• Elastomers and Composites
• /
• v.58 no.4
• /
• pp.179-190
• /
• 2023

The effect of the particle size and silica structure on the wear behavior of Silica/Styrene-Butadiene Rubber (SBR) compounds was investigated using a blade-type abrader and the findings were compared with those obtained with an Akron abrader. The compensated characteristic parameter (Ψ_c), which was the contributory factor of the combined effect of the particle size and filler structure, was introduced. This parameter was found to exhibit a linear relationship with the Young's modulus. The Young's modulus correlated more with Ψ_c than the uncompensated characteristic parameter (Ψ) modeled for carbon black. The wear rate and volume loss measured using a blade-type abrader and Akron abrader were respectively observed to be inversely proportional to Ψ_c, that is, the wear resistance of Silica/SBR compound improved as the particle size became smaller and the silica structure became intricate. The coefficient of determination (R²) obtained from the linear relationship between Ψ_c and wear rate was higher than those between Ψ_c and volume loss for the Silica/SBR compound. Thus, the blade-type abrader exhibited high potential to be used for accurately evaluating the effect of particle size and structural properties of silica on the wear behavior of SBR compounds.

• Elastomers and Composites
• /
• v.49 no.1
• /
• pp.73-81
• /
• 2014

Friction and wear behaviors of natural rubber(NR) compounds were investigated using a blade-type abrader. The effects of temperature, normal load, and rotation speed on wear rate were studied, and wear behaviors of deteriorated compounds were also evaluated. As the rotation speed of specimen and the normal load to specimen increased, the wear rate increased. However, as the experimental temperature increased, the frictional coefficient decreased and the wear rate decreased accordingly. It was found from the wear studies that a power-law relation works between the frictional work input and the wear rate. It was observed that the wear rate dramatically increased by the degradation of the rubber specimen. The wear pattern was developed and the bigger ridge space of the pattern was observed usually in the higher normal load applied. In determining the wear rate of rubber compound, the continuous measurements of wear distance using the blade-type abrader could be successfully used instead of intermittent measurements of wear-loss weight.

• Elastomers and Composites
• /
• v.56 no.3
• /
• pp.172-178
• /
• 2021

The wear behavior of styrene-butadiene rubber (SBR) and butadiene rubber (BR) was investigated using a blade-type abrader with a steel blade (SB), Ti-coated tungsten carbide blade (TiB), or zirconia blade (ZB). The wear rate of SBR against SB and TiB decreased with increasing number of revolutions because of the blunting of the blades during wear. However, the wear rate of SBR against ZB remained nearly constant with little blade blunting. Generally, the wear rate of BR was largely unaffected by the blade material used for abrasion. The wear rate and frictional coefficient of SBR were found to be higher than those of BR at similar levels of frictional energy input. A power-law relationship was found between the wear rate and frictional energy input during abrasion. A well-known Schallamach pattern was observed for SBR, while a much finer pattern was observed for BR. The blade material affects the wear rate of the rubbers because the macromolecular free radicals and blade tend to undergo mechano-chemical reactions. The inorganic ZB was found to be the most inert for such a mechanism.

• Elastomers and Composites
• /
• v.41 no.3
• /
• pp.194-204
• /
• 2006

The effects of the particle size and the structure of carbon blacks on the friction and the wear behavior of filled natural rubber were investigated in this study. The particle size and the structure of carbon black had a significant effect on the wear rates and the worn surface pattern, and the effect of them on abrasion resistance should be considered for the optimum design of desired wear properties. Ten carbon blacks with various sizes and structures are mixed with natural rubber in order to investigate the effects on the wear rate ($W_R$). The friction and the wear behavior were examined by self-made blade type friction-wear abrader, and the ,elation with characteristic parameter (${\psi}=\sqrt{{N_2^2}+{DBP^2}}$), obtained from the particle size and the structure, was studied. The wear rate ($W_R$) had a Power Law relation with the frictional work ($W_f$) and it was inversely proportional to the characteristic parameter of carbon black. It means that smaller particle size and better structure development of carbon black resulted in improved abrasion resistance.