• Journal of the Microelectronics and Packaging Society
• /
• v.11 no.1
• /
• pp.21-28
• /
• 2004

We have demonstrated the applicability of dry film photoresist (DFR) in photolithography process for fine pitch solder bumping on the polytetrafluoroethylene (PTFE/Teflon ) printed circuit board (PCB). The copper lines were formed with 100$\mu\textrm{m}$ width and 18$\mu\textrm{m}$ thickness on the PTFE test board, and varying the gaps between two copper lines in a range of 100-200$\mu\textrm{m}$. The DFRs of 15$\mu\textrm{m}$ thickness were laminated by hot roll laminator, by varying laminating temperature from $100{\circ}C$ to 15$0^{\circ}C$ and laminating speed from 0.28-0.98cm/s. We have found the optimum process of DFR lamination on PTFE PCB and accomplished the formation of indium solder bumps. The optimum lamination condition was temperature of $150^{\circ}C$ and speed of about 0.63cm/s. And the smallest size of indium solder bump was diameter of 50$\mu\textrm{m}$ with pitch of 100$\mu\textrm{m}$.

• Proceedings of the International Microelectronics And Packaging Society Conference
• /
• 2003.11a
• /
• pp.169-173
• /
• 2003

We demonstrated the applicability of dry film photoresist (DFR) in photolithography process for fine pitch solder bumping on the polytetrafluoroethylene (PTFE/Teflon) printed circuit board (PCB). The copper lines were formed with $100\;{\mu}m$ width and $18\;{\mu}m$ thickness on the PTFE test board, and varying the gaps between two copper lines in a range of $100-200\;{\mu}m$. The DFRs of $15\;{\mu}m$ thickness were laminated by hot roll laminator, by varying laminating temperature from $100^{\circ}C\;to\;150^{\circ}C$ and laminating speed. We found the optimum process of DFR lamination on PTFE PCB and accomplished the formation of indium solder bumps. The optimum lamination condition was temperature of $150^{\circ}C$ and speed of about 0.63 cm/s. And the smallest size of indium solder bump was diameter of $50\;{\mu}m$ with pitch of $100\;{\mu}m$.