• 대한기계학회논문집
• /
• 제12권5호
• /
• pp.935-943
• /
• 1988

본 연구에서는 유압벌지시험기를 이용한 저속 벌지시험과 낙하해머(drop hammer)를 응용한 충격벌지시험기를 제작, 사용하여 충격벌지시험을 하여 저속변형과 충격변형에서 판재금속의 성형한계선도를 구하고 변형율속도가 판재의 불안정 및 성형 성에 미치는 영향을 조사하고 다이의 형상비(단축/장축)를 0.5, 0.75, 1.0 등으로 달 리하여 실험하므로써 변형경로에 따른 한계변형율의 변화를 관찰하고 아울러 기존의 성형한계이론과 비교, 검토하였다.

• 대한기계학회논문집A
• /
• 제30권5호
• /
• pp.543-549
• /
• 2006

The bursting properties under various conditions were investigated to ascertain the optimum conditions to yield the best properties. Fiber aspect ratio (AR: length of fiber/diameter of fiber), interphase condition and fiber content were considered as variables which impact the bursting pressure, bulge constant, torsional rigidity ratio. The bursting pressure of reinforced rubber increases up to 8.73 times compared to the virgin material. The better interphase condition shows the higher bursting pressure at given AR and fiber content. The bulge constant and torsional rigidity highly decrease with increasing AR and better interphase condition at same fiber content. The bulge constant and torsional rigidity reveal the minimum of 11% and 0.6% of the matrix, respectively. The bursted shape after test shows the different patterns between unfilled and reinforced rubbers. The case of virgin rubber shows a radiating shape while that of reinforced rubber shows a fluctuating straight line. Overall, it was found that the fiber AR and interphase condition have an important effect on bursting properties.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2009년 추계학술발표대회
• /
• pp.40-40
• /
• 2009

The Cu-bearing PFS-700 steel which has yield strength over 700 MPa was developed to replace the existing submarine structural material, HY-100. PFS-700 steel has good combination of mechanical properties and superior weldability which can be welded without pre-heating before welding. Application PFS-700 steel to submarine or battle ship will give a great reduction of cost by removing or lowing pre-heating. To develop pre-heat free welding consumables that matches and take advantage of PFS-700 steel, new welding consumables have been designed for the GMAW, SAW processes and explosion bulge test(EBT) were conducted to see the reliability of welded structure. All welding was conducted without pre-heating before welding, the inter-pass temperatures were below $50^{\circ}C$ for SAW50 and $150^{\circ}C$ for GMAW and SAW150. All EBT specimens show over 14% reduction of thickness without through-thickness crack or propagation of crack to the hole-down area. Tensile properties for all welding conditions show higher(GMAW) or similar values(SAW50, SAW150) to the base metal. Charpy impact values for the weld metal also show 163.5J(GMAW), 95.4J(SAW50) and 69.0J(SAW150), which meet the goal, 50J, of this project.

• Journal of Welding and Joining
• /
• 제27권6호
• /
• pp.80-86
• /
• 2009

The Cu-bearing PFS-700 steel which has yield strength over 700 MPa was developed to replace the existing submarine structural material, HY-100. The PFS-700 steel has a combination of good mechanical properties and superior weldability. Becaus of that, it can be welded without pre-heating. The application of PFS-700 steel to submarine or battle ship will give a great reduction of cost by omitting pre-heating or lowering pre-heat temperature. To develop pre-heating free welding consumables that match and take advantage of PFS-700 steel, new welding consumables have been designed for the GMAW, SAW processes and explosion bulge test(EBT) was conducted to see the reliability of welded structure. All welds were made without pre-heating, and the inter-pass temperature was below $50^{\circ}C$ for SAW50 and $150^{\circ}C$ for GMAW and SAW150. All EBT specimens show over 14% thickness reduction without through-thickness crack or crack propagation to the hole-down area. Tensile properties for all welding conditions show higher(GMAW) or similar values(SAW50, SAW150) to the base metal. Charpy impact values for the weld metal also show 163.5J(GMAW), 95.4J(SAW50) and 69.0J(SAW150), which meet the goal(higher than 50J) of this project.