodes were usable as rectifying gate electrodes.

• 한국표면공학회지
• /
• 제20권3호
• /
• pp.95-105
• /
• 1987

For the purpose of improving the hot corrosion resistance of Ni-base superalloy, Inconel 600, aluminide and chromium-aluminide coatings by pack cementation process were studied. The morphology of these coatings is dependent on the type of process employed. And their overall composition depends on the composition of the base alloy and on the nature of the cement. Therefore the different aluminide and chromium-aluminide coatings obtained on a superalloy do not possess the same resistance to oxidation and hot corrosion. The mechanisms governing the formation of the coatings and the composition of the coating were varied by pack composition and temperature, and cyclic hot corrosion resistance of the auluminide coating formed by one-step process was inferior to that of the coating formed by two-step process. and Cr-Al composite coating showed good resistance for cyclic hot corrosion.

• 열처리공학회지
• /
• 제19권2호
• /
• pp.103-108
• /
• 2006

Microstructural evolution of Pt-aluminide coated Ni-based superalloy has been investigated with ductilization heat treatment. The Pt coat was prepared on the superalloy and then aluminide coating was conducted using a pack cementation process. Samples were heat-treated at $1050^{\circ}C$ for 2 hrs and the microstructure and element analysis were preformed. A various precipitated compounds were observed within the coating layer and the diffusion region in the Pt-aluminide coating and heat treatment, indicating that the bi-phase compounds of $PtAl_2$ and NiAl were performed during the Pt-aluminide coating, whereas $M_{23}C_6$, MC, $Ni_3Al$ and ${\sigma}$ phases were precipitated in the inter-diffusion region. The bi-phase compounds of $PtAl_2$ and NiAl were transformed into the single phase compound of $PtAl_2$ with the heat treatment, increasing the amount of carbide and ${\sigma}$ phase.

• 한국주조공학회지
• /
• 제17권2호
• /
• pp.195-206
• /
• 1997

AC8A matrix composites reinforced with Ni-aluminide were fabricated by squeeze casting process, and the characteristics and nature of the growth of Ni-aluminide phases at the interface between nickel and aluminurn were investigated. In the as-cast composites, the reaction layer between Ni skeleton and aluminum matrix was found to be $NiAl_3$, regardless of the casting temperatures and the kinds of preforms. During high temperature solution treatment the $NiAl_3$ layer grew and formed new $Ni_2Al_3$ layer. Because of presence of the porosity formed by Kirkendall effect at the interface between $NiAl_3$ and aluminum matrix, the tensile strength of composites was inferior to that of AC8A matrix alloy. However, the composites exhibited superior wear resistance due to the formation Ni-aluminide intermetallic phases. Composite A, of which Ni skeleton was fully transformed into Ni-aluminide, shows better wear resistance than that of composite B which still possessed some unreacted Ni skeleton.

• Corrosion Science and Technology
• /
• 제15권6호
• /
• pp.259-264
• /
• 2016

With a specially designed electrochemical cell, the changes in impedance behavior for Inconel 600 and aluminide diffusion coatings under molten sulfate film with thermal cycles (from $800^{\circ}C$ to $350^{\circ}C$) were monitored with electrochemical impedance measurements. It was found that corrosion resistance for both materials increased with lower temperatures. At the same time, the state of molten salt was also monitored successfully by measuring the changes in impedance at high frequency, which generally represents the resistance of molten salt itself. After two thermal cycles, both Inconel 600 and aluminide diffusion coatings showed excellent corrosion resistance. The results from SEM observation and EDS analysis correlated well with the results obtained by electrochemical impedance measurements. It is concluded that electrochemical impedance is very useful for monitoring the corrosion resistance of materials under molten salt film conditions even with thermal cycles.

• 한국표면공학회지
• /
• 제20권2호
• /
• pp.60-73
• /
• 1987

For the purpose of improving the cyclic oxidation resistance of Ni-base superalloy, Inconel 600, aluminide coating methods are studied. The formation rate of aluminide coating layers is measured as a function of time and pack composition to find out the optimum coating condition. The evaluation of cyclic oxidation is established by the change in weight, the microphotography and EPMA of cross sectional area during $200^{\circ}C\;{\leftrightarrow}\;950^{\circ}C\;and\;200^{\circ}C\;{\leftrightarrow}\;1100^{\circ}C$, respectively. The thickness of coating layer and weight gains are parabolic behavior in propotion to time and Al contents. In pack of low aluminum contents, 2 wt%, however, weight gain is decreased when activator, $NH_4Cl$ is higher than 2 wt%. The cyclic oxidation resistance of the coating carried out at 1100$^{\circ}C$ are superior to those of the coating diffusion-treated after pack cementation at 800$^{\circ}C$. Aluminide oxide, which is formed in external scale, is barrier to the cyclic oxidation.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 1994년도 추계학술대회강연 및 발표대회 강연및 발표논문 초록집
• /
• pp.25-25
• /
• 1994

• 한국표면공학회지
• /
• 제29권6호
• /
• pp.607-614
• /
• 1996

Yttrium(Y) coating was incorporated by ion-plating method either directly on the TiAl substrate or after pack aluminizing on TiAl to improve the oxidation resistance of TiAl alloy. After Y-coating, heat treatment at low oxygen partial pressure was carried out. Performance of various coating was evaluated by isothermal and cyclic oxidation tests. A simple Y-coating without pack aluminizing can give a detrimental effect on the. oxidation resistance of TiAl alloy, because it enhances formation of $TiO_2$. On the other hand, a composite coating of aluminide-yttrium has shown excellent oxidation resistance. A continuous protective $Al_2O_3$ scale is formed on the aluminized TiAl, and Y-coating improves $Al_2O_3$ scale adherence and substantially prevents depletion of Al in the aluminide-coating layer.

• 한국표면공학회지
• /
• 제28권3호
• /
• pp.152-163
• /
• 1995

A theoretical model which combines gaseous transport and solid state diffusion with the multi-component equilibrium at the gas/pack and gas/coating interfaces was used to study the kinetics of diffusion aluminide coating. The diffusion aluminide coatings were applied by pack cementation with Ni substrate under argon atmosphere in the high activity and the low activity pack containing $NH_4CL$ or $AlF_3$ activator. On the basis of the process conditions, the suggested model allows the surface composition, the growth rate of coating layers and the aluminium concentration profiles in coatings to be calculated. In the case of $NH_4$Cl activator, careful consideration was required in the analysis, because activator contains nitrogen and hydrogen as well as halogen element to activate the pack. A good agreement is obtained between the theoretical predictions and the experimental results.