• 대한기계학회논문집A
• /
• 제24권7호
• /
• pp.1697-1702
• /
• 2000

This study has been performed to investigate the effects of glass fiber characteristics on the mechanical properties of thermoplastic composite. The surface of glass fiber was coated with the silan e to enhance the bonding strength between fiber and matrix. A micro-droplet pull-off test was performed to investigate the influence of the silane concentration on the bonding strength. The maximum bonding strength was observed around 10.8% silane concentration. In order to examine the influence of the fiber length and fiber content on the properties of the composite, the composite materials involving tile fiber lengths of 5mm, 10mm, 15mm 20mm, and 25mm were tested. The composites used contain 20%, 30%, and 40% by weight of glass fibers. Tension and flexural tests were performed to investigate their mechanical properties of the composites. The tensile strength and tensile modulus of the composite increase with increasing the glass fiber content. The tensile modulus increases slightly with increasing the fiber length. The maximum tensile strength is observed around the fiber length of 15-20mm. The flexural modulus and strength also increase slightly with increasing the fiber length.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 1999년도 춘계학술대회 논문집
• /
• pp.536-539
• /
• 1999

Physical properties of glass fiber-reinforced nylon 6,6 and ionomer blends were investigated in variation of ionomer and glass fiber content. With the increase of ionomer content, tensile strength, impact strength and flexural strength decreased, whereas increasing glass fiber content, these properties were improves. Both permittivity and tan $\delta$ remain unchanged. Space charge distribution was investigated by PEA (Pulsed electroacoustic) method. Heterocharge was found in nylon 6,6 and 히ass fiber composites, whereas composites, whereas when ionomer is blended.

• 한국전산유체공학회지
• /
• 제15권4호
• /
• pp.92-98
• /
• 2010

In a modern high speed drawing process of optical fibers, it is necessary to use helium as a cooling gas in a glass fiber cooling unit in order to sufficiently cool down the fast moving glass fiber freshly drawn from the heated silica preform in the furnace. Since the air is entrained unavoidably when the glass fiber passes through the cooling unit, the helium is needed to be injected constantly into the cooling unit. The present numerical study investigates and analyzes the air entrainment using an axisymmetric geometry of glass fiber cooling unit. The effects of helium injection rate and direction on the air entrainment rate are discussed in terms of helium purity of cooling gas inside the cooling unit. For a given rate of helium injection, it is found that there exists a certain drawing speed that results in sudden increase in the air entrainment rate, which leads to the decreasing helium purity and therefore the cooling performance of the glass fiber cooling unit. Also, the helium injection in aiding direction is found to be more advantageous than the injection in opposing direction.

• Composites Research
• /
• 제29권5호
• /
• pp.293-298
• /
• 2016

본 연구에서는 PPS(Polyphenylene sulfide) 수지와 단면이 원형(round type), 누에형(cocoon type), 플랫형(flat type)인 3종류의 유리섬유를 사용하여 컴파운딩 및 사출을 통해 차량 전조등 광원 모듈용 유리섬유 강화 열가소성 플라스틱(glass fiber reinforced thermoplastic : GFRTP)을 제조하였다. 섬유 단면형태 및 함유량에 따른 효과를 알아보기 위해 인장, 굴곡, 충격 특성을 평가하였고, 단면에 따른 유동성, 형태안정성 및 평탄성을 관찰하였다. 그 결과 플랫 단면의 유리섬유를 사용했을 때 기계적 특성이 가장 우수했고 섬유함유량이 증가할수록 강도가 향상되는 경향을 보였다. 또한, 형태안정성, 평탄성의 경우에도 플랫 단면 섬유 사용 시 더 좋은 결과를 나타내었다.

• 한국결정성장학회지
• /
• 제23권4호
• /
• pp.180-188
• /
• 2013

삼척도계지역의 탄광에서 석탄채굴시에 부산물로 발생되는 사암계 석탄폐석을 원료로 사용하여 E-glass fiber 조성의 유리를 제조하였다. 본 연구에서는 카본함량이 비교적 적은 실리카-알루미나질의 사암계 석탄폐석을 사용하였으며, 폐석의 투입량을 0~35 %까지 변화시켰다. 서로 다른 석탄폐석 투입량을 갖는 배치원료를 $1550^{\circ}C$에서 2시간 용융하여 E-glass조성을 갖는 투명하고 맑은 유리가 얻어졌고, 81~84 %의 높은 가시광투과율, $5.39{\sim}5.61{\times}10^{-6}/^{\circ}C$의 열팽창계수, 851~$860^{\circ}C$의 연화점을 나타내었다. 유리섬유 시편은 $1150^{\circ}C$에서 섬유인상장치를 통해 얻어졌고, 복합재료의 보강용 유리섬유로서 내화학성 시험과 기계적 특성평가를 위한 인장강도를 측정하였다. 그 결과 석탄폐석을 사용한 E-glass fiber의 특성이 석탄폐석을 사용하지 않은 보통 E-glass 섬유에 비해 충분히 양호한 특성을 나타내어 E-glass 섬유용 원료로서 석탄폐석의 활용가능성을 확인할 수 있었다.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2001년도 봄 학술발표회 논문집
• /
• pp.49-54
• /
• 2001

Using waste glass in concrete can cause crack and strength loss by the expansion of alkali-silica reaction(ASR). In this study, ASR expansion and properties of strength were analyzed in terms of brown waste glass content, and fibers(steel fiber, polypropylene fiber) and fiber content for reduction ASR expansion due to waste glass. In this accelerated ASTM C 1260 test of waste glass, pessimum content can not be found. Also, when used the fibers with waste g1ass, there is an effect on reduction of expansion and strength loss due to ASR between the alkali in the cement paste and the silica in the waste glass. Specially, adding 1.5 vol.% of steel fiber to 20% of waste glass the expansion ratio was reduced by 40% and flexural strength was developed by up to 110% comparing with only Waste glass ( $80^{\circ}C$ $H_{2}$ O curing).

• Korea-Australia Rheology Journal
• /
• 제19권1호
• /
• pp.17-25
• /
• 2007

In liquid composite molding (LCM), composites are produced by impregnation of a dry preform with liquid resin. The resin flow through the preform is usually described by Darcy's law and the permeability tensor must be obtained for filling analysis. While the resin flow in the thickness direction can be neglected for thin parts, the resin flow in the transverse direction is important for thicker parts. However, the transverse permeability of the preform has not been investigated frequently. In this study, the transverse permeability was measured experimentally for five different fiber preforms. In order to verify the experimental results, the measured transverse permeability was compared with numerical results. Five different fiber mats were used in this study: glass fiber woven fabric, aramid fiber woven fabric, glass fiber random mat, glass fiber braided preform, and glass/aramid hybrid braided preform. The anisotropic braided preforms were manufactured by using a three dimensional braiding machine. The pressure was measured at the inlet and outlet positions with pressure transducers.

• Journal of the Korean Wood Science and Technology
• /
• 제48권5호
• /
• pp.685-695
• /
• 2020

The connection performance between cross-laminated timber (CLT) walls and support has the greatest effect on the horizontal shear strength. In this study, the horizontal shear performance of CLT walls with reinforced connection systems was evaluated. The reinforcements of metal bracket connections in the CLT connection system was made by attaching glass fiber-based reinforcement to the connection zone of a CLT core lamina. Three types of glass fiber-based reinforcement were used: glass fiber sheet (GS), glass fiber cloth (GT) and fiber cloth plastic (GTS). The horizontal shear strength of the fabricated wall specimens was compared and evaluated through monotonic and cyclic tests. The test results showed that the resistance performance of the reinforced CLT walls to a horizontal load based on a monotonic test did not improve significantly. The residual and yield strengths under the cyclic loading test were 38 and 18% higher, respectively, while the ductility ratio was 38% higher than that of the unreinforced CLT wall. The glass fiber-based reinforcement of the CLT connection showed the possibility of improving the horizontal shear strength performance under a cyclic load, and presented the research direction for the application of real-scale CLT walls.

• 한국지반공학회:학술대회논문집
• /
• 한국지반공학회 2000년도 토목섬유 특별세미나
• /
• pp.35-38
• /
• 2000

Reflection cracks can be occurred in the asphalt layer overlaid on portland cement concrete pavements, because this layer is sensitive to environmental conditions including temperature changes and displacements of the pavement. A result of trial applications using glass fiber grids is introduced in this paper. Glass fiber grids were used between the asphalt layer and the concrete base to reduce the reflection crack of the asphalt layer. No cracks were observed in the glass grid installed area about 2 years later from trial constructions.

• 대한소아치과학회지
• /
• 제32권1호
• /
• pp.132-135
• /
• 2005

본 연구의 목적은 유전치 심미수복의 새로운 방법으로 glass fiber를 이용한 강화형 strip crown의 사용을 제시하고자 하는 것이다. Strip crown의 제작을 위하여 celluloid crown form(3M, USA)과 복합레진은 Z100(P shade, 3M, USA)을, 유동성 복합레진은 Aeliteflo(Bisco Inc., USA)를 사용하였다. 상아질 결합제는 Clearfil SE Bond(Kuraray Medical Inc., Japan)를 사용하였고 강화를 위하여 그물형 glass fiber(TESCERA Fiber Mesh, Bisco Inc, USA)를 사용하였다. 적절한 크기의 celluloid crown form을 성형하여 삭제된 치아에 시적한 후 레진 접착제와 유동성 복합레진으로 처리한 그물형 glass fiber를 설측 내면에 삽입하고 광중합하였다. 잔여 공간에 복합레진을 채우고 치아에 끼운 다음 광중합하였다. 복합레진의 심미성은 유지하면서 glass fiber로부터 기계적 장점을 얻을 수 있을 것으로 사료된다. 새로운 강화형 strip crown의 물성에 대한 후속연구가 필요하다.