• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.859-860
• /
• 2006

TiC-$TiB_2$-SiC system was a ternary eutectic, whose eutectic composition was 34TiC-$22TiB_2$-44SiC (mol%). TiC-$TiB_2$-SiC ternary eutectic composite were synthesized by a floating zone method using TiC, $TiB_2$ and SiC powders as starting materials. The TiC-$TiB_2$-SiC eutectic composite showed a lamellar texture. TiC(022), $TiB_2(010)$ and SiC(111) of the eutectic composite were perpendicular to the growth direction. TiC-$TiB_2$-SiC ternary eutectic composite had specific relationship among the crystal planes: TiC[011]//$TiB_2[010]$//SiC[112], TiC(200)//$TiB_2$(001)//SiC(402) and $TiC(1\bar{1}1)$//$TiB_2(101)$//SiC(220).

• Journal of Korea Foundry Society
• /
• v.10 no.1
• /
• pp.57-63
• /
• 1990

Continuous casting of the $Al-CuAl_2$ eutectic composite was carried out by the upward continuous casting process. The morphology of the eutectic growth and the stability of solid-liquid interface were investigated under various growth conditions. It was possible to get the planar solid-liquid interface at the condition of $G_L/R$＝$3.6{\times}10^3^{\circ}Csec/mm^2$. And the colony structures were formed at the conditions of $G_L/R$ < $R=0.33{\times}10^3^{\circ}Csec/mm^2$. The inter-lamellar spacing of $Al-CuAl_2$ eutectic composite was decreased with the increase of pulling speed. The reduction of inter-lamellar spacing & value of $G_L/R$ caused the increase of ultimate tensile strength and Rockwell hardness in $Al-CuAl_2$ eutectic composite.

• Journal of Korea Foundry Society
• /
• v.10 no.1
• /
• pp.50-56
• /
• 1990

Continuous casting of the $Al-Al_3Ni$: eutectic composite was carried out by the upward continuous casting process. The morphology of the eutectic growth and the stability of solid-liquid interface were investigated under various growth conditions in an upward continuous casting. The effect of growth conditions on the mechanical properties of the $Al-Al_3$ Ni eutectic composit was also investigated, and the results were compared with those by the Bridgman method. As for the results, it was possible to get the planar solid-liquid interface at the condition of $G_L/R$＝$1.04{\times}10^3^{\circ}Csec/mm^2$. And the inter-rod spacing of $Al-Al_3Ni$ eutectic composite was decreased with the increase of pulling speed. The reduction of inter-rod spacing & value of $G_L/R$ caused the increase of ultimate tensile strength in $Al-Al_3Ni$: eutectic composite. The ultimate tensile strengths of $Al-Al_3Ni$ by the upward continuous casting were higher then those by the Bridgman method.

• Journal of Korea Foundry Society
• /
• v.10 no.6
• /
• pp.503-508
• /
• 1990

The effect of interlamellar spacing on tensile behavior and fracture mode at high temperatures has been studied for unidirectionally solidified $Al-CuAl_2$ eutectic composite. The tensile properties at room temperature in $Al-CuAl_2$ eutectic composite improved as the interlamellar spacing decreased due to the constraint effects of closely spaced lamellae, while the opposite behavior was observed at high temperatures due to the annihilation of the constraint effects by phase boundary sliding. The $Al-CuAl_2$ eutectic composite exhibited brittle fracture mode below the temperature at which the reinforcing phase softened but ductile fracture mode above the temperature.

• Journal of Korea Foundry Society
• /
• v.15 no.6
• /
• pp.566-573
• /
• 1995

In this study, the microstructural characteristics such as primary silicon, eutectic silicon, $SiC_p$ dispersion behavior, compound amount and Si solubility in $Al/SiC_p$ composite fabricated by the squeeze casting under various conditions were investigated systematically. As applied pressure(MPa) increases, cooling rate and compound amount are increased. In gravity casting, the cooling rate of hypereutectic composite is slower than of hypoeutectic composite by exothermic reaction of primary Si crystallization. But the cooling rate of hypereutectic composite is faster than that of hypoeutectic composite fabricated by same applied pressure, because amount of primary Si crystallization in hypereutectic composite was decreased, on the contrary, primary ${\alpha}-Al$ in hypoeutetic composite was increased due to increase of Si solubility in matrix by applied pressure. The crystalized primary silicon in hypereutectic composite fabricated by squeeze casting become more fine than that in non-pressure casting This is because mush zone became narrow due to increase of Si content of eutectic composition by pressure and time for growth of primary silicon got shorter according to applied pressure. It is turned out that eutectic temperature and liquidus are decreased by the increasing of squeeze pressure in all the composite due to thermal unstability of matrix owing to increasing of Si solubility in matrix by the increasing of applied pressure, as indicated in thermal anaiysis(DSC) results.

• Journal of Nuclear Fuel Cycle and Waste Technology(JNFCWT)
• /
• v.15 no.1
• /
• pp.83-90
• /
• 2017

The pyroprocessing of spent nuclear fuel generates LiCl-KCl eutectic waste salt containing radioactive rare earth nuclides. It is necessary to develop a simple process for the treatment of LiCl-KCl eutectic waste in a hot-cell facility. In this study, capture and solidification of a rare earth nuclide (Nd) in LiCl-KCl eutectic salt using an inorganic composite with a $Li_2O-Al_2O_3-SiO_2-B_2O_3$ system was conducted to simplify the existing separation and solidification process of rare earth nuclides in LiCl-KCl eutectic waste salt from the pyroprocessing of spent nuclear fuel. More than 98wt% of Nd in LiCl-KCl eutectic salt was captured when the mass ratio of the composite was 0.67 over $NdCl_3$ in the eutectic salt. The content of $Nd_2O_3$ in the Nd captured-composite reached about 50wt%, and this composite was directly fabricated into a homogeneous and chemical resistant glass waste in a monolithic form. These results will be utilized in designing a process to simplify the existing separation and solidification process.

• Journal of the Korean Ceramic Society
• /
• v.23 no.2
• /
• pp.13-20
• /
• 1986

Composite polycrystals including ${\gamma}$-$6Bi_2O_3$.$SiO_2$ crystal which have needlelike regular structure are useful for the high resolution optical devices. For the purpose of obtaining the composite polycrystals described above the melts of eutectic composition in the three eutectic systems including $6Bi_2O_3$.$SiO_2$ composition were unidirectionally solidified at a rate of 0.05 and 0.25 cm/h under a thermal gradient of 10$0^{\circ}C$/m. Composite polycrystals of relatively regular structure in which needlelike ${\gamma}$-$6Bi_2O_3$.$SiO_2$ crystals were arrayed in parallel with $2Bi_2O_3$.$B_2O_3$ crystal matrix were obtained when the eutectic melt of $6Bi_2O_3$.$SiO_2 -2Bi_2O_3$.$B_2O_3$ system was solidified at a rate of 0.25 cm/h. Partial structural irregularity however was found in the obtained composite polycrystals.

• Journal of the Korean Ceramic Society
• /
• v.56 no.4
• /
• pp.331-339
• /
• 2019

While high-temperature ceramic composites consisting of carbides, borides, and nitrides, the so-called ultra-high-temperature ceramics (UHTCs), have been commonly produced through solid-state sintering, melt-solidification is an alternative method for their manufacture. As many UHTCs are binary or ternary eutectic systems, they can be melted and solidified at a relatively low temperature via a eutectic reaction. The microstructure of the eutectic composites is typically rod-like or lamellar, as determined by the volume fraction of the second phase. Directional solidification can help fabricate more sophisticated UHTCs with highly aligned textures. This review describes the fabrication of UHTCs through the eutectic reaction and explains their mechanical properties. The use of melt-solidification has been limited to small specimens; however, the recently developed laser technology can melt large-sized UHTCs, suggesting their potential for practical applications. An example of laser melt-solidification of a eutectic ceramic composite is demonstrated.

• Journal of Korea Foundry Society
• /
• v.10 no.5
• /
• pp.399-407
• /
• 1990

The effect of thermal cycling and isothermal exposure on the high temperature microstructural stability of unidirectionally solidified $Al-CuAl_2$ eutectic composite has been studied. A coarsening procedures of lamellar eutectic structures were initiated at growth fault region because of diffusion through low angle boundary at this region. It was considered that thermally induced residual stresses produced by thermal cycling were high enough to increase the dislocation density in Al-rich matrix phase. However, it was also considered that dislocations generated by these high thermal stresses were annihilated at high temperature by stress relaxation. Consequently, the thermal cycling up to 1440 cycles between 20 and $520^{\circ}C$ did not affect the microstructural stability.

• Korean Journal of Materials Research
• /
• v.23 no.10
• /
• pp.568-573
• /
• 2013

The deformation properties of a TiC-Mo eutectic composite were investigated in a compression test at temperatures ranging from room temperature to 2053 K and at strain rates ranging from $3.9{\times}10^{-5}s^{-1}$ to $4.9{\times}10^{-3}s^{-1}$. It was found that this material shows excellent high-temperature strength as well as appreciable room-temperature toughness, suggesting that the material is a good candidate for high-temperature application as a structure material. At a low-temperature, high strength is observed. The deformation behavior is different among the three temperature ranges tested here, i.e., low, intermediate and high. At an intermediate temperature, no yield drop occurs, and from the beginning the work hardening level is high. At a high temperature, a yield drop occurs again, after which deformation proceeds with nearly constant stress. The temperature- and yield-stress-dependence of the strain is the strongest in this case among the three temperature ranges. The observed high-temperature deformation behavior suggests that the excellent high-temperature strength is due to the constraining of the deformation in the Mo phase by the thin TiC components, which is considerably stronger than bulk TiC. It is also concluded that the appreciable room-temperature toughness is ascribed to the frequent branching of crack paths as well as to the plastic deformation of the Mo phase.