• Journal of Powder Materials
• /
• v.10 no.3
• /
• pp.201-208
• /
• 2003

Distributions of diamond particles protruding on the surface of worn diamond segments in circular saw has been investigated. Scanning electron microscope was used to examine the worn ,surface and radial saw blade wear and grinding ratio was measured. The number of protruded diamond particle was approximately 50% of the total number of particles, and that was independent of diamond particle concentration and table speed. It was also noted that the inter-particle distance did not follow a symmetric function like Gaussian distribution function, instead it fitted well with a probability density function based on gamma function. The distribution of inter-particle spacing, therefore, was analyzed using a gamma function model.

• Proceedings of the Korean Society of Machine Tool Engineers Conference
• /
• 2001.04a
• /
• pp.101-106
• /
• 2001

In order to establish the optimum process parameters and diamond saw blade composition for machining natural stone, the chip formation process and the wear process must be understood. Diamond saw blade is one of the most effective, versatile, and extensively used methods of processing rock and other hard materials, such as granite, marble, concrete and asphalt. For many years, it has been known that chip thickness is one of the most significant in the understanding of the sawing process, and other variables such as force and power have been correlated with it. In this study, mathematical relations of a material chipped by a single grit of the saw blade will be undertaken. The material chipping geometries have been mathematically defined and derived as maximum chip thickness.

• Journal of Powder Materials
• /
• v.11 no.5
• /
• pp.412-420
• /
• 2004

The purpose of the present study is to determine an optimum composition using cheaper powders keeping with high performance of hard rock cutting diamond saw blade. With 50Fe-20(Cu . Sn)-30Co specimen, a part of Co was replaced by Ni(5%, 10%, and 15%, respectively). These specimens were hot pressed and sintered for predetermined time at various temperature. Sintering is performed by two different methods of temperature controlled method and specimen dimension controlled method. In order to determine the property of the sintered diamond saw blade, 3 point bending tester, X-ray diffractometer, and SEM were used. As the Co in the bond alloy was replaced by Ni, the hardness of the specimen increased. Thus the 50Fe-20(CuㆍSn)-15Co-15Ni specimen showed the maximum hardness of 104(HRB). The results of 3 point bending test showed that flexure strength decreased along with increase in Ni content. This is attributed to the formation of intermetallic compound(Ni$_{x}$Sn) determined by X-ray diffraction. The fracture surface after 3 point bending test showed that diamond was fractured in the specimen containing 0%, 5%, and 10%Ni, and the fracture occurred at the interface between diamond and matrix in the specimen containing 15%Ni. The cutting ability test showed that the abrasive property was not changed in the specimen containing 0%, 5%, and 10%Ni. The optimum composition determined in this study is 50Fe-20(CuㆍSn)-20Co-10Ni.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.1140-1141
• /
• 2006

Diamond tools with several layers of diamond grits through thickness direction were tested by sawing. The saw blades with evenly distributed grits showed better cutting performance compared to the random distributed saw. At a given concentration of grits, as the spacing between layers was increased, the cutting performance was improved, and as decreased, it showed more tool life

• Proceedings of the KWS Conference
• /
• 2002.10a
• /
• pp.639-643
• /
• 2002

The main purpose of this study was to investigate the formation mechanisms of imperfections such as irregular humps, outer cavity and inner cavity in the laser fusion zone of diamond saw blade. Laser beam welding was conducted to join two parts of blade; mild steel shank and Fe-Co-Ni sintered tip. The variables were beam power and travel speed. The microstructure and elements distributions of specimens were analyzed with SEM, AES, EPMA and so on. It was found that these imperfections were responded to heat input. Irregular humps were reduced in 10.4∼17.6kJ/m heat input range. However there were no clear evidences, which could explain the relations between humps formation and heat input. The number of outer cavity and inner cavity decreased as heat input was increased. Considering both possible defects formations mechanisms, it could be thought that outer cavity was caused by insufficient refill of keyhole, which was from rapid solidification of molten metal and fast molten metal flow to the rear keyhole wall at low heat input. More inner cavities were found near the interface of the fusion zone and sintered segment and in the bottom of the fusion zone. Inner cavity was mainly formed in the upper fusion zone at high heat input whereas was in the bottom at low heat input. Inner cavity was from trapping of coarsened preexist pores in the sintered tip and metal vapor due to rapid solidification of molten metal before the bubbles escaped.

• International Journal of Korean Welding Society
• /
• v.2 no.1
• /
• pp.21-24
• /
• 2002

The main purpose of this study was to investigate the formation mechanisms of imperfections such as irregular humps, outer cavity and inner cavity in the laser fusion zone of diamond saw blade. Laser beam welding was conducted to join two parts of blade; mild steel shank and Fe-Co-Ni sintered tip. The variables were beam power and travel speed. The microstructure and elements distributions of specimens were analyzed with SEM, AES, EPMA and so on. It was found that these imperfections were responded to heat input. Irregular humps were reduced in 10.4∼l7.6kJ/m heat input range. However there were no clear evidences, which could explain the relations between humps formation and heat input. The number of outer cavity and inner cavity decreased as heat input was increased. Considering both possible defects formations mechanisms, it could be thought that outer cavity was caused by insufficient refill of keyhole, which was from rapid solidification of molten metal and fast molten metal flow to the rear keyhole wall at low heat input. More inner cavities were found near the interface of the fusion zone and sintered segment and in the bottom of the fusion zone. Inner cavity was mainly formed in the upper fusion zone at high heat input whereas was in the bottom at low heat input. Inner cavity was from trapping of coarsened preexist pores in the sintered tip and metal vapor due to rapid solidification of molten metal before the bubbles escaped.

• Korean Journal of Materials Research
• /
• v.14 no.4
• /
• pp.300-306
• /
• 2004

A laser welding has been made between sintered tip of Fe-Co-W and low carbon steel shank for the diamond saw blade. The welding characteristics and formation of defect has been investigated carefully for the weld fusion zone in different welding condition. Full penetration has been observed for the whole range of heat input investigated in the present work. Bead width and under-fill have been increased with the increase of heat input. With increasing of heat input small cavities were decreased while large cavities were increased. The ratio of total cavity area to the entire weld bead area was not changed significantly with change of heat input. Most of cavities were found near the tip, and supposed to be formed from the pore in the tip.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.20 no.10
• /
• pp.72-79
• /
• 2021

A circular saw is an effective tool for cutting glass and carbon-fiber hybrid composites. This study investigated tool wear and cut quality when reusing saw blades. The carbide saws wear four times faster than the new ones, and polycrystalline diamond (PCD) is very resistant to tool wear, except at the end of its lifespan. The cut cross-section quality is affected by the blade type, tool wear, and spindle speed. Alternate top bevel (ATB)-type blades are suitable for cutting fiber-reinforced plastics, but triple-chip grind (TCG)-type blades are unsuitable because they cause fiber-pullout defects. Tool wear and low spindle speeds increase the occurrence of arc scratches, due to the rear saw blade. A microscopic examination showed that the burr, which is a mixture of fiber chips and epoxy matrix, was bonded on top, and glass-fiber delamination occurred on the bottom glass-fiber-reinforced polymer (GFRP) surface.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2005.05a
• /
• pp.272-272
• /
• 2005

• Proceedings of the Korean Society of Laser Processing Conference
• /
• 2002.05a
• /
• pp.65-70
• /
• 2002